Segmented elastomer
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1990-01-16
•
Granted: 1991-12-03
•
Expires: 2010-01-16
Abstract
Abstract It is important for tire treads to exhibit good wet skid resistance, low rolling resistance, good wear characteristics and good abrasion resistance. This is often accomplished by utilizing a blend of various rubbers in making tire tread compositions. However, some of the desirable characteristics of the individual rubbers in the blend are frequently lost on mixing. The segmented elastomers of this invention offer a unique combination of desirable characteristics for utilization in making tire tread compositions. This invention more specifically discloses a rubber polymer which has an excellent combination of properties for use in making tire treads which is comprised of: (a) a first segment which is comprised of repeat units which are derived from isoprene having a microstructure wherein there are from about 75% to about 98% 1,4-linkages and from about 2% to about 25% 3,4-linkages and wherein the first segment has a number average molecular weight which is within the range of about 25,000 to about 350,000; and (b) a second segment which is comprised of repeat units which are derived from 30 to 95 weight percent 1,3-butadiene and from 5 to 70 weight percent styrene, wherein the sum of (1) the product of 1.7 and the weight percent of styrene in the segment and (2) the percentage of 1,2-butadiene linkages in the second segment is within the range of about 50% to about 92%, and wherein the second segment has a number average molecular weight which is within the range of about 50,000 to about 350,000.
Inventors
- 👤 Wen-Liang Hsu
- 👤 Adel F. Halasa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 18:36
CPC Classifications
C; C08; C08F; C08F297/00; C08F297/02; C08F297/04; C08F297/046; B; B60; B60C; B60C1/00; B60C1/0016; Y; Y02; Y02T; Y02T10/00; Y02T10/80; Y02T10/86
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
202 words
A rubber polymer which has an excellent combination of properties for use in making tire treads which is comprised of: (a) a first segment which is comprised of repeat units which are derived from isoprene having a microstructure wherein there are from about 75% to about 98% 1,4-linkages and from about 2% to about 25% 3,4-linkages and wherein the first segment has a number average molecular weight which is within the range of about 25,000 to about 350,000; and (b) a second segment which is comprised of repeat units which are derived from 30 to 95 weight percent 1,3-butadiene and from 5 to 70 weight percent styrene, wherein the sum of (1) the product of 1.7 and the weight percent of styrene in the second segment and (2) the percentage of 1,2-butadiene linkages in the second segment is within the range of about 50% to about 92%, wherein the second segment has a number average molecular weight which is within the range of about 50,000 to about 350,000 and wherein the ratio of the number average molecular weight of the first segment to the number average molecular weight of the second segment is within the range of about 25:75 to about 75:25.
Claim 2
Dependent Claim
202 words
A rubber polymer which has an excellent combination of properties for use in making tire treads which is comprised of: (a) a first segment which is comprised of repeat units which are derived from isoprene having a microstructure wherein there are from about 75% to about 98% 1,4-linkages and from about 2% to about 25% 3,4-linkages and wherein the first segment has a number average molecular weight which is within the range of about 25,000 to about 350,000; and (b) a second segment which is comprised of repeat units which are derived from 30 to 95 weight percent 1,3-butadiene and from 5 to 70 weight percent styrene, wherein the sum of (1) the product of 1.7 and the weight percent of styrene in the second segment and (2) the percentage of 1,2-butadiene linkages in the second segment is within the range of about 50% to about 92%, wherein the second segment has a number average molecular weight which is within the range of about 50,000 to about 350,000 and wherein the ratio of the number average molecular weight of the first segment to the number average molecular weight of the second segment is within the range of about 25:75 to about 75:25.
Claim 3
Dependent Claim
42 words
A rubbery polymer as specified in claim 1 wherein the first segment is comprised of repeat units which are derived from isoprene having a microstructure wherein there are from about 5% to 20% 3,4-linkages and from about 80% to about 95% 1,4-linkages.
Claim 4
Dependent Claim
29 words
A rubbery polymer as specified in claim 1 wherein the first segment has a number average molecular weight which is within the range of about 50,000 to about 200,000.
Claim 5
Dependent Claim
29 words
A rubbery polymer as specified in claim 1 wherein the second segment has a number average molecular weight which is within the range of about 100,000 to about 250,000.
Claim 6
Dependent Claim
39 words
A rubbery polymer as specified in claim 1 wherein the second segment is comprised of repeat units which are derived from about 10 to about 45 weight percent styrene and from about 55 to about 90 weight percent 1,3-butadiene.
Claim 7
Dependent Claim
48 words
A rubbery polymer as specified in claim 1 wherein the sum of (1) the product of 1.7 and the weight percent of styrene in the second segment and (2) the percentage of 1,2-butadiene linkages in the second segment is within the range of about 70% to about 90%.
Claim 8
Dependent Claim
41 words
A rubbery polymer as specified in claim 1 wherein the ratio of the number average molecular weight of the first segment to the number average molecular weight of the second segment is within the range of about 25:75 to about 60:40.
Claim 9
Dependent Claim
32 words
A rubbery polymer as specified in claim 1 wherein less than 1% of the total repeat units derived from styrene in the second segment are present in blocks of four or more.
Claim 10
Dependent Claim
73 words
A rubbery polymer as specified in claim 5 wherein the first segment has a microstructure wherein there are from about 80% to 95% 1,4-linkages and from about 5% to about 20% 3,4-linkages; wherein the first segment has a number average molecular weight within the range of about 50,000 to about 200,000; and wherein the second segment has a number average molecular weight which is within the range of about 100,000 to about 250,000.
