Assignee: Eastman Kodak Co
•
Filing: 1987-05-04
•
Granted: 1989-11-14
•
Expires: 2007-05-04
Abstract
Abstract A metalorganic deposition method is disclosed for manufacturing a superconducting oxide film on a substrate, in which a mixed metalorganic precursor is coated and heated to its thermal decomposition temperature to create an amorphous mixed metal oxide layer. The amorphous layer is then converted to a crystalline coating by further heating followed by cooling in the presence of O 2 atmosphere.
Inventors
- 👤 Jose M. Mir
- 👤 John A. Agostinelli
- 👤 David L. Peterson
- 👤 Gustavo R. Paz-Pujalt
- 👤 Brian J. Higberg
- 👤 Gopalan Rajeswaran
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 03:02
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C04B35/00; C04B35/01; C04B35/45; C04B35/4504; C04B41/45; C04B41/50; C04B41/5025; C04B41/80; C04B41/81; C04B41/85; C04B41/87; C23; C23C; C23C26/00; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0324; H10N60/0801; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/23; C04B2111/00; C04B2111/00474; C04B2111/00844
Claims Analysis
Total Claims: 50
Claim 1
Independent Claim
141 words
A process of forming a uniform electrically conductive metal oxide coating on a substrate comprising applying to the substrate a coating of a solution consisting essentially of a volatilizable film forming solvent, an organic film promoting agent chosen from the class consisting of 2-ethylhexanoic acid, rosin, ethyl lactate, 2-ethoxyethyl acetate, and a terpene containing from 10 to 30 carbon atoms, metal-ligand compounds of each of rare earth and alkaline earth containing at least one thermally volatilizable organic ligand, and at least one copper-ligand compound containing a thermally volatilizable carboxylate ligand, removing the solvent, organic film promoting agent, and ligands from the substrate by heating in the presence of oxygen to form an amorphous rare earth alkaline earth copper oxide coating of less than 1 μm in thickness on the substrate and forming a crystalline conductive metal oxide coating on the substrate.
Claim 2
Dependent Claim
141 words
A process of forming a uniform electrically conductive metal oxide coating on a substrate comprising applying to the substrate a coating of a solution consisting essentially of a volatilizable film forming solvent, an organic film promoting agent chosen from the class consisting of 2-ethylhexanoic acid, rosin, ethyl lactate, 2-ethoxyethyl acetate, and a terpene containing from 10 to 30 carbon atoms, metal-ligand compounds of each of rare earth and alkaline earth containing at least one thermally volatilizable organic ligand, and at least one copper-ligand compound containing a thermally volatilizable carboxylate ligand, removing the solvent, organic film promoting agent, and ligands from the substrate by heating in the presence of oxygen to form an amorphous rare earth alkaline earth copper oxide coating of less than 1 μm in thickness on the substrate and forming a crystalline conductive metal oxide coating on the substrate.
Claim 3
Dependent Claim
49 words
A process according to claim 1 in which the crystalline conductive metal oxide coating is formed on the substrate by heating the amorphous oxide coating to a temperature in the range of from 900° to 1100° C. followed by contact with air or an oxygen enriched atmosphere during cooling.
Claim 4
Dependent Claim
17 words
A process according to claim 1 in which said ligands each contain less than 30 carbon atoms.
Claim 5
Dependent Claim
16 words
A process according to claim 3 in which said ligands contain at least 4 carbon atoms.
Claim 6
Dependent Claim
15 words
A process according to claim 4 in which said ligands contain branched carbon atom chains.
Claim 7
Dependent Claim
22 words
A process according to claim 5 in which said ligands of copper are carboxylates which contain from 6 to 20 carbon atoms.
Claim 8
Dependent Claim
29 words
A process according to claim 5 in which said ligands of each of rare earth, alkaline earth, and copper are carboxylates which contain from 6 to 20 carbon atoms.
Claim 9
Dependent Claim
35 words
A process according to claim 1 in which the substrate is a flexible elongated substrate and the coating is applied to the substrate by drawing the substrate upwardly out of a reservoir containing the solution.
