Diffusion bonding and superplastic forming
Assignee: BAE Systems PLC
•
Filing: 1991-04-30
•
Granted: 1991-12-03
•
Expires: 2011-04-30
Abstract
Abstract In a superplastic forming/diffusion bonding process, in particular for aluminum-lithium alloys, the stop-off material in the diffusion bonding step is a porous lamellar material such as glass cloth or vermiculite paper. In one embodiment, prior to diffusion bonding, the stack of alloy sheets and lamellar material may be sealed under vacuum.
Inventors
- 👤 Graham A. Cooper
- 👤 Ian E. Bottomley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:43
CPC Classifications
B; B23; B23K; B23K20/00; B23K20/22; B23K20/233; B23K20/2333
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
184 words
A method of forming a structure having an internal cavity, which method comprises (a) arranging a plurality of sheets of a superplastic metal in a stack, (b) interposing a self-supporting lamella of predetermined shape of inert porous material between adjacent sheets to prevent bonding between said adjacent sheets in selected regions thereof covered by the lamella, while permitting bonding to occur in other regions not covered by the lamella, (c) subjecting the stack of sheets to diffusion bonding to bond the sheets together in the said other regions, (d) subjecting the thus bonded stack to superplastic forming to form the said structure by (i) placing the stack in a mould, (ii) heating the stack to a temperature at which the metal becomes superplastic and (iii) injecting a gas between the sheets at one or more selected points to inflate the stack to conform to the shape of the mould, thereby also forming the said cavity within the structure, said gas passing from the gas injection point through the porous lamella to reach the said selected regions, and (e) removing the structure from the mould.
Claim 2
Independent Claim
184 words
A method of forming a structure having an internal cavity, which method comprises (a) arranging a plurality of sheets of a superplastic metal in a stack, (b) interposing a self-supporting lamella of predetermined shape of inert porous material between adjacent sheets to prevent bonding between said adjacent sheets in selected regions thereof covered by the lamella, while permitting bonding to occur in other regions not covered by the lamella, (c) subjecting the stack of sheets to diffusion bonding to bond the sheets together in the said other regions, (d) subjecting the thus bonded stack to superplastic forming to form the said structure by (i) placing the stack in a mould, (ii) heating the stack to a temperature at which the metal becomes superplastic and (iii) injecting a gas between the sheets at one or more selected points to inflate the stack to conform to the shape of the mould, thereby also forming the said cavity within the structure, said gas passing from the gas injection point through the porous lamella to reach the said selected regions, and (e) removing the structure from the mould.
Claim 3
Dependent Claim
15 words
A method according to claim 1, wherein said lamella comprises a mat, paper or cloth.
Claim 4
Dependent Claim
17 words
A method according to claim 1, wherein said lamella of inert porous material comprises a filamentary material.
Claim 5
Dependent Claim
16 words
A method according to claim 3, wherein the lamella of filamentary material comprises a glass cloth.
Claim 6
Dependent Claim
16 words
A method according to claim 1, wherein said lamella of inert porous material comprises vermiculite paper.
Claim 7
Dependent Claim
22 words
A method according to claim 1, wherein said lamellar material is preheated prior to said diffusion bonding to drive off any contaminants.
Claim 8
Dependent Claim
35 words
A method according to claim 6, wherein the said lamella of inert porous material is preheated prior to said diffusion bonding step to a temperature in excess of the temperature of the diffusion bonding step.
Claim 9
Dependent Claim
18 words
A method according to claim 1, wherein said stack, prior to said diffusion bonding, is sealed under vacuum.
Claim 10
Dependent Claim
21 words
A method according to claim 1, wherein said superplastic metal is selected from the group consisting of aluminum and aluminum alloys.
Claim 11
Dependent Claim
14 words
A method according to claim 9, wherein said aluminum alloy is an aluminum-lithium alloy.
References Cited (Backward Citations)
GB820033A
Cited
GB883359A
Cited
GB1495655A
Cited
US4197977A
Cited
GB2095137A
Cited
US4426032A
Cited
EP0266073A1
Cited
US4732312A
Cited
US4942999A
Cited
US4811766A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-02 | 1995-06-03 | 1995-12-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-02 | 1999-06-03 | 1999-12-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-02 | 2003-06-03 | 2003-12-03 | $7700.00 | Window Closed / Lapsed |