Methods for rapid purging of blowing agents from foamed polymer products
Assignee: Pregis Innovative Packaging Inc
•
Filing: 1989-04-20
•
Granted: 1991-10-22
•
Expires: 2009-04-20
Abstract
Abstract Objects of thermoplastic polymer foam such as, e.g., sheeting of polyolefins such as polyethylene, are treated at elevated temperatures effective to rapidly purge the foam of a substantial portion of the residual blowing agent. Significant economies are achieved by reducing the amounts of residual blowing agents (such as flammable, toxic or environmentally hazardous gases) to levels presenting no fire hazard or other safety hazards in times substantially less than required in conventional aging under ambient conditions. The processes can be carried out in ovens or other heating zones which form continuations of the basic production line, with the extracted blowing agents recycled or disposed of by combustion.
Inventors
- 👤 Thomas M. Pontiff
- 👤 Joseph P. Rapp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:24
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/36; C08J9/0014; B; B29; B29C; B29C44/00; B29C44/34; B29C44/56; B29C44/5609; B29C48/00; B29C48/03; B29C48/07; B29C48/08; B29C48/25; B29C48/88; B29C48/91; B29C71/00; B29C71/02; C08J11/00; C08J11/02; C08J9/04; C08J9/12; C08J9/14; C08J9/143; B29C37/00; B29C37/006; B29K; B29K2105/00; B29K2105/04; C08J2323/00; C08J2323/02; Y; Y10; Y10S; Y10S264/00; Y10S264/15
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
60 words
A method for rapidly purging residual blowing agent from polymeric foam products comprising a step of heating extruded thermoplastic polymer foam structures at an elevated temperature effective to remove a substantial portion of the residual blowing agent from said foam and to cause sufficient air to diffuse into said foam so as not to cause substantial collapse of said foam.
Claim 2
Independent Claim
60 words
A method for rapidly purging residual blowing agent from polymeric foam products comprising a step of heating extruded thermoplastic polymer foam structures at an elevated temperature effective to remove a substantial portion of the residual blowing agent from said foam and to cause sufficient air to diffuse into said foam so as not to cause substantial collapse of said foam.
Claim 3
Dependent Claim
16 words
A method in accordance with claim 1 wherein said elevated temperature is above about 120° F.
Claim 4
Dependent Claim
34 words
A method in accordance with claim 1 wherein said thermoplastic polymer is a polyolefin selected from the group consisting of homopolymers and copolymers comprising olefin monomers having from 2 to about 8 carbon atoms.
Claim 5
Dependent Claim
35 words
A method in accordance with claim 3 wherein said polyolefin is selected from the group consisting of polypropylene, medium density polyethylene, high density polyethylene, low density polyethylene, linear low density polyethylene, polybutylene and mixtures thereof.
Claim 6
Dependent Claim
31 words
A method in accordance with claim 1 wherein a substantial portion of said residual blowing agent is removed in a substantially shorter time than by aging said foam at ambient conditions.
Claim 7
Dependent Claim
18 words
A method in accordance with claim 1 wherein said foam structures are formed as sheets, planks or films.
Claim 8
Dependent Claim
19 words
A method in accordance with claim 1 wherein said structures are moved through a heating zone by transport means.
Claim 9
Dependent Claim
40 words
A method in accordance with claim 7 wherein said polymer structure is a sheet or film which is festooned over driven roller means or plaited in rumpled fashion to increase the surface area thereof which is exposed to the atmosphere.
Claim 10
Dependent Claim
17 words
A method in accordance with claim 7 wherein said transport means include at least one conveyor belt.
Claim 11
Dependent Claim
30 words
A method in accordance with claim 1 wherein said elevated temperature is produced by heating means selected from the group consisting of convection heaters, heated gas currents and radiant heaters.
Claim 12
Dependent Claim
35 words
A method in accordance with claim 1 wherein said polymer foam comprises a permeability adjustment additive in an amount effective to reduce the time required for purging a substantial portion of said residual blowing agent.
Claim 13
Dependent Claim
51 words
A method in accordance with claim 11 wherein said permeability adjustment additives are selected from the group consisting of esters of long-chain fatty acids and polyhydric alcohols, saturated higher fatty acid amides, saturated higher aliphatic amines, complete esters of saturated higher fatty acids, mixtures of glycerol mono- and diglycerides and polystyrenes.
Claim 14
Dependent Claim
26 words
A method in accordance with claim 1 wherein said blowing agent is selected for relatively rapid diffusion through the cell walls of the polymer foam employed.
Claim 15
Dependent Claim
15 words
A method in accordance with claim 1 wherein said blowing agent is a halogenated hydrocarbon.
Claim 16
Dependent Claim
24 words
A method in accordance with claim 1 wherein said blowing agent is selected from the group consisting of hydrocarbons, alcohols, aldehydes, ketones and esters.
Claim 17
Dependent Claim
40 words
A method in accordance with claim 15 wherein the amount of the residual blowing agent is reduced sufficiently to prevent the formation of explosive mixtures with air under ambient conditions in which the purged foam products are transported or stored.
Claim 18
Dependent Claim
35 words
A method in accordance with claim 1 wherein said residual blowing agent is reduced to an amount less than about 2 weight percent of said polymer foam within a time less than about 12 hours.
Claim 19
Dependent Claim
16 words
A method in accordance with claim 17 wherein said time is less than about 3 hours.
Claim 20
Dependent Claim
48 words
A method in accordance with claim 7 wherein an extruded sheet or other elongated foam product is passed through an oven or other chamber for thermal treatment by driven roller means or conveyor belt in a time effective to remove a substantial portion of the residual blowing agent.
