US5064734A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Current-transmitting components for stacked high-temperature fuel cells and method of producing them
Assignee: ABB Asea Brown Boveri Ltd
•
Filing: 1990-10-11
•
Granted: 1991-11-12
•
Expires: 2010-10-11
Abstract
Abstract Current-transmitting components for conducting current between adjacent, planar, stacked high-temperature fuel cells containing solid electrolyte (1) comprising a carrier (7; 10) which determines the geometrical shape and is composed of an oxide-dispersion-hardened nickel or nickel/chromium alloy containing up to 2% by weight of ThO 2 as dispersoid, an electrically conductive Cr 2 O 3 layer (8) and a noble-metal surface layer (9; 12) supported on the latter at the contact/touching faces. Variants having continuous (13; 14) or porous (9; 12) noble-metal surface layer composed of Au, a Pt metal or alloys. Separating plate (4) composed of an oxide-dispersion-hardened nickel/chromium alloy with nickel plating (5) on the fuel side and noble-metal plating (6) on the oxygen side.
Inventors
- 👤 Mohamed Nazmy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:14
CPC Classifications
H; H01; H01M; H01M8/00; H01M8/02; H01M8/0202; H01M8/0204; H01M8/0223; H01M8/0228; H01M8/0206; H01M8/0208; H01M8/023; H01M8/0232; H01M8/0241; H01M8/0245; H01M8/0247; H01M8/24; H01M8/241; H01M8/2425; H01M8/2432; H01M8/10; H01M8/12; H01M2008/1293; H01M2300/00; H01M2300/0017; H01M2300/0065; H01M2300/0068; H01M2300/0071; H01M2300/0074; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108; Y10T29/49115
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
267 words
Current-transmitting components for conducting current between adjacent shallow, planar, stacked ceramic high-temperature fuel cells containing solid electrolyte (1) based on doped stabilized zirconium oxide, the oxygen electrode (2) of one fuel cell being electrically conductively connected in each case to the fuel electrode (3) of the subsequent fuel cell and the gap between the electrodes (2; 3) being subdivided by a gas-impervious electrically conducting separating plate (4) into two chambers conducting the different gaseous media comprising fuel (CH 4 ) and oxygen (O 2 ) carrier, wherein a separating plate (4) composed of an oxide-dispersion-hardened nickel/chromium alloy carrying a nickel plating (5) on the fuel side and a noble-metal plating (6) on the oxygen side is provided, and wherein, furthermore, current collectors are provided both on the fuel side and on the oxygen side, each current collector comprising a carrier (7; 10) which determines the geometrical shape and is composed of electrically conducting oxide-dispersion-hardened nickel or nickel/chromium alloy having a high Cr content at least in the surface zones, ThO 2 being present as dispersoid in a content of up to 2% by weight, furthermore of a porous or impervious noble-metal surface layer (9; 12; 13; 14) which is present only at the contact/touching faces and is made of Au or a Pt metal or an alloy of at least two of said metals, and of a continuous layer (8) which is present between carrier (7; 10) and noble-metal surface layer (9; 12; 13; 14) and is made of electrically conductive Cr 2 O 3 which simultaneously acts as an oxidation protection and as a diffusion barrier.
Claim 2
Dependent Claim
267 words
Current-transmitting components for conducting current between adjacent shallow, planar, stacked ceramic high-temperature fuel cells containing solid electrolyte (1) based on doped stabilized zirconium oxide, the oxygen electrode (2) of one fuel cell being electrically conductively connected in each case to the fuel electrode (3) of the subsequent fuel cell and the gap between the electrodes (2; 3) being subdivided by a gas-impervious electrically conducting separating plate (4) into two chambers conducting the different gaseous media comprising fuel (CH 4 ) and oxygen (O 2 ) carrier, wherein a separating plate (4) composed of an oxide-dispersion-hardened nickel/chromium alloy carrying a nickel plating (5) on the fuel side and a noble-metal plating (6) on the oxygen side is provided, and wherein, furthermore, current collectors are provided both on the fuel side and on the oxygen side, each current collector comprising a carrier (7; 10) which determines the geometrical shape and is composed of electrically conducting oxide-dispersion-hardened nickel or nickel/chromium alloy having a high Cr content at least in the surface zones, ThO 2 being present as dispersoid in a content of up to 2% by weight, furthermore of a porous or impervious noble-metal surface layer (9; 12; 13; 14) which is present only at the contact/touching faces and is made of Au or a Pt metal or an alloy of at least two of said metals, and of a continuous layer (8) which is present between carrier (7; 10) and noble-metal surface layer (9; 12; 13; 14) and is made of electrically conductive Cr 2 O 3 which simultaneously acts as an oxidation protection and as a diffusion barrier.
