Process for preparing superconductive thick films
Assignee: Eastman Kodak Co
•
Filing: 1990-07-20
•
Granted: 1992-02-11
•
Expires: 2010-07-20
Abstract
Abstract A process of forming on a substrate a coating of a precursor of a crystalline rare earth alkaline earth copper oxide or heavy pnictide mixed alkaline earth copper oxide electrical conductor and converting the precursor to the crystalline electrical conductor. The coating precursor is provided by (a) preparing a solution comprised of a volatilizable solvent and, as a solute, metal-ligand compounds of each of the metals forming the crystalline electrical conductor, the proportions of the solute metals corresponding to those present in the precursor coating and the ligands being inorganic ligands chosen to be volatilizable on heating, (b) spraying the aqueous solution to form discrete liquid particles each containing the metals as metal-ligand compounds in proportions corresponding to those present in the precursor coating, (c) evaporating at least a portion of the volatilizable solvent fronm the liquid particles to form solid particles each containing the metals as metal-ligand compounds in proportions corresponding to those present in the precursor coating. The solid particles can be formulated as a screen printing composition to facilitate coating on the substrate.
Inventors
- 👤 Laurie A. Strom
- 👤 Edward Carnall, Jr.
- 👤 Steven A. Ferranti
- 👤 Jose M. Mir
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:17
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0548; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/737; Y10S505/739; Y10S505/741
Claims Analysis
Total Claims: 47
Claim 1
Independent Claim
291 words
A process of forming an electrical conductor on a substrate capable of withstanding processing temperatures comprising forming on the substrate a coating of a precursor of a crystalline electrical conductor chosen from the group consisting of (a) a rare earth alkaline earth copper oxide and (b) a heavy pnictide mixed alkaline earth copper oxide and converting the precursor to the crystalline electrical conductor by heating, characterized by the steps of preparing a solution comprised of volatilizable aqueous solvent and, as a solute, inorganic salts forming metal-ligand compounds of each of the metals forming the crystalline electrical conductor, the proportions of the solute metals corresponding to those present in the precursor coating and the ligands being inorganic ligands chosen to be volatilizable on heating, spraying the aqueous solution to form discrete liquid particles each containing the metals as metal-ligand compounds in proportions corresponding to those present in the precursor coating, evaporating at least a portion of the volatilizable solvent from the ligand particles to form solid particles each containing the metals as metalligand compounds in proportions corresponding to those present in the precursor coating, coating the solid particles together with a volatilizable liquid as a paste on the substrate, thereafter heating the solid particles in the presence of oxygen to volatilize the ligands and form the precursor as an intermediate coating on the substrate, and converting the intermediate coating to the crystalline electrical conductor by heating to a temperature in the range of from 900° to 1100° C. when the rare earth alkaline earth copper oxide crystalline electrical conductor is being formed and by heating to a temperature in the range of from 750° to 1000° C. when the heavy pnictide mixed alkaline earth copper oxide crystalline electrical conductor is being formed.
Claim 2
Dependent Claim
291 words
A process of forming an electrical conductor on a substrate capable of withstanding processing temperatures comprising forming on the substrate a coating of a precursor of a crystalline electrical conductor chosen from the group consisting of (a) a rare earth alkaline earth copper oxide and (b) a heavy pnictide mixed alkaline earth copper oxide and converting the precursor to the crystalline electrical conductor by heating, characterized by the steps of preparing a solution comprised of volatilizable aqueous solvent and, as a solute, inorganic salts forming metal-ligand compounds of each of the metals forming the crystalline electrical conductor, the proportions of the solute metals corresponding to those present in the precursor coating and the ligands being inorganic ligands chosen to be volatilizable on heating, spraying the aqueous solution to form discrete liquid particles each containing the metals as metal-ligand compounds in proportions corresponding to those present in the precursor coating, evaporating at least a portion of the volatilizable solvent from the ligand particles to form solid particles each containing the metals as metalligand compounds in proportions corresponding to those present in the precursor coating, coating the solid particles together with a volatilizable liquid as a paste on the substrate, thereafter heating the solid particles in the presence of oxygen to volatilize the ligands and form the precursor as an intermediate coating on the substrate, and converting the intermediate coating to the crystalline electrical conductor by heating to a temperature in the range of from 900° to 1100° C. when the rare earth alkaline earth copper oxide crystalline electrical conductor is being formed and by heating to a temperature in the range of from 750° to 1000° C. when the heavy pnictide mixed alkaline earth copper oxide crystalline electrical conductor is being formed.
