Method of inserting medical devices incorporating SIM alloy elements
Assignee: Medtronic Inc
•
Filing: 1988-09-27
•
Granted: 1991-11-26
•
Expires: 2008-09-27
Abstract
Abstract Medical devices which are currently proposed to use elements made from shape memory alloys may be improved by the use of stress-induced martensite alloy elements instead. The use of stress-induced martensite decreases the temperature sensitivity of the devices, thereby making them easier to install and/or remove.
Inventors
- 👤 James E. Jervis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:16
CPC Classifications
A; A61; A61B; A61B17/00; A61B17/064; A61B17/0642; A61B17/08; A61B17/56; A61B17/58; A61B17/68; A61B17/72; A61C; A61C7/00; A61C7/12; A61F; A61F2/00; A61F2/01; A61F2/011; A61F2/02; A61F2/24; A61F2/2409; A61F6/00; A61F6/06; A61F6/14; A61L; A61L27/00; A61L27/02; A61L27/04; A61L31/00; A61L31/02; A61L31/022; A61B2017/00831; A61B2017/00867; A61C2201/00; A61C2201/007; A61F2/0004; A61F2/04; A61F2/06; A61F2/07; A61F2/30; A61F2002/30001; A61F2002/30003; A61F2002/3006; A61F2002/30092; A61F2210/00; A61F2210/0014; A61F2210/0019; A61L2400/00; A61L2400/16; Y; Y10; Y10S; Y10S606/00; Y10S606/907; Y10S606/911
Claims Analysis
Total Claims: 49
Claim 1
Independent Claim
131 words
A method of medical treatment of a mammal which comprises the steps of: (a) providing a device comprising an element which comprises a shape memory alloy which displays stress induced martensite behavior at body temperature of the mammal, the element being restrained in a deformed configuration, the restraining means stressing the element thereby inducing stress induced martensite in the alloy; (b) positioning the device so that the shape memory alloy element is within a mammalian body or in such proximity to a mammalian body that the element and the restraining means are substantially at body temperature; and (c) at least partially removing the restraining means from the element thereby transforming the element from the deformed configuration, the transformation occurring with the element and the restraining means being substantially at body temperature.
Claim 2
Independent Claim
131 words
A method of medical treatment of a mammal which comprises the steps of: (a) providing a device comprising an element which comprises a shape memory alloy which displays stress induced martensite behavior at body temperature of the mammal, the element being restrained in a deformed configuration, the restraining means stressing the element thereby inducing stress induced martensite in the alloy; (b) positioning the device so that the shape memory alloy element is within a mammalian body or in such proximity to a mammalian body that the element and the restraining means are substantially at body temperature; and (c) at least partially removing the restraining means from the element thereby transforming the element from the deformed configuration, the transformation occurring with the element and the restraining means being substantially at body temperature.
Claim 3
Dependent Claim
32 words
A method as claimed in claim 1, in which transformation of the shape memory alloy element causes one or more parts of the body in contact with the element to be displaced.
Claim 4
Dependent Claim
24 words
The method of claim 1 wherein the step of removing the restraining means transforms the element without change in state of the restraining means.
Claim 5
Dependent Claim
14 words
The method of claim 1 wherein the shape memory alloy element is a catheter.
Claim 6
Independent Claim
252 words
A method for installing a medical device within or proximate to a mammalian body such that the device is substantially at body temperature, the method comprising the steps of: (a) providing a medical device comprising a memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the shape-memory alloy can display reversible stress-induced martensite at about body temperature such that the shape-memory alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a deformed shape when the alloy is in its stress-induced martensitic state and (ii) a different unstressed shape; (b) engaging the memory alloy element with a restraining means at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its deformed shape and subsequently positioning the medical device within or proximate to the body at a temperature greater than the As of the alloy while the memory alloy element remains in its deformed shape; and (c) while maintaining the temperature of the memory alloy element above the As of the alloy, disengaging the restraining means from the memory alloy element so that at least a portion of the alloy transforms from its stress-induced martensitic state so that the memory alloy element spontaneously transforms from its deformed shape toward its unstressed shape, wherein substantially all of the transformation occurs from removing the restraining means and not from any change in temperature of the device or the restraining means.
