Laser ablation damascene process
Assignee: International Business Machines Corp
•
Filing: 1991-02-01
•
Granted: 1992-03-03
•
Expires: 2011-02-01
Abstract
Abstract A laser ablation damascene process for the planarizing of metal/polymer structures. More specifically, the process is especially adapted for the fabrication of both interlevel via metallization and circuitization layers in integrated circuit (IC) interconnects. Subsequent to the forming or etching of holes or depressions in a polymer insulating layer, a metal layer or film is deposited thereon for the purpose of fabricating vias or trenches for metallization and circulation layers in IC connects. Thereafter, the surface of the metal layer which has been deposited or superimposed on the polymer substrate through any suitable method known in the art is irradiated with at least one laser pulse which will cause the metal layer to melt and reflow and resultingly fill the vias and trenches etched in the polymer substrate while simultaneously ablating and removing the metal from the planarized surface of the substrate in the regions about the vias and trenches.
Inventors
- 👤 Joseph C. Andreshak
- 👤 Robert J. Baseman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:31
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056; H10W20/057; H10P; H10P95/00; H10W20/062; H05; H05K; H05K3/00; H05K3/02; H05K3/027; H05K3/40; H05K3/4038; H05K3/4076; Y; Y10; Y10S; Y10S148/00; Y10S148/093; Y10S438/00; Y10S438/94
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
94 words
A laser ablation damascene process for the planarizing of a surface on a substrate having a surface depression therein, comprising the steps of: (a) depositing a metal layer to at least partially fill said surface depression and to cover the substrate surface about said depression; (b) and applying at least one laser pulse having a fluence optimized in correlation with the characteristics of said metal layer for substantially filling said depression with said metal and concurrently substantially ablating the metal from the surface area on said substrate surrounding said at least one surface depression.
Claim 2
Dependent Claim
94 words
A laser ablation damascene process for the planarizing of a surface on a substrate having a surface depression therein, comprising the steps of: (a) depositing a metal layer to at least partially fill said surface depression and to cover the substrate surface about said depression; (b) and applying at least one laser pulse having a fluence optimized in correlation with the characteristics of said metal layer for substantially filling said depression with said metal and concurrently substantially ablating the metal from the surface area on said substrate surrounding said at least one surface depression.
Claim 3
Dependent Claim
51 words
A laser ablation process as claimed in claim 1, wherein a plurality of said surface depressions form vias and trenches in at least one insulating layer of said substrate, said laser pulse melting said metal in said vias and trenches to produce metallization and circuitization layers in an integrated circuit interconnect.
Claim 4
Dependent Claim
20 words
A laser ablation process as claimed in claim 2, wherein said insulating layer is constituted from an organic insulator material.
Claim 5
Dependent Claim
18 words
A laser ablation process as claimed in claim 2, wherein said insulating layer is constituted from a polyimide.
Claim 6
Dependent Claim
37 words
A laser ablation process as claimed in claim 2 or 3 or 4, wherein said metal layer comprises an adhesion-promoting layer deposited on said insulating layer, and a layer of copper deposited on said metallic adhesion-promoting layer.
Claim 7
Dependent Claim
37 words
A laser ablation process as claimed in claim 5, wherein said polyimide has a thickness of about 2.0μ, said metallic adhesion-promoting layer has a thickness of about 0.2μ, and said copper has a thickness of about 3.2μ.
Claim 8
Dependent Claim
29 words
A laser ablation process as claimed in claim 5 or 6, wherein said metallic adhesion-promoting layer is selected from the group of materials consisting of tantalum, titanium and chromium.
Claim 9
Dependent Claim
40 words
A laser ablation process as claimed in claim 1, wherein said at least one pulse is a 15 ns long, 532 nm, 2.5 J/cm 2 visible laser pulse produced by frequency doubling the 1.04μ output of a pulsed infrared laser.
Claim 10
Dependent Claim
56 words
A laser ablation process as claimed in claim 1, wherein said at least one pulse is a 248 nm, 30 ns long, 4.5 J/cm 2 excimer laser pulse applied to a 1.6 micron layer of copper deposited over damascene trenches in silicone dioxide etched to a depth through the oxide layer to contact the underlying silicon.
Claim 11
Dependent Claim
42 words
A laser ablation process as claimed in claim 1, wherein said at least one pulse is a 248 nm, 30 ns long, 5.0 J/cm 2 excimer laser pulse sputtered into 0.7 micron deep vias etched into approximately 1.0 micron thick silicon dioxide.
Claim 12
Dependent Claim
33 words
A laser ablation process as claimed in claim 1, comprising raising the temperature of said substrate to enable relaxing the energy requirements of the laser pulse and enlarge the window of said process.
Claim 13
Dependent Claim
23 words
A laser ablation process as claimed in claim 1, wherein said laser operates within wavelengths of either the ultraviolet, visible or infrared range.
Claim 14
Dependent Claim
28 words
A laser ablation process as claimed in claim 1, wherein debris formed during said process is removed concurrently with the application of said at least one laser pulse.
References Cited (Backward Citations)
US4674176A
Cited
US4789648A
Cited
US4684437A
Cited
US4920070A
Cited
JPS63215055A
Cited
US4758533A
Cited
US4998239A
Cited
US5024968A
Cited
US5032233A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-03 | 1995-09-02 | 1996-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-03 | 1999-09-02 | 2000-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-03 | 2003-09-02 | 2004-03-03 | $7700.00 | Window Closed / Lapsed |