High active oxygen content granulated sodium perborate product and method of making the same
Assignee: Evonik Operations GmbH
•
Filing: 1990-08-20
•
Granted: 1992-03-10
•
Expires: 2010-08-20
Abstract
Abstract The spray drying of a solution containing hydrogen peroxide and sodium metaborate to obtain primary particles which are immediately conveyed after leaving the drying zone to a granulating device and are then granulated in the presence of free and/or perborate water of crystallization. The granulated materials are dried, if necessary. The generally amorphous primary particles are converted into granulated materials with at least partially crystalline structure and significantly improved shelf life. The work is performed with advantage in a spray dryer with integrated fluid bed or in a compressing granulating device. The method is suitable for preparing perborate granulated materials with an active oxygen content of over 10% by weight, especially perborate monohydrate granular materials with 14 to 16% by weight active oxygen. A rapidly dissolving product is produced with an acceptable apparent weight for ease in packaging.
Inventors
- 👤 Birgit Bertsch-Frank
- 👤 Klaus Mueller
- 👤 Thomas Lieser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:08
CPC Classifications
C; C01; C01B; C01B15/00; C01B15/055; C01B15/12; B; B01; B01J; B01J2/00; C01B15/126
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
61 words
A granulated sodium perborate product, wherein said product includes an active oxygen content in the range of 14 to 16% by weight, a dissolution rate of less than one minute as measured for a 2% by weight product concentration at 15° C., a bulk weight over 600 g/l, and an abrasion index less than 10%, as measured by ISO Test 5937.
Claim 2
Dependent Claim
61 words
A granulated sodium perborate product, wherein said product includes an active oxygen content in the range of 14 to 16% by weight, a dissolution rate of less than one minute as measured for a 2% by weight product concentration at 15° C., a bulk weight over 600 g/l, and an abrasion index less than 10%, as measured by ISO Test 5937.
Claim 3
Dependent Claim
20 words
A granulated sodium perborate product according to claim 1, wherein the active oxygen content is 15 to 16% by weight.
Claim 4
Dependent Claim
18 words
A granulated sodium perborate product according to claim 1, wherein the bulk weight is greater than 800 g/l.
Claim 5
Dependent Claim
18 words
A granulated sodium perborate product according to claim 1, wherein said product is free from foreign auxiliary agents.
Claim 6
Dependent Claim
20 words
A granulated sodium perborate product according to claim 1, wherein the bulk weight is in the range of 600-1000 g/l.
Claim 7
Dependent Claim
19 words
A granulated sodium perborate product according to claim 1, wherein the rate of dissolution is less than one-half minute.
Claim 8
Independent Claim
125 words
A method for producing granulated sodium perborate monohydrate with an active oxygen content of 14 to 16% by weight and a dissolution rate of less than 1 minute, measured with a 2% by weight solution at 15° C., comprising the steps of: removing spray-dried sodium perborate primary particles from a spray drier; introducing said perborate to an intensive mixing zone; heating said perborate to a temperature in the range of at least 60° C. to 75° C., and before, during or after said heating, adding an effective amount of powdery sodium perborate tetrahydrate under mixing condition, whereby said perborate tetrahydrate melts from said heating; allowing said perborate and said perborate tetrahydrate melt mixture to form the granulated sodium perborate; and post-drying said granulated sodium perborate.
Claim 9
Independent Claim
125 words
A method for producing granulated sodium perborate monohydrate with an active oxygen content of 14 to 16% by weight and a dissolution rate of less than 1 minute, measured with a 2% by weight solution at 15° C., comprising the steps of: removing spray-dried sodium perborate primary particles from a spray drier; introducing said perborate to an intensive mixing zone; heating said perborate to a temperature in the range of at least 60° C. to 75° C., and before, during or after said heating, adding an effective amount of powdery sodium perborate tetrahydrate under mixing condition, whereby said perborate tetrahydrate melts from said heating; allowing said perborate and said perborate tetrahydrate melt mixture to form the granulated sodium perborate; and post-drying said granulated sodium perborate.
Claim 10
Dependent Claim
22 words
The method according to claim 7, wherein the heating step is to a temperature in the range of 65° to 75° C.
Claim 11
Dependent Claim
19 words
The method according to claim 8, wherein said powdery sodium perborate tetrahydrate is introduced via a gravimetric feed apparatus.
Claim 12
Dependent Claim
16 words
The method according to claim 7, wherein the granulated product is cooled in a fluid-bed cooler.
Claim 13
Dependent Claim
16 words
The method according to claim 9, wherein the granulated product is post-dried in a flow-bed drier.
Claim 14
Dependent Claim
15 words
The method according to claim 11, wherein the flow-bed drier temperature is approximately 60° C.