Claim 7
Independent Claim
252 words
A method for installing a medical device within or proximate to a mammalian body such that the device is substantially at body temperature, the method comprising the steps of: (a) providing a medical device comprising a memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the shape-memory alloy can display reversible stress-induced martensite at about body temperature such that the shape-memory alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a deformed shape when the alloy is in its stress-induced martensitic state and (ii) a different unstressed shape; (b) engaging the memory alloy element with a restraining means at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its deformed shape and subsequently positioning the medical device within or proximate to the body at a temperature greater than the As of the alloy while the memory alloy element remains in its deformed shape; and (c) while maintaining the temperature of the memory alloy element above the As of the alloy, disengaging the restraining means from the memory alloy element so that at least a portion of the alloy transforms from its stress-induced martensitic state so that the memory alloy element spontaneously transforms from its deformed shape toward its unstressed shape, wherein substantially all of the transformation occurs from removing the restraining means and not from any change in temperature of the device or the restraining means.
Claim 8
Dependent Claim
36 words
The method of claim 5 wherein the step of engaging comprises directly contacting the memory alloy element with the restraining means, and the step of disengaging comprises separating the restraining means from the memory alloy element.
Claim 9
Dependent Claim
29 words
The method of claim 5 wherein the step of disengaging results in at least a portion of the alloy transforming from its stress-induced martensitic state to its austenitic state.
Claim 10
Dependent Claim
71 words
The method of claim 7 including the additional step after step (c) of re-engaging the memory alloy element with the restraining means so that the memory alloy element transforms toward its deformed shape by reversion of at least a portion of the alloy from its austenitic state to its stress-induced martensitic state, wherein the step of re-engaging occurs while maintaining the temperature of the device above the As of the alloy.
Claim 11
Dependent Claim
41 words
The method of claim 7 wherein when the memory alloy element is in its unstressed shape, the shape-memory alloy is in its austenitic state, and the step of disengaging causes the memory alloy element to transform completely to its unstressed shape.
Claim 12
Independent Claim
255 words
A method for installing a medical device within or proximate to a mammalian body such that the device is substantially at body temperature, the method comprising the steps of: (a) providing a medical device comprising a memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the shape-memory alloy can display reversible stress-induced martensite at about body temperature such that the shape-memory alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a deformed shape when the alloy is in its stress-induced martensitic state and (ii) a different unstressed shape; (b) placing the memory alloy element within a hollow restraining member at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its deformed shape, and positioning the medical device within or proximate to the body at a temperature greater than the As of the alloy while the memory alloy element remains in its deformed shape; and (c) while maintaining the temperature of the memory alloy element above the As of the alloy, causing relative movement between the hollow restraining member and the memory alloy element so that at least a portion of the alloy transforms from its stress-induced martensitic state so that the memory alloy element spontaneously transforms from its deformed shape toward its unstressed shape, wherein substantially all of the transformation occurs from the relative movement and not from any change in temperature of the device or the restraining means.
Claim 13
Independent Claim
255 words
A method for installing a medical device within or proximate to a mammalian body such that the device is substantially at body temperature, the method comprising the steps of: (a) providing a medical device comprising a memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the shape-memory alloy can display reversible stress-induced martensite at about body temperature such that the shape-memory alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a deformed shape when the alloy is in its stress-induced martensitic state and (ii) a different unstressed shape; (b) placing the memory alloy element within a hollow restraining member at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its deformed shape, and positioning the medical device within or proximate to the body at a temperature greater than the As of the alloy while the memory alloy element remains in its deformed shape; and (c) while maintaining the temperature of the memory alloy element above the As of the alloy, causing relative movement between the hollow restraining member and the memory alloy element so that at least a portion of the alloy transforms from its stress-induced martensitic state so that the memory alloy element spontaneously transforms from its deformed shape toward its unstressed shape, wherein substantially all of the transformation occurs from the relative movement and not from any change in temperature of the device or the restraining means.
Claim 14
Dependent Claim
68 words
The method of claim 10 wherein the hollow member is a tube and the memory alloy element is axially slidable within the tube, and wherein the step of causing relative movement comprises causing relative axial movement between the tube and the memory alloy element so that at least a portion of the memory alloy element extends out of the tube and thereby spontaneously transforms toward its unstressed shape.