Claim 3
Dependent Claim
53 words
A current-transmitting component as claimed in claim 1, wherein the noble-metal surface layer (13; 14) is present at the contact/touching faces in a completely continuous and impervious form in a thickness of 5 to 100 μm and the Cr 2 O 3 layer (8) underneath in a thickness of 1 to 20 μm.
Claim 4
Dependent Claim
53 words
A current-transmitting component as claimed in claim 1, wherein the noble-metal surface layer (9; 12) is present at the contact/touching faces in a partially continuous and porous form in a thickness of 5 to 150 μm and the Cr 2 O 3 layer (8) underneath in a thickness of 1 to 20 μm.
Claim 5
Dependent Claim
83 words
A current-transmitting component as claimed in claim 1, wherein it is constructed as separating plate (4) or wherein it is constructed as current collector and has the form of a contact finger or of a corrugated strip or wire or of a wire helix or of a woven metal fabric or of a fleece, and wherein only the points and projections situated nearest the electrodes (2; 3) and/or the separating plate (4) are provided with a noble-metal surface layer (9; 12; 13; 14).
Claim 6
Dependent Claim
156 words
A method of producing a current-transmitting component as claimed in claim 1 which comprises first manufacturing a carrier (7; 10) from the oxide-dispersion-hardened nickel or nickel/chromium alloy by thermo-mechanical treatment and/or mechanical machining from suitable fine-grained input material (semi-finished product in the form of sheet, strip or wire and recrystallizing it under protective gas or vacuum at 1,250° to 1,320° C. for 1/2 h to 3 h to produce a heat-resistant coarse-grained structure and, if nickel is used, electrochemically providing it with an intermediate Cr layer (11) 0.5 to 10 μm thick, roasting in oxygen atmosphere at 800° to 900° C. for 1 to 24 h to form a continuous layer (8) of electrically conductive Cr 2 O 3 , and which comprises providing the carrier (7; 10) coated in this way with a noble-metal surface layer (9; 12; 13; 14) at the contact/touching faces to the electrodes (2; 3) and to the separating plate (4).
Claim 7
Dependent Claim
93 words
The method as claimed in claim 5, wherein, to deposit a porous noble-metal surface layer (9; 12), the carrier (7; 10) is superficially coated at the contact/touching faces with a paste or suspension of noble-metal powder in binder and solvent by brushing, spreading, rolling an impregnated felt or partial immersion and the whole is dried and subjected to a sintering process at 0.7-0.8 of the absolute melting point of the noble metal in inert atmosphere or vacuum and then roasted at 800° to 1,100° C. in oxidizing atmosphere for at least 24 h.
Claim 8
Dependent Claim
53 words
The method as claimed in claim 5, wherein, to deposit a continuous, more or less impervious noble-metal surface layer (13; 14), the carrier (7; 10) is superficially coated electrochemically at the contact/touching faces and the whole is dried and roasted at 800° to 1,100° C. in oxidizing atmosphere for at least 24 h.
References Cited (Backward Citations)
US3300344A
Cited
US3516865A
Cited
US4395468A
Cited
US4692274A
Cited
WO1986006762A1
Cited
EP0338823A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-11-11 | 1995-05-13 | 1995-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-11-11 | 1999-05-13 | 1999-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-11-11 | 2003-05-13 | 2003-11-12 | $7700.00 | Window Closed / Lapsed |