Process of producing porous ceramics

Claim 2

A process of producing a porous ceramic, which comprises forming an inverted emulsion having a sinterable ceramic powder in the oil phase thereof from a mixture of (a) an emulsifying agent (b) 10 to 50 parts by weight of a mixture of at least one polymerizable monofunctional unsaturated compound having one polymerizable unsaturated bond and at least one polymerizable polyfunctional unsaturated compound (c) 10 to 300 parts by weight of water and (d) 100 parts by weight of said sinterable ceramic powder, radical-polymerizing or redox-polymerizing said mixture of said polymerizable monofunctional unsaturated compound and said polymerizable polyfunctional unsaturated compound in said inverted emulsion to cure and crosslink said mixture of said unsaturated compounds in said inverted emulsion and thereby form a cured crosslinked product, drying said cured crosslinked product to remove water and thereby form a porous cured product having cell walls comprising said sinterable ceramic powder and an organic binder material formed by said polymerization of said unsaturated compounds, and then firing said porous cured product to combust said organic binder material in said cell walls and to sinter said sinterable ceramic powder in said cell walls to form said porous ceramic.

Claim 3

The process of producing a porous ceramic as claimed in claim 1, wherein said porous ceramic comprises pores of from 1 μm to 10 μm, said pores are continuous pores, and said sintered ceramic powder forms a continuous layer.

Claim 4

The process of producing a porous ceramic as claimed in claim 1, wherein said porous cured product is fired at a firing temperature of at least 1000° C.

Claim 5

The process of producing a porous ceramic as claimed in claim 1, wherein the amount of said emulsifying agent in said inverted emulsion is from 5 to 100 parts by weight per 100 parts by weight of said mixture of said polymerizable unsaturated compounds.

Claim 6

The process of producing a porous ceramic as claimed in claim 1, wherein a polymerization initiator exists in said inverted emulsion in an amount of from 0.02 to 5 parts by weight per 100 parts by weight of said mixture of said polymerizable unsaturated compounds.

Claim 7

The process of producing a porous ceramic as claimed in claim 1, wherein the polymerization temperature of said polymerizable unsaturated compounds in said inverted emulsion is not more than 100° C.

Claim 8

The process of producing a porous ceramic as claimed in claim 1, wherein the polymerization time of said polymerizable unsaturated compounds in said inverted emulsion is from 1 hour to 48 hours.

Claim 9

The process of producing a porous ceramic as claimed in claim 1, wherein said porous cured product is fired at a temperature raising speed of from 1 to 200° C./hr. and at a firing temperature of at least 1000° C.

Claim 10

A process of producing a porous ceramic, which comprises forming an inverted emulsion having a sinterable ceramic powder in the oil phase thereof from a mixture of (a) an emulsifying agent selected from the group consisting of sorbitan tristearate, sorbitan monostearate, sorbitan monooleate, sorbitan sesquiolate and sorbitan monopalmitate, (b) 10 to 50 parts by weight of a mixture of at least one polymerizable unsaturated compound having one polymerizable unsaturated bond and at least one polymerizable polyfunctional unsaturated compound, (c) 10 to 300 parts by weight of water and (d) 100 parts by weight of said sinterable ceramic powder, radical-polymerizing or redoxpolymerizing said mixture of said polymerizable monofunctional unsaturated compound and said polymerizable polyfunctional unsaturated compound in said inverted emulsion to cure and crosslink said mixture of said unsaturated compounds in said inverted emulsion and thereby form a cured crosslinked product, drying said cured crosslinked product to remove water and thereby form a porous cured product having cell walls comprising said sinterable ceramic powder and an organic binder material formed by said polymerization of said unsaturated compounds said organic binder material in said cell walls and to sinter said sinterable ceramic powder in said cell walls to form said porous ceramic.

Claim 11

A process of producing a porous ceramic, which comprises forming an inverted emulsion having a sinterable ceramic powder in the oil phase thereof from a mixture of (a) an emulsifying agent selected from the group consisting of sorbitan tristearate, sorbitan monostearate, sorbitan monooleate, sorbitan sesquiolate and sorbitan monopalmitate, (b) 10 to 50 parts by weight of a mixture of at least one polymerizable unsaturated compound having one polymerizable unsaturated bond and at least one polymerizable polyfunctional unsaturated compound, (c) 10 to 300 parts by weight of water and (d) 100 parts by weight of said sinterable ceramic powder, radical-polymerizing or redoxpolymerizing said mixture of said polymerizable monofunctional unsaturated compound and said polymerizable polyfunctional unsaturated compound in said inverted emulsion to cure and crosslink said mixture of said unsaturated compounds in said inverted emulsion and thereby form a cured crosslinked product, drying said cured crosslinked product to remove water and thereby form a porous cured product having cell walls comprising said sinterable ceramic powder and an organic binder material formed by said polymerization of said unsaturated compounds said organic binder material in said cell walls and to sinter said sinterable ceramic powder in said cell walls to form said porous ceramic.

Claim 12

A process of producing a porous ceramic as claimed in claim 9, wherein said porous cured product is fired at a firing temperature of at least 1000° C.

Claim 13

The process of producing a porous ceramic as claimed in claim 9 wherein said polyfunctional unsaturated compound is divinylbenzene, ethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, ethylene glycol diacrylate, trimethylolpropane triacrylate, diallyl phthalate, or an unsaturated polyester.