Claim 15
Dependent Claim
42 words
The method of claim 10 wherein the step of causing relative movement comprises completely separating the hollow member from the memory alloy element, and wherein at least a portion of the alloy transforms from its stress-induced martensitic state to its austenitic state.
Claim 16
Dependent Claim
22 words
The invention of claim 10 wherein the transformation of the alloy occurs without any change in the state of the restraining member.
Claim 17
Independent Claim
256 words
A method for installing a medical device within or proximate to a mammalian body such that the device is substantially at body temperature, the method comprising the steps of: (a) providing a medical device comprising a hollow memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the shape-memory alloy can display reversible stress-induced martensite at about body temperature such that the shape-memory alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a deformed shape when the alloy is in its stress-induced martensitic state and (ii) a different unstressed shape; (b) placing a restraining means in the hollow memory alloy element at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its deformed shape and positioning the medical device within or proximate to the body at a temperature greater than the As of the alloy while the hollow memory alloy element remains in its deformed shape; and (c) while maintaining the temperature of the memory alloy element above the As of the alloy, causing relative movement between the restraining means and the memory alloy element so that at least a portion of the alloy transforms from its stress-induced martensitic state so that the memory alloy element spontaneously transforms from its deformed shape toward its unstressed shape, wherein substantially all of the transformation occurs from the relative movement and not from any change in temperature of the device or the restraining means.
Claim 18
Independent Claim
256 words
A method for installing a medical device within or proximate to a mammalian body such that the device is substantially at body temperature, the method comprising the steps of: (a) providing a medical device comprising a hollow memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the shape-memory alloy can display reversible stress-induced martensite at about body temperature such that the shape-memory alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a deformed shape when the alloy is in its stress-induced martensitic state and (ii) a different unstressed shape; (b) placing a restraining means in the hollow memory alloy element at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its deformed shape and positioning the medical device within or proximate to the body at a temperature greater than the As of the alloy while the hollow memory alloy element remains in its deformed shape; and (c) while maintaining the temperature of the memory alloy element above the As of the alloy, causing relative movement between the restraining means and the memory alloy element so that at least a portion of the alloy transforms from its stress-induced martensitic state so that the memory alloy element spontaneously transforms from its deformed shape toward its unstressed shape, wherein substantially all of the transformation occurs from the relative movement and not from any change in temperature of the device or the restraining means.
Claim 19
Dependent Claim
68 words
The method of claim 14 wherein the hollow member is a tube and the restraining means is axially slidable within the tube, and wherein the step of causing relative movement comprises causing relative axial movement between the memory alloy element and the restraining means so that at least a portion of the memory alloy element extends beyond the restraining means and thereby spontaneously transforms toward its unstressed shape.
Claim 20
Independent Claim
239 words
A method for inserting a medical device into a mammalian body comprising the steps of: (a) providing a medical device comprising (i) a restraining means and (ii) a memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the alloy can display reversible stress-induced martensite at about human body temperature such that the alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a deformed shape when the alloy is in its stress-induced martensitic state and (ii) a different unstressed shape when the alloy is in its austenitic state; (b) directly contacting the memory alloy element with the restraining means at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and deforming the memory alloy element into its deformed shape; and (c) after step (b), while maintaining the temperature of the device above the As of the alloy, inserting the memory alloy element into the human body and at least partly separating the restraining means from the memory alloy element so that at least a portion of the alloy transforms from its stress-induced martensitic state to its austenitic state so that the memory alloy element spontaneously transforms from its deformed shape toward its unstressed shape, wherein substantially all of the transformation occurs from disengaging the restraining means and not from any change in temperature of the device or the restraining means.
Claim 21
Independent Claim
239 words
A method for inserting a medical device into a mammalian body comprising the steps of: (a) providing a medical device comprising (i) a restraining means and (ii) a memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the alloy can display reversible stress-induced martensite at about human body temperature such that the alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a deformed shape when the alloy is in its stress-induced martensitic state and (ii) a different unstressed shape when the alloy is in its austenitic state; (b) directly contacting the memory alloy element with the restraining means at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and deforming the memory alloy element into its deformed shape; and (c) after step (b), while maintaining the temperature of the device above the As of the alloy, inserting the memory alloy element into the human body and at least partly separating the restraining means from the memory alloy element so that at least a portion of the alloy transforms from its stress-induced martensitic state to its austenitic state so that the memory alloy element spontaneously transforms from its deformed shape toward its unstressed shape, wherein substantially all of the transformation occurs from disengaging the restraining means and not from any change in temperature of the device or the restraining means.