Claim 11
Dependent Claim
48 words
A rubbery polymer as specified in claim 9 wherein the sum of (1) the product of 1.7 and the weight percent of styrene in the second segment and (2) the percentage of 1,2-butadiene linkages in the second segment is within the range of about 70% to about 90%.
Claim 12
Dependent Claim
303 words
A process for preparing a rubber polymer which has an excellent combination of properties for use in making tire treads which comprises: (a) polymerizing isoprene monomer with a lithium catalyst in an inert organic medium at a temperature which is within the range of about 40° C. to about 100° C. in the absence of a significant quantity of a polar modifier to produce a living polyisoprene segment having a microstructure wherein there are from about 75% to about 98% 1,4-linkages and from about 2% to about 25% 3,4-linkages and having a number average molecular weight which is within the range of about 25,000 to about 350,000; and (b) utilizing the living polyisoprene segment to initiate the copolymerization of 1,3-butadiene and styrene wherein the copolymerization is conducted in the presence of at least one polar modifier at a temperature which is within the range of about 40° C. to about 100° C. wherein the total amount of monomers and polymer within the polymerization medium is maintained within the range of about 5 weight percent to about 35 weight percent to produce a second segment which is comprised of repeat units which are derived from 50 to 95 weight percent 1,3-butadiene and from 5 to 50 weight percent styrene, wherein the sum of (1) the product of 1.7 and the weight percent of styrene in the second segment and (2) the percentage of 1,2-butadiene linkages in the second segment is within the range of about 50% to about 92%, wherein the second segment has a number average molecular weight which is within the range of about 50,000 to about 350,000, and wherein the ratio of the number average molecular weight of the polyisoprene segment to the number average molecular weight of the second segment is within the range of about 25:75 to about 75:25.
Claim 13
Dependent Claim
303 words
A process for preparing a rubber polymer which has an excellent combination of properties for use in making tire treads which comprises: (a) polymerizing isoprene monomer with a lithium catalyst in an inert organic medium at a temperature which is within the range of about 40° C. to about 100° C. in the absence of a significant quantity of a polar modifier to produce a living polyisoprene segment having a microstructure wherein there are from about 75% to about 98% 1,4-linkages and from about 2% to about 25% 3,4-linkages and having a number average molecular weight which is within the range of about 25,000 to about 350,000; and (b) utilizing the living polyisoprene segment to initiate the copolymerization of 1,3-butadiene and styrene wherein the copolymerization is conducted in the presence of at least one polar modifier at a temperature which is within the range of about 40° C. to about 100° C. wherein the total amount of monomers and polymer within the polymerization medium is maintained within the range of about 5 weight percent to about 35 weight percent to produce a second segment which is comprised of repeat units which are derived from 50 to 95 weight percent 1,3-butadiene and from 5 to 50 weight percent styrene, wherein the sum of (1) the product of 1.7 and the weight percent of styrene in the second segment and (2) the percentage of 1,2-butadiene linkages in the second segment is within the range of about 50% to about 92%, wherein the second segment has a number average molecular weight which is within the range of about 50,000 to about 350,000, and wherein the ratio of the number average molecular weight of the polyisoprene segment to the number average molecular weight of the second segment is within the range of about 25:75 to about 75:25.
Claim 14
Dependent Claim
15 words
A process as specified in claim 11 wherein the lithium catalyst is an organomonolithium compound.
Claim 15
Dependent Claim
15 words
A process as specified in claim 11 wherein the lithium catalyst is an alkyllithium compound.
Claim 16
Dependent Claim
22 words
A process as specified in claim 11 wherein the isoprene monomer is polymerized in step (a) in the absence of polar modifiers.
Claim 17
Dependent Claim
38 words
A process as specified in claim 11 wherein said process is conducted in a polymerization medium which contains from about 10 to about 30 weight percent monomers and polymers, based upon the total weight of the polymerization medium.
Claim 18
Dependent Claim
29 words
A rubbery polymer as specified in claim 10 wherein the first segment has a number average molecular weight which is within the range of about 70,000 to about 150,000.
Claim 19
Dependent Claim
28 words
A rubbery polymer as specified in claim 16 wherein the second segment has a number average molecular weight which is within the range of about 220,000 to 240,000.
Claim 20
Dependent Claim
48 words
A rubbery polymer as specified in claim 16 wherein the sum of (1) the product of 1.7 and the weight percent of styrene in the second segment and (2) the percentage of 1,2-butadiene linkages in the second segment is within the range of about 75% to about 85%.
Claim 21
Dependent Claim
32 words
A process as specified in claim 11 wherein the polar modifier utilized in step (b) is selected from the group consisting of dipiperidinoethane, dipyrrolidinoethane, tetramethylethylene diamine, diethylene glycol dimethyl ether, and tetrahydrofuran.
Claim 22
Dependent Claim
31 words
A process as specified in claim 11 wherein step (a) and step (b) are conducted at a temperature which is within the range of about 50° C. to about 75° C.
References Cited (Backward Citations)
US3937760A
Cited
US4377665A
Cited
US4304886A
Cited
US4463123A
Cited
US4782119A
Cited
US4616065A
Cited
US4908401A
Cited
US4981911A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-02 | 1995-06-03 | 1995-12-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-02 | 1999-06-03 | 1999-12-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-02 | 2003-06-03 | 2003-12-03 | $7700.00 | Window Closed / Lapsed |