Method for diffusion bonding of alloys having low solubility oxides
Assignee: Grumman Corp
•
Filing: 1986-11-10
•
Granted: 1988-03-22
•
Expires: 2006-11-10
Abstract
Abstract Diffusion bonding of surface layers of an alloy, such as an aluminum alloy, having surface oxides of low solubility in the alloy includes treating the surface layers to be bonded to remove existing surface oxide coatings, and diffusion bonding the surface layers to one another by placing the alloy to be bonded under sufficient pressure to cause disruption of the oxide coatings by localized surface deformation of the alloy, enhanced by a superplastic microstructure, without substantial deformation of the alloy, i.e., macroscopic deformation approaching zero percent, while heating the alloy in a non-oxidizing atmosphere for a time sufficient for diffusion bonding to occur. The alloy may be treated so that at least the surface layers thereof have a fine grain structure of the type associated with superplastic forming properties. Components may be formed by diffusion bonding and superplastic forming.
Inventors
- 👤 James R. Kennedy
- 👤 Edmund Y. Ting
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:22
CPC Classifications
B; B23; B23K; B23K20/00; B23K20/22; B23K20/233; B23K20/2336; B23K20/24
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
106 words
A method for diffusion bonding surface layers of an alloy having surface oxide coatings of low solubility in the alloy, comprising the steps of: treating said alloy so that at least the surface layers to be bonded have a fine grain structure; removing existing surface oxide coatings from the surface layers to be bonded; diffusion bonding the surface layers to one another by placing the alloy to be bonded under a pressure sufficient to cause disruption of the oxide coatings and insufficient to cause macroscopic deformation of the alloy while heating the alloy in a non-oxidizing atmosphere for a time sufficient for diffusion bonding to occur.
Claim 2
Independent Claim
106 words
A method for diffusion bonding surface layers of an alloy having surface oxide coatings of low solubility in the alloy, comprising the steps of: treating said alloy so that at least the surface layers to be bonded have a fine grain structure; removing existing surface oxide coatings from the surface layers to be bonded; diffusion bonding the surface layers to one another by placing the alloy to be bonded under a pressure sufficient to cause disruption of the oxide coatings and insufficient to cause macroscopic deformation of the alloy while heating the alloy in a non-oxidizing atmosphere for a time sufficient for diffusion bonding to occur.
Claim 3
Dependent Claim
12 words
The method of claim 1, wherein said alloy is an aluminum alloy.
Claim 4
Dependent Claim
12 words
The method of claim 2, wherein said aluminum alloy is 7475 aluminum.
Claim 5
Dependent Claim
12 words
The method of claim 2, wherein said aluminum alloy is 7075 aluminum.
Claim 6
Dependent Claim
35 words
The method of claim 1, wherein said step of treating said alloy comprises: thermomechanically processing the surface layers sufficiently to deform the near surface microstructure; and recrystalizing the deformed microstructure to create said fine-grained structure.
Claim 7
Dependent Claim
25 words
The method of claim 1, wherein said step of treating said alloy comprises localized mechanical surface deformation and heating of the alloy to cause recrystallization.
Claim 8
Dependent Claim
16 words
The method of claim 1, wherein said pressure is less than 1000 pounds per square inch.
Claim 9
Dependent Claim
16 words
The method of claim 1, wherein said pressure is less than 100 pounds per square inch.
Claim 10
Dependent Claim
23 words
The method of claim 1, wherein said step of heating is performed for a time ranging from one half hour to ten hours.
Claim 11
Dependent Claim
17 words
The method of claim 1, further comprising the step of heat treating the alloy after diffusion bonding.
Claim 12
Dependent Claim
16 words
The method of claim 1, further comprising the step of tempering after diffusion bonding has occured.
Claim 13
Dependent Claim
27 words
The method of claim 1, further comprising the step of: cooling the alloy to room temperature, after bonding, over a period of at least approximately twenty minutes.
Claim 14
Dependent Claim
41 words
The method of claim 1, wherein said step of treating the surface layers comprises: abrading with successively finer grades of grinding paper; rinsing with one of high purity acetone and distilled water; abrading with a metallic brush; and removing the brushings.
