Method of producing a superconductive body, and apparatus and systems comprising the body
Assignee: Nokia of America Corp
•
Filing: 1987-05-12
•
Granted: 1992-01-14
•
Expires: 2007-05-12
Abstract
Abstract Disclosed are normal metal-clad superconductive bodies (e.g., wires, ribbons) having a normal metal cladding that is porous during at least a part of the manufacture of the body. The porous cladding permits access of an ambient atmosphere to the superconductive material. Exemplarily, the superconductive material is an oxide such as a (Ba, Y) cuprate, the normal metal cladding comprises Ag particles (or Ag-coated particles), and the body is treated in an oxygen-containing atmosphere. Techniques for producing such a body are also disclosed.
Inventors
- 👤 Sungho Jin
- 👤 Richard C. Sherwood
- 👤 Thomas H. Tiefel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:31
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0801; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12736
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
130 words
Method of producing a normal metal-clad superconductive body, the method comprising a) forming an intermediate body comprising normal metal cladding material surrounding a quantity of material that comprises superconductive oxide material; b) forming the body from the intermediate body by means of one or more shape-changing operations; and c) heat treating the body such that substantial sintering of the material occurs, and such that, after completion of the heat treatment, the chemical composition of the oxide material is within predetermined limits that are associated with the occurrence of superconductivity in the oxide material; Characterized in that at least during a part of c) the normal metal cladding material surrounding the material is a substantially porous material, such that an ambient oxygen-containing atmosphere can come into contact with the oxide material.
Claim 2
Dependent Claim
130 words
Method of producing a normal metal-clad superconductive body, the method comprising a) forming an intermediate body comprising normal metal cladding material surrounding a quantity of material that comprises superconductive oxide material; b) forming the body from the intermediate body by means of one or more shape-changing operations; and c) heat treating the body such that substantial sintering of the material occurs, and such that, after completion of the heat treatment, the chemical composition of the oxide material is within predetermined limits that are associated with the occurrence of superconductivity in the oxide material; Characterized in that at least during a part of c) the normal metal cladding material surrounding the material is a substantially porous material, such that an ambient oxygen-containing atmosphere can come into contact with the oxide material.
Claim 3
Dependent Claim
26 words
Method of claim 1, comprising providing a normal metal cladding material that comprises a metal selected from the group consisting of Au, Ag, Pt, and Pd.
Claim 4
Dependent Claim
35 words
Method of claim 1, wherein the body is an elongate body, and comprising providing a material that comprises (Ba, Y) cuprate powder or (La, Ba) cuprate powder, and normal metal cladding material that comprises Ag.
Claim 5
Dependent Claim
86 words
Method of claim 1, wherein a) comprises i) providing a substantially tubular outer jacket and an inner member positioned in the bore of the outer jacket such that a substantially annular space is defined; ii) substantially filling the annular space with a normal metal powder; and iii) removing the inner member such that a substantially cylindrical space surrounded by porous normal metal results, and substantially filling the cylindrical space with the material comprising superconductive oxide powder; and wherein the outer jacket is removed prior to c).
Claim 6
Dependent Claim
14 words
Method of claim 4, comprising providing an outer jacket that consists substantially of Al.
Claim 7
Dependent Claim
38 words
Method of claim 1, wherein prior to c) the normal metal cladding material comprises a relatively low porosity material, and comprising transforming the relatively low porosity material into a relatively high porosity material prior to completion of c).
Claim 8
Dependent Claim
61 words
Method of claim 6, wherein the relatively low porosity material consists substantially of interspersed particles of at least a first and a second material, and wherein transforming the low porosity material into the relatively high porosity material comprises contacting the body with a selective etching medium adapted for removing the first material at a substantially higher rate than the second material.
Claim 9
Dependent Claim
27 words
Method of claim 7, comprising providing a relatively low porosity cladding material in which the first material particles are Al and the second material particles are Ag.
Claim 10
Dependent Claim
39 words
Method of claim 1, wherein the material is a multicomponent material that comprises, in addition to a superconductive first component, a non-superconductive second component consisting substantially of one or more normal metals that are interspersed with the first component.
Claim 11
Dependent Claim
37 words
Method of claim 1, wherein the shape-changing operation comprises a cross section-reducing operation, the body is an elongate body, and the method further comprises forming, prior to completion of c), the elongate body into a predetermined shape.
Claim 12
Dependent Claim
30 words
Method of claim 1, comprising providing a normal metal cladding material that comprises compound particles consisting substantially of a first metal core and a second metal coating surrounding the core.
Claim 13
Dependent Claim
85 words
Method of claim 3, comprising providing a (Ba, Y) cuprate powder of nominal composition Ba 2 YCu 3 O 7 and a normal cladding material that consists substantially of Ag powder, further comprising forming prior to completion of c), the elongate body into a predetermined shape, and wherein c) comprises maintaining the elongate body at a temperature in the range 500°-1000° C. for a time in the range 1-100 hours, and relatively slowly cooling the elongate body to a temperature in the range 200°-500° C.
Claim 14
Dependent Claim
26 words
Method of claim 1, further comprising treating the body, subsequent to c), such that the ambient atmosphere is substantially precluded from contact with the oxide material.
Claim 15
Dependent Claim
15 words
Method of claim 13, wherein treating the body comprises applying a coating to the body.
Claim 16
Dependent Claim
18 words
Method of claim 13, wherein treating the body comprises melting the outer portion of the normal metal cladding.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-13 | 1995-07-15 | 1996-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-13 | 1999-07-15 | 2000-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-13 | 2003-07-15 | 2004-01-14 | $7700.00 | Window Closed / Lapsed |