Claim 22
Dependent Claim
71 words
The method of claim 16 including the additional step after step (c) of re-engaging the memory alloy element with the restraining means so that the memory alloy element transforms toward its deformed shape by reversion of at least a portion of the alloy from its austenitic state to its stress-induced martensitic state, wherein the step of re-engaging occurs while maintaining the temperature of the device above the As of the alloy.
Claim 23
Independent Claim
213 words
A method for inserting a catheter into a mammalian body comprising the steps of: (a) providing a catheter at least partly formed from a pseudoelastic shape-memory alloy, wherein the alloy can display reversible stress-induced martensite at about body temperature such that the alloy has a stress-induced martensitic state and an austenitic state, the catheter having (i) an easy insertion shape when the alloy is in its stressed-induced martensitic state and (ii) a different unstressed shape when the alloy is in its austenitic state; (b) stressing the catheter with a restraint at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its deformed easy insertion shape; (c) after step (b), inserting the catheter into the mammalian body at a temperature greater than the As of the alloy; and (d) after step (c), at least partly disengaging the restraint from the catheter so that at least a portion of the alloy transforms from its stress-induced martensitic state to its austenitic state so that the catheter spontaneously transforms from its easy insertion shape to its unstressed shape, wherein substantially all of the transformation occurs from disengaging the restraint and not from any change in temperature of the catheter or the restraint.
Claim 24
Independent Claim
213 words
A method for inserting a catheter into a mammalian body comprising the steps of: (a) providing a catheter at least partly formed from a pseudoelastic shape-memory alloy, wherein the alloy can display reversible stress-induced martensite at about body temperature such that the alloy has a stress-induced martensitic state and an austenitic state, the catheter having (i) an easy insertion shape when the alloy is in its stressed-induced martensitic state and (ii) a different unstressed shape when the alloy is in its austenitic state; (b) stressing the catheter with a restraint at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its deformed easy insertion shape; (c) after step (b), inserting the catheter into the mammalian body at a temperature greater than the As of the alloy; and (d) after step (c), at least partly disengaging the restraint from the catheter so that at least a portion of the alloy transforms from its stress-induced martensitic state to its austenitic state so that the catheter spontaneously transforms from its easy insertion shape to its unstressed shape, wherein substantially all of the transformation occurs from disengaging the restraint and not from any change in temperature of the catheter or the restraint.
Claim 25
Dependent Claim
59 words
The method of claim 18 including the additional steps after step (d) of (e) stressing the catheter with the restraint at a temperature greater than the As of the alloy for placing the alloy in its stressed-induced martensitic state and the memory alloy element in its easily inserted shape, and (f) removing the easily inserted catheter from the body.
Claim 26
Dependent Claim
14 words
The method of claim 18 wherein a catheter is stressed with an internal restraint.
Claim 27
Dependent Claim
11 words
The method of claim 18 wherein the catheter is a cannula.
Claim 28
Dependent Claim
17 words
The method of claim 18 wherein the step of disengaging comprises removing the restraint from the catheter.
Claim 29
Dependent Claim
16 words
The method of claim 18 wherein the restraint is a pin axially slidable within the catheter.
Claim 30
Dependent Claim
20 words
The invention of claim 18 wherein the transformation of the alloy occurs without any changes in state of the restraint.
Claim 31
Independent Claim
209 words
A method for inserting a catheter into a mammalian body such that the catheter is substantially at body temperature, the method comprising the steps of: (a) providing a medical device comprising a catheter at least partly formed from a pseudoelastic shape-memory alloy, wherein the alloy can display reversible stress-induced martensite at about body temperature such that the catheter has a stress-induced martensitic state and an austenitic state, the catheter being (i) straightened when the alloy is in its stress-induced martensitic state and (ii) curved when the alloy is in its austenitic state; (b) sliding a straight pin down the catheter axis at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and straightening the catheter; and (c) after step (b), while maintaining the temperature of the catheter above As, inserting the catheter into the body and withdrawing the pin from the catheter so that at least a portion of the alloy transforms from its stress-induced martensitic state to its austenitic state so that the catheter spontaneously transforms from being straightened to being curved, wherein substantially all of the transformation occurs from withdrawing the pin from the catheter and not from any change in temperature of the catheter or the pin.