Claim 15
Dependent Claim
38 words
The method of claim 13, wherein said step of abrading with a metallic brush comprises: abrading in a first direction; abrading in a second direction at an angle of approximately ninety degrees with respect to said first direction.
Claim 16
Dependent Claim
33 words
The method of claim 13, wherein said step of removing the brushings comprises: exposing brushed surfaces to a stream of compressed, filtered air moving at a velocity sufficiently high to remove said brushings.
Claim 17
Dependent Claim
21 words
The method of claim 13, wherein said grades of grinding paper vary from 240 grit to 600 grit SiC grinding paper.
Claim 18
Dependent Claim
66 words
The method of claim 1, further comprising the step of: placing components of said alloy in a fixture; exposing a first opposite surface to a first surface layer to be diffusion bonded to one of a partial vacuum and a pressurized gas; and exposing a second opposite surface of a second surface layer to be diffusion bonded to another of said partial vacuum and pressurized gas.
Claim 19
Dependent Claim
25 words
The method of claim 1, wherein said non-oxidizing atmosphere is produced by surrounding said alloy with one of an inert gas and a soft vacuum.
Claim 20
Dependent Claim
23 words
The method of claim 1, further comprising the step of: superplastically forming at least one of the alloys to change the shape thereof.
Claim 21
Dependent Claim
17 words
The method of claim 1, wherein at least the surface layers of the alloy have superplastic properties.
Claim 22
Independent Claim
108 words
A method for diffusion bonding surface layers of alloys having surface oxide coatings of low solubility in the alloy, comprising the steps of: treating the surface layer of a first of said alloys so that it has a fine grained microstructure characteristic of superplasticity; treating the surface layers to be bonded to remove existing surface oxide coatings; diffusion bonding the surface layers to one another by placing the alloys to be bonded under sufficient pressure to cause disruption of the oxide coatings and insufficient to cause macroscopic deformation of the alloys while heating the alloys in a nonoxidizing atmosphere for a time sufficient for diffusion bonding to occur.
Claim 23
Independent Claim
108 words
A method for diffusion bonding surface layers of alloys having surface oxide coatings of low solubility in the alloy, comprising the steps of: treating the surface layer of a first of said alloys so that it has a fine grained microstructure characteristic of superplasticity; treating the surface layers to be bonded to remove existing surface oxide coatings; diffusion bonding the surface layers to one another by placing the alloys to be bonded under sufficient pressure to cause disruption of the oxide coatings and insufficient to cause macroscopic deformation of the alloys while heating the alloys in a nonoxidizing atmosphere for a time sufficient for diffusion bonding to occur.
Claim 24
Dependent Claim
23 words
The method of claim 21, wherein the surface layer of a second of said alloys has a coarse grained microstructure which is non-superplastic.
Claim 25
Dependent Claim
19 words
The method of claim 22, wherein said first alloy is 7475 aluminum and said second alloy is 2219 aluminum.
Claim 26
Dependent Claim
14 words
The method of claim 21, wherein said alloys are each of a different material.
Claim 27
Dependent Claim
14 words
The method of claim 21, wherein said alloys are each different alloys of aluminum.
Claim 28
Dependent Claim
21 words
The method of claim 11, wherein said step of tempering comprises the steps of solution treating; quenching; and aging the alloy.
Claim 29
Dependent Claim
23 words
The method of claim 1, wherein said fine grain structure includes grains having a size equal to or less than substantially ten microns.
References Cited (Backward Citations)
SU287069A1
Cited
US3041718A
Cited
US3180022A
Cited
US3500532A
Cited
US3552898A
Cited
US3680197A
Cited
US3657801A
Cited
US3815219A
Cited
US3758741A
Cited
US3937387A
Cited
US3920175A
Cited
US3927817A
Cited
SU585937A1
Cited
US4025036A
Cited
US4087037A
Cited
JPS5333846A
Cited
US4117970A
Cited
US4197978A
Cited
US4220276A
Cited
US4331284A
Cited
US4361262A
Cited
US4483478A
Cited
US4452389A
Cited
US4499156A
Cited
SU1151404A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-22 | 1991-09-21 | 1992-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-22 | 1995-09-21 | 1996-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-22 | 1999-09-21 | 2000-03-22 | $7700.00 | Window Closed / Lapsed |