Claim 3
Dependent Claim
29 words
A process according to claim 1 further characterized in that the conductor precursor is coated on the substrate in a pattern corresponding to the desired pattern of electrical conductivity.
Claim 4
Dependent Claim
18 words
A process according to claim 1 further characterized in that the solid particles are formed by spray drying.
Claim 5
Dependent Claim
38 words
A process according to claim 3 further characterized in that the liquid particles are generated in the form of a mist in a gaseous medium and the solvent is evaporated from the liquid particles into the gaseous medium.
Claim 6
Dependent Claim
18 words
A process according to claim 1 further characterized in that the paste is screen printed onto the substrate.
Claim 7
Dependent Claim
39 words
A process according to claim 1 further characterized in that evaporation of the solvent is continued until the solid particles form a powder and the powder is then mixed with sufficient liquid to form a paste to facilitate coating.
Claim 8
Dependent Claim
35 words
A process according to claim 1 further characterized in that evaporation of the solvent is discontinued after the solid particles are formed but before the solvent is entirely evaporated so that a paste is formed.
Claim 9
Dependent Claim
27 words
A process according to claim 1 further characterized in that the inorganic salts contain ligand moieties chosen from the group consisting of halide, nitrate, and sulfate anions.
Claim 10
Dependent Claim
19 words
A process according to claim 8 further characterized in that the halide ligand moieties are bromide or chloride anions.
Claim 11
Dependent Claim
16 words
A process according to claim 8 further characterized in that the ligand moieties are, nitrate anions.
Claim 12
Dependent Claim
23 words
A process according to claim 1 further characterized in that the conductor precursor is coated to a thickness of at least 5 μm.
Claim 13
Dependent Claim
27 words
A process according to claim 11 further characterized in that the conductor precursor is coated to a thickness in the range of from 5 to 200 μm.
Claim 14
Dependent Claim
23 words
A process according to claim 11 further characterized in that the conductor precursor is coated to a thickness of at least 10 μm.
Claim 15
Dependent Claim
27 words
A process according to claim 13 further characterized in that the conductor precursor is coated to a thickness in the range of from 10 to 100 μm.
Claim 16
Dependent Claim
20 words
A process according to claim 1 further characterized in that the substrate is strontium titanate, magnesia, alumina or aluminum nitride.
Claim 17
Dependent Claim
23 words
A process according to claim 1 further characterized in that the intermediate coating is converted to an electrically conductive crystalline coating by heating.
Claim 18
Dependent Claim
23 words
A process according to claim 16 further characterized in that the electrically conductive crystalline coating is a rare earth alkaline earth copper oxide.
Claim 19
Dependent Claim
19 words
A process according to claim 17 further characterized in that the crystalline coating is annealed to improve crystalline order.
Claim 20
Dependent Claim
29 words
A process according to claim 18 further characterized in that the crystalline coating is cooled at a rate of 25° C. per minute or less to improve crystalline order.
Claim 21
Dependent Claim
20 words
A process according to claim 17 further characterized in that the crystalline coating is enriched with oxygen following crystal growth.
Claim 22
Dependent Claim
24 words
A process according to claim 16 further characterized in that the electrically conductive crystalline coating is a heavy pnictide mixed alkaline earth copper oxide.
Claim 23
Dependent Claim
42 words
A process according to claim 21 further characterized in that the intermediate coating is converted to a crystalline heavy pnictide mixed alkaline earth calcium copper oxide electrical conductor by heating to a temperature in the range of from 750 to 1000° C.
