US4490112A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Orthodontic system and method
Assignee: TAKEHIKO DAISAKU 2-194-24 25 SUZUKI-CHO KODAIRA-SHI TOKYO JAPAN A Co OF JAPAN
•
Filing: 1982-09-02
•
Granted: 1984-12-25
•
Expires: 2002-09-02
Abstract
Abstract An orthodontic system including an ultraelastic archwire having a transformation temperature of normal body temperature of about 37° C. is provided. Only a small load is applied to the teeth when the orthodontic system is disposed in a patient's mouth. An increased load is applied to the teeth only when the temperature in the mouth is increased by placing a material having a higher than body temperature in the mouth. As a result, the temperature in the patient's mouth can be controlled without inflicting pain during natural every day actions. The orthodontic effect is available intermittently by raising the mouth temperature for producing higher stress or load which serves to move the teeth orthodontically. The ultaelastic alloy is preferably Ni-Ti alloy containing at least about 50.5 atomic percent of nickel and preferably about 50.7 atomic percent.
Inventors
- 👤 Susumu Tanaka
- 👤 Takehiko Daisaku
- 👤 Yoshihide Suda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:05
CPC Classifications
A; A61; A61C; A61C7/00; A61C7/12; A61C7/20; A61C2201/00; A61C2201/007
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
68 words
An orthodontic arch wire member comprising an alloy of the thermoelastic-type which undergoes a martensitic transformation caused by stress at a temperature above normal body temperature for selectively applying a variable orthodontic load in response to the difference between normal body temperature and a temperature in the mouth above normal body temperature caused by placing a temperature-affecting material having a temperature above normal body temperature in the mouth.
Claim 2
Dependent Claim
68 words
An orthodontic arch wire member comprising an alloy of the thermoelastic-type which undergoes a martensitic transformation caused by stress at a temperature above normal body temperature for selectively applying a variable orthodontic load in response to the difference between normal body temperature and a temperature in the mouth above normal body temperature caused by placing a temperature-affecting material having a temperature above normal body temperature in the mouth.
Claim 3
Dependent Claim
20 words
The orthodontic member of claim 1, wherein said alloy is formed of principally an intermetallic compound of nickel and titanium.
Claim 4
Dependent Claim
23 words
The orthodontic member of claim 2, wherein the inverse martensitic transformation of the Ni-Ti alloy terminates at a temperature below normal body temperature.
Claim 5
Dependent Claim
18 words
The orthodontic member of claim 3, wherein the Ni-Ti alloy comprises at least about 50.5 atomic percent nickel.
Claim 6
Dependent Claim
21 words
The orthodontic member of claim 5 having the shape of a wire with a diameter of about 0.4 mm before polishing
Claim 7
Dependent Claim
23 words
The orthodontic member of claim 3, wherein the Ni-Ti alloy comprises between about 50.5 and 51.0 atomic percent nickel with the balance titanium.
Claim 8
Dependent Claim
20 words
The orthodontic member of claim 3, wherein the Ni-Ti alloy comprises about 50.7 atomic percent nickel with the balance titanium.
Claim 9
Dependent Claim
23 words
The orthodontic member of claim 4, wherein a portion of the nickel is replaced by at least one of copper, iron and cobalt.
Claim 10
Dependent Claim
78 words
An orthodontic arch wire system comprising an orthodontic member comprising an orthodontic member comprising a thermoelastic-type alloy which undergoes a martensitic transformation caused by stress at a temperature above normal body temperature for selectively applying a variable orthodontic load to malaligned teeth in response to a temperature difference between normal body temperature and a temperature in the mouth above normal body temperature caused by placing a temperature-affecting material having a temperature above normal body temperature in the mouth.
Claim 11
Dependent Claim
78 words
An orthodontic arch wire system comprising an orthodontic member comprising an orthodontic member comprising a thermoelastic-type alloy which undergoes a martensitic transformation caused by stress at a temperature above normal body temperature for selectively applying a variable orthodontic load to malaligned teeth in response to a temperature difference between normal body temperature and a temperature in the mouth above normal body temperature caused by placing a temperature-affecting material having a temperature above normal body temperature in the mouth.
Claim 12
Dependent Claim
77 words
An orthodontic method for the orthodontic arch wire movement of teeth comprising coupling to the teeth to be moved an orthodontic member which undergoes a martensitic transformation for select applying a variable orthodontic load in response to the difference between normal body temperature and a temperature caused by placing a temperature-affecting material in the mouth and selectively raising the temperature of the mouth to above normal body temperature to increase the orthodontic load applied to said teeth.
Claim 13
Dependent Claim
77 words
An orthodontic method for the orthodontic arch wire movement of teeth comprising coupling to the teeth to be moved an orthodontic member which undergoes a martensitic transformation for select applying a variable orthodontic load in response to the difference between normal body temperature and a temperature caused by placing a temperature-affecting material in the mouth and selectively raising the temperature of the mouth to above normal body temperature to increase the orthodontic load applied to said teeth.
Claim 14
Dependent Claim
22 words
The orthodontic member of claim 1, wherein the inverse martensitic transformation of Ni-Ti alloy terminates at a temperature above normal body temperature.
References Cited (Backward Citations)
US4037324A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-25 | 1988-06-25 | 1988-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-25 | 1992-06-25 | 1992-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-25 | 1996-06-25 | 1996-12-25 | $7700.00 | Window Closed / Lapsed |