Dual density non-woven batt
Assignee: Polyester Fibers LLC
•
Filing: 1990-08-31
•
Granted: 1992-01-07
•
Expires: 2010-08-31
Abstract
Abstract A dual layer, dual density batt having a first batt layer comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of the fibers, at least some of the fibers in the first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of the fiber in the first or second fiber constituents having a relatively high predetermined melting temperature and a second batt layer comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of the fibers. At least some of the fibers in the first or second fiber constituents have a relatively low predetermined melting temperature and the remainder of the fiber in the first or second fiber constituents have a relatively high predetermined melting temperature. The first and second fiber constituents of the first batt layer comprise a different proportion or selection of fibers from the second batt layer to produce a different density in the first and second batt layers upon compression. The first and second fiber batt layers are overlaid to define a multi-layer web structure having intimately interconnected and fused first and second batt layers and intimately interconnected and fused first and second fiber constituents in both first and second batt layers. The first batt layer has a relatively high density and the second batt layer has a relatively low density. Both first and second batt layers of the batt are resiliently compressible to at least one-third of the uncompressed thickness.
Inventors
- 👤 Darrell C. Steagall
- 👤 William C. Hoyle, Jr.
- 👤 George G. Gabrel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 00:15
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B27/00; B32B27/36; B32B5/14; D; D04; D04H; D04H1/00; D04H1/02; D04H1/40; D04H1/42; D04H1/4374; D04H1/54; D04H1/559; B32B2250/00; B32B2250/02; B32B2255/00; B32B2255/02; B32B2262/00; B32B2262/02; B32B2262/0276; B32B2307/00; B32B2307/70; B32B2307/72; B32B2307/722; B32B2367/00; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/24992; Y10T428/31504; Y10T428/31652; Y10T428/31663; Y10T442/00; Y10T442/50; Y10T442/56
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
255 words
A dual layer, dual density batt, comprising: (a) a first batt layer comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of said fibers, at least some of said fibers in said first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of said fiber in said first or second fiber constituents having a relatively high predetermined melting temperature; (b) a second batt layer comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of said fibers, at least some of said fibers in said first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of said fiber in said first or second fiber constituents having a relatively high predetermined melting temperature, and said first and second fiber constituents of said first batt layer comprising a different proportion or selection of fibers from the second batt layer to produce a different density in said first and second batt layers upon compression; (c) said first and second fiber batt layers being overlaid to define a multi-layer web structure having intimately interconnected and fused first and second batt layers and intimately interconnected and fused first and second fiber constituents in both first and second batt layers, said first batt layer having a relatively high density and said second batt layer having a relatively low density; and (d) both first and second batt layers of the batt being resiliently compressible to at least one third of the uncompressed thickness.
Claim 2
Dependent Claim
255 words
A dual layer, dual density batt, comprising: (a) a first batt layer comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of said fibers, at least some of said fibers in said first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of said fiber in said first or second fiber constituents having a relatively high predetermined melting temperature; (b) a second batt layer comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of said fibers, at least some of said fibers in said first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of said fiber in said first or second fiber constituents having a relatively high predetermined melting temperature, and said first and second fiber constituents of said first batt layer comprising a different proportion or selection of fibers from the second batt layer to produce a different density in said first and second batt layers upon compression; (c) said first and second fiber batt layers being overlaid to define a multi-layer web structure having intimately interconnected and fused first and second batt layers and intimately interconnected and fused first and second fiber constituents in both first and second batt layers, said first batt layer having a relatively high density and said second batt layer having a relatively low density; and (d) both first and second batt layers of the batt being resiliently compressible to at least one third of the uncompressed thickness.
Claim 3
Dependent Claim
59 words
A batt according to claim 1, wherein the first, relatively high density batt layer comprises: (a) dry fibers; and (b) fibers having a relatively low melting temperature; and the second, relatively low density batt layer comprises: (c) fibers having a slickening finish applied to the surface thereof; (d) dry fibers; and (e) fibers having a relatively low melting temperature.
Claim 4
Dependent Claim
48 words
A batt according to claim 1, wherein the first, relatively high density batt layer comprises: (a) dry fibers; and (b) fibers having a relatively low melting temperature; and the second, relatively low density batt layer comprises: (c) dry fibers; and (d) fibers having a relatively low melting temperature.
Claim 5
Dependent Claim
39 words
A batt according to claim 1, wherein the first, relatively high density batt layer and the second, relatively low density batt layer both comprise slickened fiber with dry fibers in varying proportions to vary the characteristics of the batt.
Claim 6
Dependent Claim
36 words
A batt according to claim 4, wherein the relatively high density batt layer comprises approximately two-thirds by weight of the batt and the relatively low density batt layer comprises approximately one-third by weight of the batt.
Claim 7
Dependent Claim
28 words
A batt according to claim 4, wherein the dry fiber of the relatively high density batt layer comprises polyester and the low melt fiber comprises low melt polyester.
Claim 8
Dependent Claim
31 words
A batt according to claim 4, wherein the slickened fiber comprises polyester coated with a slickening finish; the dry fiber comprises polyester and the low melt fiber comprises low melt polyester.
