Method for producing superconductive wires
Assignee: Karlsruher Institut für Technologie
•
Filing: 1986-09-08
•
Granted: 1987-08-18
•
Expires: 2006-09-08
Abstract
Abstract The present invention relates to a method for producing multifilament superconductive wires of Nb 3 Sn or V 3 Ga filaments embedded in a Cu or Cu alloy matrix, with the wires containing metal additive elements from the group including Ti, Zr, Hf, V, Nb, Ta, Fe, Co, Ni in the filaments and/or in the matrix. The superconductive characteristics of the wires are predetermined for medium magnetic fields (below 12 T) as well as for high magnetic fields (12 T and above). The percentage of the additive (or additives) can be set to a predetermined value and thus the superconductive properties can be set as desired. This is accomplished by mixing metal additives in powder form with a powder of niobium or a niobium alloy, or of vanadium or a vanadium alloy, in a defined grain size and in a defined quantity. The resulting powder mixture is compacted in a container of copper or a copper alloy, the compacted container is shaped into a wire and, upon removal of the container layer, is processed further into wires. Depending on the desired superconductive properties, the final reaction heat treatment of the wires is performed at a selected temperature in a range from 500° C. to 1000° C. and at a selected heat treatment duration in a range from 48 to 300 hours.
Inventors
- 👤 Rene Flukiger
- 👤 Stephen Gauss
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 16:08
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0184; H10N60/80; H10N60/85; Y; Y10; Y10S; Y10S505/00; Y10S505/80; Y10S505/812; Y10S505/813; Y10S505/815; Y10S505/822; Y10S505/823; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
211 words
A method for producing a superconductive wire, comprising steps for: mixing a first powder selected from the group consisting of: niobium; at least one niobium alloy of Nb-Ta, Nb-Ti, or Nb-Zr; vanadium; and at least one vanadium alloy of V-Ta, V-Nb, V-Ti, or V-Zr with an additive comprising, at least one elemental metal powder selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Fe, Co, and Ni, or at least one metal alloy powder-consisting of at least two of said elemental metals each powder having a grain size between about 0.1 μm and about 500 μm in diameter, to form a powder mixture, said additive comprising from about 0.1% to about 50% by weight of said powder mixture, filling a copper or copper alloy container with said powder mixture, evacuating said container, and compacting said container and powder mixture to obtain a powder density of more than 90% T.D., shaping said compacted container and powder mixture into a wire having a diameter from about 0.5 mm to about 15 mm, and removing said compacted container from said wire, and heating said wire to a temperature from about 500° C. to about 1000° C. for a period from about 48 to about 300 hours to obtain a superconductive wire.
Claim 2
Independent Claim
211 words
A method for producing a superconductive wire, comprising steps for: mixing a first powder selected from the group consisting of: niobium; at least one niobium alloy of Nb-Ta, Nb-Ti, or Nb-Zr; vanadium; and at least one vanadium alloy of V-Ta, V-Nb, V-Ti, or V-Zr with an additive comprising, at least one elemental metal powder selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Fe, Co, and Ni, or at least one metal alloy powder-consisting of at least two of said elemental metals each powder having a grain size between about 0.1 μm and about 500 μm in diameter, to form a powder mixture, said additive comprising from about 0.1% to about 50% by weight of said powder mixture, filling a copper or copper alloy container with said powder mixture, evacuating said container, and compacting said container and powder mixture to obtain a powder density of more than 90% T.D., shaping said compacted container and powder mixture into a wire having a diameter from about 0.5 mm to about 15 mm, and removing said compacted container from said wire, and heating said wire to a temperature from about 500° C. to about 1000° C. for a period from about 48 to about 300 hours to obtain a superconductive wire.
Claim 3
Dependent Claim
35 words
The method set forth in claim 1 wherein said first powder and said additive have the same or similar ductility, as defined by the respective Vickers microhardness values not differing by more than factor 2.
Claim 4
Dependent Claim
13 words
The method set forth in claim 1 wherein said first powder is niobium.
Claim 5
Dependent Claim
13 words
The method set forth in claim 1 wherein said first powder is vanadium.
Claim 6
Dependent Claim
27 words
The method set forth in claim 1 wherein said first powder is at least one niobium alloy selected from the group consisting of Nb-Ta, Nb-Ti, or Nb-Zr.
Claim 7
Dependent Claim
28 words
The method set forth in claim 1 wherein said first powder is at least one vanadium alloy selected from the group consisting of V-Ta, V-Nb, V-Ti, and V-Zr.
Claim 8
Dependent Claim
17 words
The method set forth in claim 1 wherein said additive is at least one elemental metal powder.
Claim 9
Dependent Claim
23 words
The method set forth in claim 7, wherein said elemental metal powder is selected from the group consisting of Fe, Co, and Ni.
Claim 10
Dependent Claim
14 words
The method set forth in claim 7, wherein said elemental metal powder is Ta.
Claim 11
Dependent Claim
16 words
The method set forth in claim 7, wherein said elemental metal powder is Ti and Ni.
Claim 12
Dependent Claim
17 words
The method set forth in claim 1 wherein said additive is at least one metal alloy powder.
Claim 13
Dependent Claim
27 words
The method set forth in claim 11, wherein said metal alloy powder includes at least one metal selected from the group consisting of Fe, Co, and Ni.
Claim 14
Dependent Claim
14 words
The method set forth in claim 11, wherein said metal alloy powder comprises Ta.
Claim 15
Dependent Claim
16 words
The method set forth in claim 11, wherein said metal alloy powder comprises Ti and Ni.
Claim 16
Dependent Claim
23 words
The method set forth in claim 1 wherein said additive comprises from about 0.3 to about 30% by weight of said powder mixture.
Claim 17
Dependent Claim
32 words
The method set forth in claim 1 including heating said wire to a temperature from about 550° C. to about 750° C. for a period from about 72 to about 240 hours.
Claim 18
Dependent Claim
32 words
The method set forth in claim 16 including heating said wire to a temperature between about 675° C. and about 750° C. for a period from about 64 to about 100 hours.
Claim 19
Dependent Claim
24 words
The method set forth in claim 1 wherein said powder has a grain size between about 0.1 μm and about 0.5 μm in diameter.
Claim 20
Dependent Claim
25 words
The method set forth in claim 1 wherein said first powder and said additive have about the same Vickers hardnesses so that both deform uniformly.
Claim 21
Dependent Claim
30 words
A superconductive wire having a critical current density of 10 4 A/cm 2 at a magnetic field of about 18 to 20 T produced by the method of claim 1.
References Cited (Backward Citations)
US3874074A
Cited
US3838503A
Cited
US3918998A
Cited
US3930903A
Cited
US4161062A
Cited
US4321749A
Cited
DE2909290A1
Cited
US4262412A
Cited
US4532703A
Cited
US4411959A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-17 | 1991-02-16 | 1991-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-17 | 1995-02-16 | 1995-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-17 | 1999-02-16 | 1999-08-18 | $7700.00 | Window Closed / Lapsed |