Claim 10
Dependent Claim
159 words
A process of preparing an article comprised of a substrate and a crystalline electrically conductive rare earth alkaline earth copper oxide coating on the substrate exhibiting a T c in excess of 30° K. comprising choosing the substrate from the class consisting of strontium titanate, magnesia, and alumina, applying to the substrate a coating of a solution consisting essentially of a volatilizable film forming solvent, metal-ligand compounds of each of rare earth and alkaline earth containing at least one thermally volatilizable organic ligand, and at least one copper-ligand compound containing a thermally volatilizable carboxylate ligand, removing the solvent and organic ligands from the substrate by heating in the presence of oxygen to form a coating of less than 1 μm in thickness, and forming a crystalline conductive metal oxide coating on the substrate by heating to a temperature in the range of from 900° to 1100° C. followed by contact with air or an oxygen enriched atmosphere during cooling.
Claim 11
Dependent Claim
159 words
A process of preparing an article comprised of a substrate and a crystalline electrically conductive rare earth alkaline earth copper oxide coating on the substrate exhibiting a T c in excess of 30° K. comprising choosing the substrate from the class consisting of strontium titanate, magnesia, and alumina, applying to the substrate a coating of a solution consisting essentially of a volatilizable film forming solvent, metal-ligand compounds of each of rare earth and alkaline earth containing at least one thermally volatilizable organic ligand, and at least one copper-ligand compound containing a thermally volatilizable carboxylate ligand, removing the solvent and organic ligands from the substrate by heating in the presence of oxygen to form a coating of less than 1 μm in thickness, and forming a crystalline conductive metal oxide coating on the substrate by heating to a temperature in the range of from 900° to 1100° C. followed by contact with air or an oxygen enriched atmosphere during cooling.
Claim 12
Dependent Claim
24 words
A process according to claim 9 further characterized in that the coating and the solvent and ligand removal steps are repeated prior to crystallization.
Claim 13
Dependent Claim
34 words
A process according to claim 10 in which the coating and the ligand and solvent removal steps are repeated 3 to 10 times prior to heating to form the crystalline conductive metal oxide coating.
Claim 14
Dependent Claim
40 words
A process according to claim 9 in which the solvent additionally contains an organic film promoting agent chosen from the group consisting of 2-ethylhexanoic acid, rosin, ethyl lactate, 2-ethoxyethyl acetate, and a terpene containing from 10 to 30 carbon atoms.
Claim 15
Dependent Claim
38 words
A process according to claim 9 in which the crystalline conductive metal oxide coating contains a superconductive R 1 A 2 C 3 phase, where R, A, and C represent rare earth, alkaline earth, and copper elements, respectively.
Claim 16
Dependent Claim
23 words
A process according to claim 9 further characterized in that the coating is heated to its crystallization temperature by exposure to electromagnetic radiation.
Claim 17
Dependent Claim
18 words
A process according to claim 14 further characterized in that the electromagnetic radiation is absorbed by the coating.
Claim 18
Dependent Claim
21 words
A process according to claim 15 further characterized in that the substrate is chosen to be transmissive to the electromagnetic radiation.
Claim 19
Dependent Claim
21 words
A process according to claim 14 further characterized in that the electromagnetic radiation is coherent monochromatic radiation supplied from a laser.
Claim 20
Dependent Claim
22 words
A process according to claim 17 further characterized in that the laser is employed to form a crystalline pattern on the substrate.
Claim 21
Dependent Claim
49 words
A process according to claim 9 further characterized in that the coating is converted to a crystalline coating by heating the coating to a temperature at which nucleation of rare earth alkaline earth copper oxide crystals is achieved and then growing these crystals to larger sizes by further heating.
Claim 22
Dependent Claim
22 words
A process according to claim 19, further characterized in that the crystals are grown at a higher temperature than their nucleation temperature.
Claim 23
Dependent Claim
19 words
A process according to claim 19 further characterized in that the crystalline coating is annealed to improve crystalline order.
Claim 24
Dependent Claim
29 words
A process according to claim 21 further characterized in that the crystalline coating is cooled at a rate of 25° C. per minute or less to improve crystalline order.