Claim 21
Dependent Claim
38 words
A method in accordance with claim 1 wherein said extruded polymer foam product is sheeting which is placed in a oven in rumpled fashion for a time effective to remove a substantial portion of the residual blowing agent.
Claim 22
Dependent Claim
21 words
A method in accordance with claim 20 wherein said foam is retained in said oven for less than about 24 hours.
Claim 23
Dependent Claim
18 words
A method in accordance with claim 19 wherein said oven comprises means for recovering the extracted blowing agent.
Claim 24
Dependent Claim
18 words
A method in accordance with claim 20 wherein said oven comprises means for recovering the extracted blowing agent.
Claim 25
Independent Claim
118 words
A method for rapidly purging residual blowing agent from polyolefin foam products comprising a flammable hydrocarbon blowing agent or a halogenated hydrocarbon blowing agent, said method comprising the steps of: (a) increasing extruded foam sheeting surface area exposed to the atmosphere; and (b) treating said extruded foam sheeting at an elevated temperature above about 120° F. but below the melting temperature of said polyolefin in a heating zone for a time and at a temperature effective to reduce the content of said residual blowing agent in said foam to less than about 2 weight percent of said foam and to cause air to diffuse into said polyolefin foam so as not to cause substantial collapse of said foam.
Claim 26
Independent Claim
118 words
A method for rapidly purging residual blowing agent from polyolefin foam products comprising a flammable hydrocarbon blowing agent or a halogenated hydrocarbon blowing agent, said method comprising the steps of: (a) increasing extruded foam sheeting surface area exposed to the atmosphere; and (b) treating said extruded foam sheeting at an elevated temperature above about 120° F. but below the melting temperature of said polyolefin in a heating zone for a time and at a temperature effective to reduce the content of said residual blowing agent in said foam to less than about 2 weight percent of said foam and to cause air to diffuse into said polyolefin foam so as not to cause substantial collapse of said foam.
Claim 27
Dependent Claim
30 words
A method in accordance with claim 24 wherein said residual blowing agent is reduced to less than about 2 weight percent of said foam within less than about 12 hours.
Claim 28
Dependent Claim
26 words
A method in accordance with claim 24 wherein said foam sheeting is festooned over roller transport means to increase the surface area exposed to the atmosphere.
Claim 29
Dependent Claim
26 words
A method in accordance with claim 24 wherein said foam sheeting is arranged in rumpled fashion upon a conveyor belt for transport through a heating zone.
Claim 30
Dependent Claim
31 words
A method in accordance with claim 24 wherein said blowing agent is selected from the group consisting of ethane, propane, n-butane, isobutane, pentane, neopentane, isopentane, n-hexane, isohexane, cyclohexane and petroleum ether.
Claim 31
Independent Claim
81 words
A method for rapidly purging residual, flammable blowing agent from polyolefin foam products, comprising the step of heating extruded foam sheeting to a temperature range above about 120° F. to below about the melting temperature of said polyolefin for a sufficient time and at a sufficient temperature to purge a substantial portion of the residual blowing agent from said foam products and to cause air to diffuse into the foam so as not to cause substantial collapse of said foam products.
Claim 32
Independent Claim
81 words
A method for rapidly purging residual, flammable blowing agent from polyolefin foam products, comprising the step of heating extruded foam sheeting to a temperature range above about 120° F. to below about the melting temperature of said polyolefin for a sufficient time and at a sufficient temperature to purge a substantial portion of the residual blowing agent from said foam products and to cause air to diffuse into the foam so as not to cause substantial collapse of said foam products.
Claim 33
Dependent Claim
22 words
The method of claim 29 wherein the method is a batch method and wherein said sufficient time is less than 24 hours.
Claim 34
Dependent Claim
27 words
The method of claim 30 wherein the content of the residual, flammable blowing agent is reduced to less than about 2 weight percent of said foam products.
Claim 35
Dependent Claim
22 words
The method of claim 29 wherein the method is a continuous method and wherein said sufficient time is less than 3 hours.
Claim 36
Dependent Claim
27 words
The method of claim 32 wherein the content of the residual, flammable blowing agent is reduced to less than about 2 weight percent of said foam products.
References Cited (Backward Citations)
US2774991A
Cited
US3067147A
Cited
GB844801A
Cited
US3584090A
Cited
US3194854A
Cited
US3808300A
Cited
US3558753A
Cited
US3843757A
Cited
US3616162A
Cited
US3644230A
Cited
US3960792A
Cited
US3647329A
Cited
US3657165A
Cited
US3637458A
Cited
US3640913A
Cited
US3810964A
Cited
US3822331A
Cited
US3725320A
Cited
US3888608A
Cited
US4110269A
Cited
US4214054A
Cited
US4217319A
Cited
US4399086A
Cited
US4347329A
Cited
US4368276A
Cited
US4337321A
Cited
US4426065A
Cited
US4387169A
Cited
US4419309A
Cited
US4420448A
Cited
JPS60122131A
Cited
US4531951A
Cited
US4528300A
Cited
US4649001A
Cited
US4681715A
Cited
US4721591A
Cited
US4657938A
Cited
US4640933A
Cited
US4663361A
Cited
US4694027A
Cited
US4640933B1
Cited
US4721588A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-10-21 | 1995-04-22 | 1995-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-10-21 | 1999-04-22 | 1999-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-10-21 | 2003-04-22 | 2003-10-22 | $7700.00 | Window Closed / Lapsed |