Process for producing block copolymer resin
Assignee: Asahi Kasei Corp
•
Filing: 1981-10-29
•
Granted: 1983-03-22
•
Expires: 2001-10-29
Abstract
Abstract In producing a block copolymer resin having vinyl aromatic hydrocarbon polymer blocks such as of styrene and polymer blocks primarily composed of conjugated diene such as of butadiene successively through living polymers using an organolithium compound as a catalyst in an aliphatic solvent, the vinyl aromatic hydrocarbon monomer for forming the vinyl aromatic hydrocarbon polymer block is added at a controlled rate, at the stage when the vinyl aromatic hydrocarbon content in the polymer formed has reached a certain value, higher than the polymerization rate of the vinyl aromatic hydrocarbon monomer at the polymerization temperature but at a rate which can maintain the solubility parameter of the liquid phase portion in the polymerization system at 7.7 or less, whereby a block copolymer resin with good transparency and impact strength can be produced with good productivity.
Inventors
- 👤 Toshinori Shiraki
- 👤 Akio Yamori
- 👤 Hideo Morita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:23
CPC Classifications
C; C08; C08F; C08F297/00; C08F297/02; C08F297/04
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
151 words
A process for producing a block copolymer resin comprising at least one vinyl aromatic hydrocarbon polymer block and at least one polymer block primarily composed of a conjugated diene, the weight ratio of vinyl aromatic hydrocarbon to conjugated diene being 55:45 to 95:5, using an organolithium compound as a catalyst in a solvent composed principally of an aliphatic hydrocarbon, wherein the improvement comprises adding continuously a monomer of a vinyl aromatic hydrocarbon to be added for formation of the vinyl aromatic hydrocarbon polymer block, at a stage of polymerization at which the vinyl aromatic hydrocarbon content in the polymer formed has reached 55% by weight or more, at a rate which is higher than the substantial average polymerization rate of said monomer at the polymerization temperature and yet maintains the solubility parameter of the liquid phase portion in the polymerization system at substantially not higher than 7.7 to further continue polymerization.
Claim 2
Dependent Claim
151 words
A process for producing a block copolymer resin comprising at least one vinyl aromatic hydrocarbon polymer block and at least one polymer block primarily composed of a conjugated diene, the weight ratio of vinyl aromatic hydrocarbon to conjugated diene being 55:45 to 95:5, using an organolithium compound as a catalyst in a solvent composed principally of an aliphatic hydrocarbon, wherein the improvement comprises adding continuously a monomer of a vinyl aromatic hydrocarbon to be added for formation of the vinyl aromatic hydrocarbon polymer block, at a stage of polymerization at which the vinyl aromatic hydrocarbon content in the polymer formed has reached 55% by weight or more, at a rate which is higher than the substantial average polymerization rate of said monomer at the polymerization temperature and yet maintains the solubility parameter of the liquid phase portion in the polymerization system at substantially not higher than 7.7 to further continue polymerization.
Claim 3
Dependent Claim
26 words
A process according to claim 1, wherein the vinyl aromatic hydrocarbon content in the block copolymer resin finally obtained is from 65 to 85% by weight.
Claim 4
Dependent Claim
63 words
A process according to claim 1, wherein the vinyl aromatic hydrocarbon monomer for formation of the vinyl aromatic hydrocarbon polymer block is added, at the stage when the vinyl aromatic hydrocarbon content has reached 60% or more, continuously at such a rate that the solubility parameter of the liquid phase portion in the polymerization system is maintained substantially at from 6.0 to 7.6.
Claim 5
Dependent Claim
63 words
A process according to claim 2, wherein the vinyl aromatic hydrocarbon monomer for formation of the vinyl aromatic hydrocarbon polymer block is added, at the stage when the vinyl aromatic hydrocarbon content has reached 60% or more, continuously at such a rate that the solubility parameter of the liquid phase portion in the polymerization system is maintained substantially at from 6.0 to 7.6.
Claim 6
Dependent Claim
135 words
A process according to claim 1, claim 2, claim 3 or claim 4, wherein a block copolymer represented by the formula B 1 -A 1 -B 2 -A 2 (wherein B 1 and B 2 represent polymer blocks composed principally of conjugated diene; and A 1 and A 2 vinyl aromatic hydrocarbon polymer blocks) is produced, the B 1 -A 1 segments in said copolymer containing from 50 to 90% by weight of vinyl aromatic hydrocarbon, said B 1 -A 1 segments in which the content of the intermediary vinyl aromatic hydrocarbon polymer block(A 1 ) is from 10 to 40% by weight based on the total content of the vinyl aromatic hydrocarbon polymer blocks (A 1 +A 2 ) being first formed and thereafter B 2 segment and A 2 segment being further formed.
Claim 7
Dependent Claim
28 words
A process according to any one of claims 1 to 4, wherein the polymer block composed principally of conjugated diene is a hompolymer block of a conjugated diene.