Claim 9
Dependent Claim
42 words
A batt according to claim 4, wherein the slickened fiber comprises polyester coated with a slickening finish; the dry fiber comprises polyester and the low melt fiber comprises a high melting point polyester core fiber covered with a low melt polyester covering.
Claim 10
Dependent Claim
34 words
A batt according to claim 4, wherein the dry fiber of the relatively high density batt layer comprises approximately 85% by weight polyester, and the low melt fiber comprises approximately 15% by weight polyester.
Claim 11
Dependent Claim
40 words
A batt according to claim 4, wherein the dry fiber of the relatively high density batt layer comprises between approximately 50% and 85% by weight polyester, and the low melt fiber comprises between approximately 15% and 50% by weight polyester.
Claim 12
Dependent Claim
29 words
A batt according to claim 4, wherein the slickened fiber comprises 50% polyester; the dry fiber comprises approximately 45% polyester and the low melt fiber comprises approximately 5% polyester.
Claim 13
Dependent Claim
35 words
A batt according to claim 4, wherein the slickened fiber comprises 95% to 80% polyester; the dry fiber comprises approximately 95% to 80% polyester and the low melt fiber comprises approximately 5% to 20% polyester
Claim 14
Dependent Claim
46 words
A batt according to claim 1, wherein the relatively high density layer of the batt weighs between approximately two and five ounces per square foot and the relatively low density layer of the batt weights between approximately seven-tenths and one and one-half ounces per square foot.
Claim 15
Dependent Claim
15 words
A batt according to claim 4, wherein said slickened fiber includes a durable, siliconized finish.
Claim 16
Dependent Claim
15 words
A batt according to claim 4, wherein said slickened fiber includes a nondurable, wax finish.
Claim 17
Dependent Claim
63 words
A batt according to claim 1, wherein the relatively high density layer of the batt is between approximately two an five inches thick when uncompressed, the relatively low density layer of the batt is between approximately one and one and one-half inches thick when uncompressed, and the thickness of the entire batt is between three and six and one-half inches thick when uncompressed.
Claim 18
Dependent Claim
270 words
A dual layer, dual density batt, comprising: (a) a first batt layer between approximately seven and twelve inches thick and comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of said fibers, at least some of said fibers in said first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of said fiber in said first or second fiber constituents having a relatively high predetermined melting temperature; (b) a second batt layer between approximately three and six inches thick comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of said fibers, at least some of said fibers in said first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of said fiber in said first or second fiber constituents having a relatively high predetermined melting temperature, and said first and second fiber constituents of said first batt layer comprising a different proportion or selection of fibers from the second batt layer to produce a different density in said first and second batt layers upon compression; (c) said first and second fiber batt layers being overlaid to define a multi-layer web structure having intimately interconnected and fused first and second batt layers and intimately interconnected and fused first and second fiber constituents in both first and second batt layers, said first batt layer having a relatively high density and said second batt layer having a relatively low density; and (d) both first and second batt layers of the batt being resiliently compressible to at least one third of the uncompressed thickness.
Claim 19
Dependent Claim
270 words
A dual layer, dual density batt, comprising: (a) a first batt layer between approximately seven and twelve inches thick and comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of said fibers, at least some of said fibers in said first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of said fiber in said first or second fiber constituents having a relatively high predetermined melting temperature; (b) a second batt layer between approximately three and six inches thick comprising at least first and second staple polymer fiber constituents forming a homogeneous intermixture of said fibers, at least some of said fibers in said first or second fiber constituents having a relatively low predetermined melting temperature and the remainder of said fiber in said first or second fiber constituents having a relatively high predetermined melting temperature, and said first and second fiber constituents of said first batt layer comprising a different proportion or selection of fibers from the second batt layer to produce a different density in said first and second batt layers upon compression; (c) said first and second fiber batt layers being overlaid to define a multi-layer web structure having intimately interconnected and fused first and second batt layers and intimately interconnected and fused first and second fiber constituents in both first and second batt layers, said first batt layer having a relatively high density and said second batt layer having a relatively low density; and (d) both first and second batt layers of the batt being resiliently compressible to at least one third of the uncompressed thickness.
References Cited (Backward Citations)
US2483405A
Cited
US2500282A
Cited
US2835047A
Cited
US3043018A
Cited
US3088859A
Cited
US3196555A
Cited
US3281951A
Cited
US3362079A
Cited
US3380175A
Cited
US3510389A
Cited
US3619322A
Cited
US3616031A
Cited
US3616035A
Cited
US3839146A
Cited
US3765971A
Cited
US4195112A
Cited
US4297404A
Cited
US4129675A
Cited
US4377615A
Cited
US4391869A
Cited
US4373000A
Cited
US4474846A
Cited
US4418031A
Cited
US4359132A
Cited
US4477515A
Cited
US4463048A
Cited
US4532099A
Cited
US4490427A
Cited
US4518642A
Cited
US4542060A
Cited
US4568581A
Cited
US4668562A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-06 | 1995-07-08 | 1996-01-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-06 | 1999-07-08 | 2000-01-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-06 | 2003-07-08 | 2004-01-07 | $7700.00 | Window Closed / Lapsed |