Claim 25
Dependent Claim
20 words
A process according to claim 19 further characterized in that the crystalline coating is enriched with oxygen following crystal growth.
Claim 26
Dependent Claim
59 words
A process according to claim 9 in which after applying the coating to the substrate and before heating to form the crystalline conductive oxide coating forming a photoresist pattern on the coating, thereby leaving a portion of the coating unprotected by the photoresist, removing the portion of the coating not protected by the photoresist pattern, and removing the photoresist.
Claim 27
Dependent Claim
203 words
A process of preparing an article comprised of a substrate and a coating on the substrate exhibiting a T c in excess of 30° K. containing greater than 45 percent by volume a tetragonal K 2 NiF 4 crystalline phase satisfying the metal ratio: L.sub.2-x :M.sub.x :Cu where L is lanthanum, M is alkaline earth metal which is at least one of barium and strontium, and x is 0.05 to 0.30, said process comprising coating onto the substrate a solution consisting essentially of a volatilizable film forming solvent and metal-ligand compounds of each of the lanthanum, alkaline earth, and copper containing at least one thermally volatilizable ligand, removing the solvent and ligands from the, substrate, this step including heating in the presence of oxygen to form an amorphous lanthanum alkaline earth copper oxide coating on the substrate, heating the amorphous coating to a temperature in the range of from 925° to 975° C. to form the crystalline phase, effecting crystal growth by heating in the temperature range of from 975° to 1050° C., and cooling the coating in the presence of oxygen at a rate of less than 25° C. per minute until it reaches a temperature of from 550° to 450° C.
Claim 28
Dependent Claim
203 words
A process of preparing an article comprised of a substrate and a coating on the substrate exhibiting a T c in excess of 30° K. containing greater than 45 percent by volume a tetragonal K 2 NiF 4 crystalline phase satisfying the metal ratio: L.sub.2-x :M.sub.x :Cu where L is lanthanum, M is alkaline earth metal which is at least one of barium and strontium, and x is 0.05 to 0.30, said process comprising coating onto the substrate a solution consisting essentially of a volatilizable film forming solvent and metal-ligand compounds of each of the lanthanum, alkaline earth, and copper containing at least one thermally volatilizable ligand, removing the solvent and ligands from the, substrate, this step including heating in the presence of oxygen to form an amorphous lanthanum alkaline earth copper oxide coating on the substrate, heating the amorphous coating to a temperature in the range of from 925° to 975° C. to form the crystalline phase, effecting crystal growth by heating in the temperature range of from 975° to 1050° C., and cooling the coating in the presence of oxygen at a rate of less than 25° C. per minute until it reaches a temperature of from 550° to 450° C.
Claim 29
Dependent Claim
17 words
A process according to claim 25 in which said metal-ligand compound of copper is a copper carboxylate.
Claim 30
Dependent Claim
17 words
A process according to claim 26 in which said ligands each contain less than 30 carbon atoms.
Claim 31
Dependent Claim
16 words
A process according to claim 27 in which said ligands contain at least 4 carbon atoms.
Claim 32
Dependent Claim
15 words
A process according to claim 28 in which said ligands contain branched carbon atom chains.
Claim 33
Dependent Claim
22 words
A process according to claim 29 in which said ligands of copper are carboxylates which contain from 6 to 20 carbon atoms.
Claim 34
Dependent Claim
28 words
A process according to claim 29 in which said ligands of each of lanthanum, alkaline earth, and copper are carboxylates which contain from 6 to 20 carbon atoms.
Claim 35
Dependent Claim
40 words
A process according to claim 25 in which said solution additionally contains an organic film promoting agent chosen from the group consisting of 2-ethylhexanoic acid, rosin, ethyl lactate, 2-ethoxyethyl acetate, and a terpene containing from 10 to 30 carbon atoms.
Claim 36
Dependent Claim
15 words
A process according to claim 25 in which the substrate presents a perovskite crystal surface.
Claim 37
Dependent Claim
13 words
A process according to claim 33 in which the substrate is strontium titanate.