Claim 8
Dependent Claim
23 words
A process according to claim 5, wherein the polymer block composed principally of conjugated diene is a homopolymer block of a conjugated diene.
Claim 9
Dependent Claim
31 words
A process according to any one of claims 1 to 4, wherein the solvent composed principally of an aliphatic hydrocarbon has a solubility parameter of from 6.0 to less than 7.6.
Claim 10
Dependent Claim
26 words
A process according to claim 5, wherein the solvent composed principally of an aliphatic hydrocarbon has a solubility parameter of from 6.0 to less than 7.6.
Claim 11
Dependent Claim
26 words
A process according to any one of claims 1 to 4, wherein the conjugated diene is butadiene and/or isoprene, and the vinyl aromatic hydrocarbon is styrene.
Claim 12
Dependent Claim
21 words
A process according to claim 5, wherein the conjugated diene is butadiene and/or isoprene, and the vinyl aromatic hydrocarbon is styrene.
Claim 13
Dependent Claim
19 words
A process according to claim 1, wherein the solvent is an aliphatic hydrocarbon having 5 to 7 carbon atoms.
Claim 14
Dependent Claim
44 words
A process according to claim 1, wherein the solvent is a mixture containing 75% or more by weight of an aliphatic hydrocarbon having 5 to 7 carbon atoms and 25% or less by weight of an alicyclic hydrocarbon having 5 to 7 carbon atoms.
Claim 15
Dependent Claim
38 words
A process according to claim 1, wherein the solvent is a mixture containing 90% or more by weight of an aliphatic hydrocarbon having 5 to 7 carbon atoms and 10% or less by weight of benzene or toluene.
Claim 16
Dependent Claim
37 words
A process according to claim 1, wherein said vinyl aromatic hydrocarbon is continuously added at said rate while keeping the existence of at least 1% by weight of unreacted monomer based on the vinyl aromatic hydrocarbon added.
Claim 17
Dependent Claim
37 words
A process according to claim 1, wherein said vinyl aromatic hydrocarbon is continuously added at said rate while keeping the existence of at least 3% by weight of unreacted monomer based on the vinyl aromatic hydrocarbon added.
Claim 18
Dependent Claim
37 words
A process according to claim 1, wherein said vinyl aromatic hydrocarbon is continuously added at said rate while keeping the existence of at least 5% by weight of unreacted monomer based on the vinyl aromatic hydrocarbon added.
Claim 19
Dependent Claim
191 words
A process for producing a block copolymer resin comprising at least one vinyl aromatic hydrocarbon polymer block and at least one polymer block primarily composed of a conjugated diene, the weight ratio of vinyl aromatic hydrocarbon to conjugated diene being 55:45 to 95:5, using an organolithium compound as a catalyst in a solvent composed principally of an aliphatic hydrocarbon, comprising the steps of: polymerizing a conjugated diene to form a polymer block primarily composed of a conjugated diene; and adding continuously a monomer of a vinyl aromatic hydrocarbon to be added for formation of the vinyl aromatic hydrocarbon polymer block, at a stage of polymerization at which the vinyl aromatic hydrocarbon content in the polymer formed has reached 55% by weight or more, at a rate which is higher than the substantial average polymerization rate of said monomer at the polymerization temperature wherein said vinyl aromatic hydrocarbon exists in an amount of at least 1% by weight or more based on the vinyl aromatic hydrocarbon added and yet maintains the solubility parameter of the liquid phase portion in the polymerization system at substantially not higher than 7.7 to further continue polymerization.
Claim 20
Dependent Claim
191 words
A process for producing a block copolymer resin comprising at least one vinyl aromatic hydrocarbon polymer block and at least one polymer block primarily composed of a conjugated diene, the weight ratio of vinyl aromatic hydrocarbon to conjugated diene being 55:45 to 95:5, using an organolithium compound as a catalyst in a solvent composed principally of an aliphatic hydrocarbon, comprising the steps of: polymerizing a conjugated diene to form a polymer block primarily composed of a conjugated diene; and adding continuously a monomer of a vinyl aromatic hydrocarbon to be added for formation of the vinyl aromatic hydrocarbon polymer block, at a stage of polymerization at which the vinyl aromatic hydrocarbon content in the polymer formed has reached 55% by weight or more, at a rate which is higher than the substantial average polymerization rate of said monomer at the polymerization temperature wherein said vinyl aromatic hydrocarbon exists in an amount of at least 1% by weight or more based on the vinyl aromatic hydrocarbon added and yet maintains the solubility parameter of the liquid phase portion in the polymerization system at substantially not higher than 7.7 to further continue polymerization.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-21 | 1986-09-20 | 1987-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-21 | 1990-09-20 | 1991-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-21 | 1994-09-20 | 1995-03-22 | $7700.00 | Window Closed / Lapsed |