Claim 24
Dependent Claim
32 words
A process according to claim 22 further characterized in that the intermediate coating is heated in an oxygen containing atmosphere to a temperature in the range of from 850° to 950° C.
Claim 25
Dependent Claim
32 words
A process according to claim 23 further characterized in that the intermediate coating is heated in an oxygen containing atmosphere to a temperature in the range of from 890° to 950° C.
Claim 26
Dependent Claim
48 words
A process according to claim 24 further characterized in that prior to heating to 890° to 950° C. the intermediate coating is heated in an oxygen containing atmosphere for a period of at least 5 minutes at a temperature in the range of from 800° to 885° C.
Claim 27
Dependent Claim
43 words
A process according to claim 24 further characterized in that following heating to 890° to 950° C. the conductive coating produced is further heated in an oxygen containing atmosphere for at least 5 minutes in the temperature range of 870° to 890° C.
Claim 28
Dependent Claim
31 words
A process according to claim 22 further characterized in that the intermediate coating is heated in a non-oxidizing atmosphere to a temperature in the range of from 780° to 850° C.
Claim 29
Dependent Claim
31 words
A process according to claim 27 further characterized in that the intermediate coating is heated in a non-oxidizing atmosphere to a temperature in the range of from 830° to 850° C.
Claim 30
Dependent Claim
42 words
A process according to claim 28 further characterized in that following heating to 830° to 850° C. the conductive coating produced is further heated in a non-oxidizing atmosphere for at least 5 minutes in the temperature range of 780° to 830° C.
Claim 31
Dependent Claim
35 words
A process according to claim 29 further characterized in that following heating to 780° to 830° C. the conductive coating is heated in an oxygen containing atmosphere to a temperature of at least 480° C.
Claim 32
Dependent Claim
80 words
A process according to claim 1 further characterized in that the heavy pnictide consists essentially of bismuth and from 0 to 30 mole percent of one or a combination of antimony and lead, based on total heavy pnictide, and the mixed alkaline earth consists essentially of heavy alkaline earth and calcium in a 3:1 to 1:3 molar ratio, where the heavy alkaline earth is strontium and from 0 to 30 mole percent barium, based on the total heavy alkaline earth.
Claim 33
Dependent Claim
297 words
A process of forming an electrical conductor on an aluminum oxide, magnesium oxide or aluminum nitride substrate comprising forming a coating of a precursor of a crystalline heavy pnictide mixed alkaline earth copper oxide electrical conductor on the substrate and converting the precursor to a crystalline heavy pnictide mixed alkaline earth copper oxide electrical conductor that becomes superconducting on cooling, characterized by the steps of preparing an aqueous solution of nitrate, sulfate or halide salts of each of the metals forming the precursor coating, spraying the aqueous solution to form discrete liquid particles each containing the metals as the nitrate, sulfate or halide salts in proportions corresponding to those present in the precursor coating, evaporating water from the liquid particles to form solid particles each containing the metals as nitrate, sulfate or halide salts in proportions corresponding to precursor coating, coating the solid particles as an aqueous paste on the substrate, thereafter heating the coating of solid particles in the presence of oxygen to form the precursor coating from which the nitrate, sulfate or halide moieties have been volatilized, and converting the precursor coating to the crystalline heavy pnictide mixed alkaline earth copper oxide film by heating to a temperature in the range of from 750° to 1000° C., the solid particles, the paste and the precursor coating each containing the following proportions of metals: P.sub.a A.sub.b-c Ca.sub.c Cu.sub.d where P is a heavy pnictide consisting essentially of bismuth and from 1 to 30 mole percent of one or a combination of antimony and lead, A is heavy alkaline earth consisting essentially of strontium and from 0 to 10 mole percent barium, a ranges from 2 to 5, b ranges from 3 to 4, c ranges from 0.5 to 2 and d ranges from 2 to 5.