Claim 32
Independent Claim
209 words
A method for inserting a catheter into a mammalian body such that the catheter is substantially at body temperature, the method comprising the steps of: (a) providing a medical device comprising a catheter at least partly formed from a pseudoelastic shape-memory alloy, wherein the alloy can display reversible stress-induced martensite at about body temperature such that the catheter has a stress-induced martensitic state and an austenitic state, the catheter being (i) straightened when the alloy is in its stress-induced martensitic state and (ii) curved when the alloy is in its austenitic state; (b) sliding a straight pin down the catheter axis at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and straightening the catheter; and (c) after step (b), while maintaining the temperature of the catheter above As, inserting the catheter into the body and withdrawing the pin from the catheter so that at least a portion of the alloy transforms from its stress-induced martensitic state to its austenitic state so that the catheter spontaneously transforms from being straightened to being curved, wherein substantially all of the transformation occurs from withdrawing the pin from the catheter and not from any change in temperature of the catheter or the pin.
Claim 33
Dependent Claim
21 words
The invention of claim 25 wherein the transformation of the alloy occurs without any change in the state of the pin.
Claim 34
Dependent Claim
30 words
The method of claim 25 wherein the catheter is a tracheal puncture catheter, and the step of inserting the catheter into the body comprises inserting the catheter into the trachea.
Claim 35
Dependent Claim
72 words
The method of claim 25 or 27 comprising the additional steps, after step (c), of (d) inserting the pin into the catheter so that at least a portion of the alloy transforms from its austenitic state to its stress-induced martensitic state so that the catheter spontaneously transforms from being curved to being straight for permitting easy withdrawal of the catheter from the body; and (e) withdrawing the straightened catheter from the body.
Claim 36
Dependent Claim
19 words
The method of claim 25 wherein the step of withdrawing the pin comprises removing the pin from the catheter.
Claim 37
Independent Claim
226 words
A method for inserting a medical device into a mammalian body such that the device is substantially at body temperature, the method comprising: (a) providing a medical device comprising a memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the shape-memory alloy displays reversible stress-induced martensite at about body temperature such that the shape-memory alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a straightened shape when the alloy is in its stressed-induced martensitic state and (ii) a different unstressed shape when the alloy is in its austenitic state; (b) placing the memory alloy element into a hollow placement device at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its straightened shape; and (c) while maintaining the temperature of the memory alloy element above the As of the alloy, extruding the memory alloy element from the placement device into the body so that at least a portion of the alloy transforms from its stress-induced martensitic state so that the memory alloy element spontaneously transforms from being straightened to being in its unstressed shape, wherein substantially all of the transformation occurs from disengaging the restraining means and not from any change in temperature of the device or the placement device.
Claim 38
Independent Claim
226 words
A method for inserting a medical device into a mammalian body such that the device is substantially at body temperature, the method comprising: (a) providing a medical device comprising a memory alloy element at least partly formed from a pseudoelastic shape-memory alloy, wherein the shape-memory alloy displays reversible stress-induced martensite at about body temperature such that the shape-memory alloy has a stress-induced martensitic state and an austenitic state, the memory alloy element having (i) a straightened shape when the alloy is in its stressed-induced martensitic state and (ii) a different unstressed shape when the alloy is in its austenitic state; (b) placing the memory alloy element into a hollow placement device at a temperature greater than the As of the alloy for placing the alloy in its stress-induced martensitic state and the memory alloy element in its straightened shape; and (c) while maintaining the temperature of the memory alloy element above the As of the alloy, extruding the memory alloy element from the placement device into the body so that at least a portion of the alloy transforms from its stress-induced martensitic state so that the memory alloy element spontaneously transforms from being straightened to being in its unstressed shape, wherein substantially all of the transformation occurs from disengaging the restraining means and not from any change in temperature of the device or the placement device.
Claim 39
Dependent Claim
19 words
The invention of claim 30 wherein the transformation occurs without any change in the state of the placement device.
Claim 40
Dependent Claim
38 words
The method of claim 30 wherein the memory alloy element is an intrauterine contraceptive device, and the step of extruding the memory alloy element from the placement device into the body comprises extruding the device into the uterus.
