Anti-skid coating composition

Claim 2

A weather-resistant temporary anti-skid coating consisting essentially of: (a) a binder composition having a viscosity of about 300 to 1200 centipoises comprising: (i) about 85 to 95 weight % of an aqueous resin selected from the group consisting of urea-formaldehyde resin, melamine formaldehyde resin, and mixtures thereof; (ii) about 3 to 20 weight % of an aqueous emulsion selected from the group consisting of polyvinyl acetate, ethylene-vinyl acetate copolymer and mixtures thereof; (iii) a catalyst comprising a salt selected from the group consisting of ammonium chloride, ammonium sulfate and mixtures thereof; (iv) a dispersant for said catalyst; and (b) an aggregate that does not dull cutting blades having a particle size of about 20 to 60 mesh; wherein the coating is sufficiently viscous to substantially prevent its penetration into a wooden substrate and wherein said coating has a cure time of about 1/2 to 11/2 minutes at about 350° F.

Claim 3

The coating of claim 1, wherein the alt catalyst is about 0.25 to 3.0 weight % of the binder composition.

Claim 4

The coating of claim 1, wherein the aggregate material is selected from the group consisting of walnut shell aggregate, rubber chips, waste plastic aggregate, and mixtures thereof.

Claim 5

The coating of claim 1, wherein the urea formaldehyde resin has a boiling water reactivity of about 25 to 90 seconds.

Claim 6

The coating of claim 1, wherein the salt catalyst contains a dispersant varying from about 15 to 60% by weight of the ammonium chloride catalyst.

Claim 7

The coating of claim 5, wherein the dispersant is selected from the group consisting of alnut shell powder, pecan shell powder, bark powder, furafil powder, wood powder, wheat powder, and mixtures thereof.

Claim 8

The coating of claim 1, wherein the anti-skid binder composition is used in conjunction with a panel board substrate.

Claim 9

A weather-resistant laminate having a temporary anti-skid coating consisting essentially of a substrate, a first coating of a binder composition in contact with the substrate comprising: (a) about 85 to 95 weight % of an aqueous resin selected from the group consisting of urea-formaldehyde resin, melamine formaldehyde resin, and mixtures thereof; (b) about 3 to 20 weight % of an aqueous emulsion selected from the group consisting of polyvinyl acetate, ethylene-vinyl acetate copolymer and mixtures thereof; (c) a catalyst comprising a salt selected from the group consisting of ammonium chloride, ammonium sulfate and mixtures thereof; (d) a dispersant for said catalyst; and an intermediate aggregate layer with an aggregate that does not dull cutting blades having a particle size of about 20 to 60 mesh in contact with the first binder coating; and a second top coating of the aforesaid binder composition in contact with the aggregate coating; wherein the binder composition has a viscosity of about 300 to 1200 centipoise, and is sufficiently viscous to substantially prevent its penetration into a wooden substrate, and wherein said composition has a cure time of about 1/2 to 11/2 minutes at about 350° F.

Claim 10

A weather-resistant laminate having a temporary anti-skid coating consisting essentially of a substrate, a first coating of a binder composition in contact with the substrate comprising: (a) about 85 to 95 weight % of an aqueous resin selected from the group consisting of urea-formaldehyde resin, melamine formaldehyde resin, and mixtures thereof; (b) about 3 to 20 weight % of an aqueous emulsion selected from the group consisting of polyvinyl acetate, ethylene-vinyl acetate copolymer and mixtures thereof; (c) a catalyst comprising a salt selected from the group consisting of ammonium chloride, ammonium sulfate and mixtures thereof; (d) a dispersant for said catalyst; and an intermediate aggregate layer with an aggregate that does not dull cutting blades having a particle size of about 20 to 60 mesh in contact with the first binder coating; and a second top coating of the aforesaid binder composition in contact with the aggregate coating; wherein the binder composition has a viscosity of about 300 to 1200 centipoise, and is sufficiently viscous to substantially prevent its penetration into a wooden substrate, and wherein said composition has a cure time of about 1/2 to 11/2 minutes at about 350° F.

Claim 11

The laminate of claim 8, wherein the aggregate material is selected from the group consisting of walnut shell aggregate, rubber chips, waste plastic aggregate, and mixtures thereof.

Claim 12

The laminate of claim 8, wherein the substrate is panel board.

Claim 15

The method of claim 11, wherein the binder composition is contacted to the substrate at a rate of about 95 to 120 grams per square meter of surface.

Claim 16

The method of claim 11, wherein the aggregate is contacted to the substrate at a rate of about 30 to 55 grams per square meter of surface.