Claim 34
Dependent Claim
297 words
A process of forming an electrical conductor on an aluminum oxide, magnesium oxide or aluminum nitride substrate comprising forming a coating of a precursor of a crystalline heavy pnictide mixed alkaline earth copper oxide electrical conductor on the substrate and converting the precursor to a crystalline heavy pnictide mixed alkaline earth copper oxide electrical conductor that becomes superconducting on cooling, characterized by the steps of preparing an aqueous solution of nitrate, sulfate or halide salts of each of the metals forming the precursor coating, spraying the aqueous solution to form discrete liquid particles each containing the metals as the nitrate, sulfate or halide salts in proportions corresponding to those present in the precursor coating, evaporating water from the liquid particles to form solid particles each containing the metals as nitrate, sulfate or halide salts in proportions corresponding to precursor coating, coating the solid particles as an aqueous paste on the substrate, thereafter heating the coating of solid particles in the presence of oxygen to form the precursor coating from which the nitrate, sulfate or halide moieties have been volatilized, and converting the precursor coating to the crystalline heavy pnictide mixed alkaline earth copper oxide film by heating to a temperature in the range of from 750° to 1000° C., the solid particles, the paste and the precursor coating each containing the following proportions of metals: P.sub.a A.sub.b-c Ca.sub.c Cu.sub.d where P is a heavy pnictide consisting essentially of bismuth and from 1 to 30 mole percent of one or a combination of antimony and lead, A is heavy alkaline earth consisting essentially of strontium and from 0 to 10 mole percent barium, a ranges from 2 to 5, b ranges from 3 to 4, c ranges from 0.5 to 2 and d ranges from 2 to 5.
Claim 35
Dependent Claim
57 words
A process according to claim 32 in which the solution, the solid particles, the paste and the precursor coating each contain the metals in the following proportions: Bi.sub.a Sr.sub.b-c Ca.sub.c Cu.sub.d where a ranges from 2 to 5, b ranges from 3 to 4, c ranges from 0.5 to 2 and d ranges from 2 to 5.
Claim 36
Dependent Claim
207 words
A process of forming an electrical conductor on an aluminum oxide, magnesium oxide or strontium titanate substrate comprising forming a coating of a precursor of a crystalline rare earth alkaline earth copper oxide electrical conductor on the substrate and converting the precursor to a crystalline rare earth mixed alkaline earth copper oxide electrical conductor that becomes superconducting on cooling, characterized by the steps of preparing an aqueous solution of nitrate, sulfate or halide salts of each of the metals forming the precursor coating, spraying the aqueous solution to form discrete liquid particles each containing the metals as the nitrate, sulfate or halide salts in proportions corresponding to those present in the precursor coating, evaporating water from the liquid particles to form solid particles each containing the metals as nitrate, sulfate or halide salts in proportions corresponding to precursor coating, coating the solid particles as an aqueous paste on the substrate, thereafter heating the coating of solid particles in the presence of oxygen to form the precursor coating from which the nitrate, sulfate or halide moieties have been volatilized, and converting the precursor coating to the crystalline rare earth alkaline earth copper oxide film by heating to a temperature in the range of from 900° to 1100° C.
Claim 37
Dependent Claim
207 words
A process of forming an electrical conductor on an aluminum oxide, magnesium oxide or strontium titanate substrate comprising forming a coating of a precursor of a crystalline rare earth alkaline earth copper oxide electrical conductor on the substrate and converting the precursor to a crystalline rare earth mixed alkaline earth copper oxide electrical conductor that becomes superconducting on cooling, characterized by the steps of preparing an aqueous solution of nitrate, sulfate or halide salts of each of the metals forming the precursor coating, spraying the aqueous solution to form discrete liquid particles each containing the metals as the nitrate, sulfate or halide salts in proportions corresponding to those present in the precursor coating, evaporating water from the liquid particles to form solid particles each containing the metals as nitrate, sulfate or halide salts in proportions corresponding to precursor coating, coating the solid particles as an aqueous paste on the substrate, thereafter heating the coating of solid particles in the presence of oxygen to form the precursor coating from which the nitrate, sulfate or halide moieties have been volatilized, and converting the precursor coating to the crystalline rare earth alkaline earth copper oxide film by heating to a temperature in the range of from 900° to 1100° C.