Claim 41
Independent Claim
56 words
The method of claims 30 or 32 including the additional steps, after step (c), of (d) withdrawing the memory alloy element into the placement device for placing the alloy in its stress-induced martensitic state and thus straightening the memory alloy element; and (e) withdrawing the placement device and the straightened memory alloy element from the body.
Claim 42
Dependent Claim
48 words
The method of claim 30 wherein the memory alloy element is a stent graft, and the unstressed shape of the stent graft is a tubular coiled shape, and the step of extruding the memory alloy element into the body comprises extruding it into a vessel of the body.
Claim 43
Dependent Claim
37 words
The method of claim 30 wherein the memory alloy element is a filter for trapping blood clots, and the step of extruding the memory alloy element into the body comprises extruding the filter into the vena cava.
Claim 44
Dependent Claim
25 words
The method of claim 30, 32, 34, or 35 wherein the step of extruding comprises completely removing the memory alloy element from the placement device.
Claim 45
Dependent Claim
25 words
The invention of claim 5, 14, or 16 wherein the transformation of the alloy occurs without any change in the state of the restraining means.
Claim 46
Dependent Claim
23 words
The invention of claim 1, 5, 10, 14, 16, or 30 wherein the memory alloy element exerts essentially constant stress during its transformation.
Claim 47
Dependent Claim
17 words
The invention of claim 18 or 25 wherein the catheter exerts essentially constant stress during its transformation.
Claim 48
Dependent Claim
33 words
The method of claim 10 or 14 wherein the step of causing relative movement results in at least a portion of the alloy transforming from its stress-induced martensitic state to its austenitic state.
Claim 49
Dependent Claim
92 words
The method of claim 40 wherein the step of causing relative movement comprises disengaging the restraining means from the memory alloy element, the method including the additional step after step (c) of directly contacting the memory alloy element with the restraining means so that the memory alloy element transforms toward its deformed shape by reversion of at least a portion of the alloy from its austenitic state to its stress-induced martensitic state, wherein the step of directly contacting occurs while maintaining the temperature of the device above the As of the alloy.
References Cited (Backward Citations)
US3416531A
Cited
US3348548A
Cited
US3500820A
Cited
DE1491628B1
Cited
US3516412A
Cited
US3539034A
Cited
US3419012A
Cited
US3620212A
Cited
US4035007A
Cited
US3729008A
Cited
CA1001034A
Cited
US3740839A
Cited
US3857391A
Cited
US3889666A
Cited
US4037324A
Cited
US3868956A
Cited
US3786806A
Cited
US3890977A
Cited
US3939828A
Cited
US3960147A
Cited
US4033331A
Cited
US4149911A
Cited
DE2703529A1
Cited
US4170990A
Cited
US4205293A
Cited
US4197593A
Cited
US4307723A
Cited
US4233690A
Cited
US4230123A
Cited
SU850067A1
Cited
US4310354A
Cited
US4401433A
Cited
SU940759A1
Cited
FR2529083A2
Cited
US4452236A
Cited
US4485816A
Cited
US4427000A
Cited
GB2106190A
Cited
JPS5825140A
Cited
JPS5829443A
Cited
JPS5841546A
Cited
JPS5844047A
Cited
JPS5850951A
Cited
US4425908A
Cited
DE3147722A1
Cited
US4411655A
Cited
US4601283A
Cited
GB2114005A
Cited
JPS58133225A
Cited
DE3225151A1
Cited
US4490112A
Cited
SU1110447A1
Cited
US4509517A
Cited
EP0105669A1
Cited
JPS5997115A
Cited
US4494531A
Cited
US4512338A
Cited
SU1113110A1
Cited
DE3305267A1
Cited
EP0129634A1
Cited
EP0132344A2
Cited
JPS6045356A
Cited
US4586335A
Cited
US4505767A
Cited
US4665906A
Cited
US4543090A
Cited
US4556050A
Cited
US4616656A
Cited
JPS6220827A
Cited
JPS6476824A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-11-25 | 1995-05-27 | 1995-11-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-11-25 | 1999-05-27 | 1999-11-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-11-25 | 2003-05-27 | 2003-11-26 | $7700.00 | Window Closed / Lapsed |