Claim 38
Dependent Claim
14 words
A process according to claim 25 in which the substrate is alumina or magnesia.
Claim 39
Dependent Claim
185 words
A process of preparing an article comprised of a substrate and a coating on the substrate exhibiting a T c in excess of 30° K. containing at least 45 percent by volume of an orthorhombic crystalline phase satisfying the metal ratio: Y:M.sub.2 :Cu.sub.3 where M is barium, optionally in combination with at least one of strontium and calcium, said process comprising, coating onto the substrate a solution consisting essentially of a volatilizable film forming solvent and metal-ligand compounds of each of the metals Y, M, and Cu containing at least one thermally volatilizable ligand, said metal-ligand compound of copper being a copper carboxylate, removing the solvent and ligands from the substrate, this step including heating in the presence of oxygen to form an amorphous rare earth alkaline earth copper oxide coating on the substrate, heating the amorphous coating to a temperature in the range of from 900° to 950° C. to form the crystalline phase, and cooling the coating in the presence of oxygen at a rate of less than 25° C. per minute until it reaches a temperature of from 750° to 400° C.
Claim 40
Dependent Claim
185 words
A process of preparing an article comprised of a substrate and a coating on the substrate exhibiting a T c in excess of 30° K. containing at least 45 percent by volume of an orthorhombic crystalline phase satisfying the metal ratio: Y:M.sub.2 :Cu.sub.3 where M is barium, optionally in combination with at least one of strontium and calcium, said process comprising, coating onto the substrate a solution consisting essentially of a volatilizable film forming solvent and metal-ligand compounds of each of the metals Y, M, and Cu containing at least one thermally volatilizable ligand, said metal-ligand compound of copper being a copper carboxylate, removing the solvent and ligands from the substrate, this step including heating in the presence of oxygen to form an amorphous rare earth alkaline earth copper oxide coating on the substrate, heating the amorphous coating to a temperature in the range of from 900° to 950° C. to form the crystalline phase, and cooling the coating in the presence of oxygen at a rate of less than 25° C. per minute until it reaches a temperature of from 750° to 400° C.
Claim 41
Dependent Claim
25 words
A process according to claim 36 in which the amorphous coating is heated to a temperature in the range of from 920° to 930° C.
Claim 42
Dependent Claim
17 words
A process according to claim 36 in which said ligands each contain less than 30 carbon atoms.
Claim 43
Dependent Claim
16 words
A process according to claim 38 in which said ligands contain at least 4 carbon atoms.
Claim 44
Dependent Claim
15 words
A process according to claim 39 in which said ligands contain branched carbon atom chains.
Claim 45
Dependent Claim
22 words
A process according to claim 40 in which said ligands of copper are carboxylates which contain from 6 to 20 carbon atoms.
Claim 46
Dependent Claim
29 words
A process according to claim 36 in which said ligands of each of the metals Y, M, and Cu are carboxylates which contain from 6 to 20 carbon atoms.
Claim 47
Dependent Claim
40 words
A process according to claim 36 in which said solution additionally contains an organic film promoting agent chosen from the group consisting of 2-ethylhexanoic acid, rosin, ethyl lactate, 2-ethoxyethyl acetate, and a terpene containing from 10 to 30 carbon atoms.
Claim 48
Dependent Claim
15 words
A process according to claim 36 in which the substrate presents a perovskite crystal surface.
Claim 49
Dependent Claim
13 words
A process according to claim 44 in which the substrate is strontium titanate.
Claim 50
Dependent Claim
14 words
A process according to claim 36 in which the substrate is alumina or magnesia.
References Cited (Backward Citations)
US3873341A
Cited
US4239816A
Cited
US4316785A
Cited
US4401474A
Cited
US4395436A
Cited
US4496398A
Cited
US4418099A
Cited
US4507643A
Cited
US4485094A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-13 | 1993-05-15 | 1993-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-13 | 1997-05-15 | 1997-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-13 | 2001-05-15 | 2001-11-14 | $7700.00 | Window Closed / Lapsed |