Claim 38
Dependent Claim
44 words
A process according to claim 34 further characterized in that the solid particles, the paste and the precursor coating each containing the following proportions of metals: L.sub.2-x :M.sub.x :Cu where L is lanthanide. M is alkaline earth metal, and x is 0.05 to 0.30.
Claim 39
Dependent Claim
13 words
A process according to claim 35 further characterized in that L is lanthanum.
Claim 40
Dependent Claim
50 words
A process according to claim 34 further characterized in that the solid particles, the paste and the precursor coating each containing the following proportions of metals: R.sub.1 :A.sub.2 :Cu.sub.3 where R is rare earth and A is barium or barium in combination with at least one of calcium and strontium.
Claim 41
Dependent Claim
13 words
A process according to claim 37 further characterized in that R is yttrium.
Claim 42
Dependent Claim
198 words
A process of forming on an insulative substrate providing a perovskite crystal structure a conductor comprised of a crystalline rare earth alkaline earth copper oxide layer which exhibits a superconducting onset transition temperature in excess of 77° K. and is comprised of a R 1 A 2 C 3 crystalline phase comprising forming a solution comprised of water as an evaporative solvent and as solute water soluble thermally volatilizable inorganic salts forming metal-ligand compounds of each of rare earth, alkaline earth, and copper, spraying the solution to form liquid particles, removing sufficient solvent from the liquid particles to convert the liquid particles to solid particles containing the metal-ligand compounds, coating a paste comprised of water and the solid particles as a conductor precursor on the insulative substrate, heating the coated conductor precursor in the presence of oxygen to form an intermediate coating on the substrate, and converting the intermediate coating to the crystalline rare earth alkaline earth copper oxide electrical conductor in the presence of oxygen by heating to a temperature in the range of from 900° to 1100° C. and cooling at a rate of 25° C. or less per minute to a temperature of 500° C.
Claim 43
Dependent Claim
198 words
A process of forming on an insulative substrate providing a perovskite crystal structure a conductor comprised of a crystalline rare earth alkaline earth copper oxide layer which exhibits a superconducting onset transition temperature in excess of 77° K. and is comprised of a R 1 A 2 C 3 crystalline phase comprising forming a solution comprised of water as an evaporative solvent and as solute water soluble thermally volatilizable inorganic salts forming metal-ligand compounds of each of rare earth, alkaline earth, and copper, spraying the solution to form liquid particles, removing sufficient solvent from the liquid particles to convert the liquid particles to solid particles containing the metal-ligand compounds, coating a paste comprised of water and the solid particles as a conductor precursor on the insulative substrate, heating the coated conductor precursor in the presence of oxygen to form an intermediate coating on the substrate, and converting the intermediate coating to the crystalline rare earth alkaline earth copper oxide electrical conductor in the presence of oxygen by heating to a temperature in the range of from 900° to 1100° C. and cooling at a rate of 25° C. or less per minute to a temperature of 500° C.
Claim 44
Dependent Claim
198 words
A process of forming on an insulative magnesia substrate providing a perovskite crystal structure a conductor comprised of a crystalline rare earth alkaline copper oxide layer which exhibits a superconducting onset transition temperature in excess of 77° K. and is comprised of a R 1 A 2 C 3 crystalline phase comprising forming a solution comprised of water as an evaporative solvent and as solute water soluble thermally volatilizable inorganic salts forming metal-ligand compounds of each of rare earth, alakline earth, and copper, spraying the solution to form liquid particles, removing sufficient solvent from the liquid particles to convert the liquid particles to solid particles containing the metal-ligand compounds, coating a paste comprised of water and the solid particles as a conductor precursor on the insulative substrate, heating the coated conductor precursor in the presence of oxygen to form an intermediate coating on the substrate, and converting the intermediate coating to the crystalline rare earth alkaline earth copper oxide electrical conductor in the presence of oxygen by heating to a temperature in the range of from 900° to 1100° C. and cooling at a rate of 25° C. or less per minute to a temperature of 500° C.