Claim 15
Dependent Claim
22 words
The method according to claim 7, wherein the heating step is to a temperature in the range of 70° to 75° C.
Claim 16
Dependent Claim
9 words
The product made by the method of claim 7.
Claim 17
Dependent Claim
19 words
The method according to claim 7 wherein the granulated sodium perborate has a bulk density greater than 600 g/l.
Claim 18
Independent Claim
156 words
A method for producing granulated sodium perborate monohydrate with an active oxygen content of 14 to 16% by weight and a dissolution rate of less than 1 minute, measured with a 2% by weight solution at 15° C., a bulk weight greater than 600 g/l and an abrasion index less than 10% based on ISO test 5937, comprising the steps of: removing spray-dried sodium perborate monohydrate primary particles from a spray drier; introducing said perborate monohydrate to an intensive mixing zone; heating said perborate monohydrate to a temperature in the range of at least 60° C. to 75° C., and before, during or after said heating, adding 10 to 15% by weight sodium perborate tetrahydrate relative to the perborate monohydrate content, under mixing condition, whereby said perborate tetrahydrate melts from said heating; allowing said perborate monohydrate and said perborate tetrahydrate melt mixture to form the granulated sodium perborate monohydrate; and post-drying said granulated sodium perborate monohydrate.
Claim 19
Independent Claim
156 words
A method for producing granulated sodium perborate monohydrate with an active oxygen content of 14 to 16% by weight and a dissolution rate of less than 1 minute, measured with a 2% by weight solution at 15° C., a bulk weight greater than 600 g/l and an abrasion index less than 10% based on ISO test 5937, comprising the steps of: removing spray-dried sodium perborate monohydrate primary particles from a spray drier; introducing said perborate monohydrate to an intensive mixing zone; heating said perborate monohydrate to a temperature in the range of at least 60° C. to 75° C., and before, during or after said heating, adding 10 to 15% by weight sodium perborate tetrahydrate relative to the perborate monohydrate content, under mixing condition, whereby said perborate tetrahydrate melts from said heating; allowing said perborate monohydrate and said perborate tetrahydrate melt mixture to form the granulated sodium perborate monohydrate; and post-drying said granulated sodium perborate monohydrate.
Claim 20
Dependent Claim
162 words
A granulated sodium perborate monohydrate with an active oxygen content of 14 to 16% by weight and a dissolution rate of less than 1 minute, measured with a 2% by weight solution at 15° C., a bulk weight greater than 600 g/l and an abrasion index less than 10% based on ISO test 5937, said granulated sodium perborate monohydrate produced by the process comprising the steps of: removing spray-dried sodium perborate monohydrate primary particles from a spray drier; introducing said perborate monohydrate to an intensive mixing zone; heating said perborate monohydrate to a temperature in the range of at least 60° C. to 75° C., and before, during or after said heating, adding 10 to 15% by weight sodium perborate tetrahydrate relative to the perborate monohydrate content, under mixing condition, whereby said perborate tetrahydrate melts from said heating; allowing said perborate monohydrate and said perborate tetrahydrate melt mixture to form the granulated sodium perborate monohydrate; and post-drying said granulated sodium perborate monohydrate.
Claim 21
Dependent Claim
162 words
A granulated sodium perborate monohydrate with an active oxygen content of 14 to 16% by weight and a dissolution rate of less than 1 minute, measured with a 2% by weight solution at 15° C., a bulk weight greater than 600 g/l and an abrasion index less than 10% based on ISO test 5937, said granulated sodium perborate monohydrate produced by the process comprising the steps of: removing spray-dried sodium perborate monohydrate primary particles from a spray drier; introducing said perborate monohydrate to an intensive mixing zone; heating said perborate monohydrate to a temperature in the range of at least 60° C. to 75° C., and before, during or after said heating, adding 10 to 15% by weight sodium perborate tetrahydrate relative to the perborate monohydrate content, under mixing condition, whereby said perborate tetrahydrate melts from said heating; allowing said perborate monohydrate and said perborate tetrahydrate melt mixture to form the granulated sodium perborate monohydrate; and post-drying said granulated sodium perborate monohydrate.
References Cited (Backward Citations)
US2900668A
Cited
US2979464A
Cited
US3555696A
Cited
US4002434A
Cited
GB1377162A
Cited
US3914380A
Cited
US4115519A
Cited
US4185960A
Cited
US4215097A
Cited
US4681748A
Cited
US4968500A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-10 | 1995-09-09 | 1996-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-10 | 1999-09-09 | 2000-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-10 | 2003-09-09 | 2004-03-10 | $7700.00 | Window Closed / Lapsed |