Claim 45
Dependent Claim
198 words
A process of forming on an insulative magnesia substrate providing a perovskite crystal structure a conductor comprised of a crystalline rare earth alkaline copper oxide layer which exhibits a superconducting onset transition temperature in excess of 77° K. and is comprised of a R 1 A 2 C 3 crystalline phase comprising forming a solution comprised of water as an evaporative solvent and as solute water soluble thermally volatilizable inorganic salts forming metal-ligand compounds of each of rare earth, alakline earth, and copper, spraying the solution to form liquid particles, removing sufficient solvent from the liquid particles to convert the liquid particles to solid particles containing the metal-ligand compounds, coating a paste comprised of water and the solid particles as a conductor precursor on the insulative substrate, heating the coated conductor precursor in the presence of oxygen to form an intermediate coating on the substrate, and converting the intermediate coating to the crystalline rare earth alkaline earth copper oxide electrical conductor in the presence of oxygen by heating to a temperature in the range of from 900° to 1100° C. and cooling at a rate of 25° C. or less per minute to a temperature of 500° C.
Claim 46
Dependent Claim
198 words
A process of forming on an insulative alumina substrate providing a perovskite crystal structure a conductor comprised of a crystalline rare earth alkaline copper oxide layer which exhibits a superconducting onset transition temperature in excess of 77° K. and is comprised of a R 1 R 2 C 3 crystalline phase comprising forming a solution comprised of water as an evaporative solvent and as solute water soluble thermally volatilizable inorganic salts forming metal-ligand compounds of each of rare earth, alkaline earth, and copper, spraying the solution to form liquid particles, removing sufficient solvent from the liquid particles to convert the liquid particles to solid particles containing the metal-ligand compounds, coating a paste comprised of water and the solid particles as a conductor precursor on the insulative substrate, heating the coated conductor precursor in the presence of oxygen to form an intermediate coating on the substrate, and converting the intermediate coating to the crystalline rare earth alkaline earth copper oxide electrical conductor in the presence of oxygen by heating to a temperature in the range of from 900° to 1100° C. and cooling at a rate of 25° C. or less per minute to a temperature of 500° C.
Claim 47
Dependent Claim
198 words
A process of forming on an insulative alumina substrate providing a perovskite crystal structure a conductor comprised of a crystalline rare earth alkaline copper oxide layer which exhibits a superconducting onset transition temperature in excess of 77° K. and is comprised of a R 1 R 2 C 3 crystalline phase comprising forming a solution comprised of water as an evaporative solvent and as solute water soluble thermally volatilizable inorganic salts forming metal-ligand compounds of each of rare earth, alkaline earth, and copper, spraying the solution to form liquid particles, removing sufficient solvent from the liquid particles to convert the liquid particles to solid particles containing the metal-ligand compounds, coating a paste comprised of water and the solid particles as a conductor precursor on the insulative substrate, heating the coated conductor precursor in the presence of oxygen to form an intermediate coating on the substrate, and converting the intermediate coating to the crystalline rare earth alkaline earth copper oxide electrical conductor in the presence of oxygen by heating to a temperature in the range of from 900° to 1100° C. and cooling at a rate of 25° C. or less per minute to a temperature of 500° C.
References Cited (Backward Citations)
US4336242A
Cited
JPS5685814A
Cited
US4395436A
Cited
US4326785A
Cited
US4571350A
Cited
US4880770A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-10 | 1995-08-12 | 1996-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-10 | 1999-08-12 | 2000-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-10 | 2003-08-12 | 2004-02-11 | $7700.00 | Window Closed / Lapsed |