US4426065A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Continuous process for the production of polystyrene foamed articles
Assignee: Sekisui Kaseihin Kogyo KK
•
Filing: 1981-12-15
•
Granted: 1984-01-17
•
Expires: 2001-12-15
Abstract
Abstract This invention relates to a process for producing economically shaped article of polystyrene foam with a small wall thickness and sufficient strength by a continuous simple operation including a short forming cycle in which the sheet of polystyrene foam having a bulk density of 0.15 to 0.7 g/cm3, a thickness of 0.3 to 1.0 mm, 5 to 20 cell membranes widthwise of the sheet and a draw ratio of up to 1.25 and containing 0.03 to 0.3 mole/kg of the residual gas of the blowing agent is formed by an extruder and utilized to produce the shaped article.
Inventors
- 👤 Nobuyuki Komatsuzaki
- 👤 Masahiro Tsubone
- 👤 Bon Machida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:20
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/20; B29C44/22; B32; B32B; B32B5/00; B32B5/18; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/507; B29C44/56; B29C44/5627; B29C44/5636; B29C51/00; B29C51/002; B32B27/00; B32B27/06; B32B27/065; C; C08; C08J; C08J9/00; C08J9/0061; B29K; B29K2009/00; B29K2025/00; B29L; B29L2007/00; B29L2009/00; B29L2031/00; B29L2031/712; B32B38/00; B32B38/0012; B32B2038/0028; B32B2266/00; B32B2266/02; B32B2266/0214; B32B2266/0221; B32B2266/0228; B32B2307/00; B32B2307/50; B32B2307/514; B32B2307/516; B32B2307/518; B32B2307/70; B32B2307/72; C08J2325/00; C08J2325/02
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
155 words
A process for continuously producing shaped articles of polystyrene foam characterized by extruding a polystyrene resin composition which contains 0 to 20% by weight of a rubber as a blend or copolymer component based on the polystyrene resin from the die of an extruder along with a blowing agent to prepare a foamed material, cooling the foamed sheet material to a surface temperature at least not higher than a softening point of the polystyrene resin while stretching the material uniaxially or biaxially to obtain a sheet of polystyrene foam having a bulk density of 0.15 to 0.7 g/cm 3 , a thickness of 0.3 to 1.0 mm, 5 to 20 cell membranes widthwise of the sheet and a draw ratio of up to 1.25 and containing 0.03 to 0.3 mole/kg of the residual gas of the blowing agent, and subsequently thermoforming the resulting sheet into the desired shape with heating substantially without aging the sheet.
Claim 2
Dependent Claim
155 words
A process for continuously producing shaped articles of polystyrene foam characterized by extruding a polystyrene resin composition which contains 0 to 20% by weight of a rubber as a blend or copolymer component based on the polystyrene resin from the die of an extruder along with a blowing agent to prepare a foamed material, cooling the foamed sheet material to a surface temperature at least not higher than a softening point of the polystyrene resin while stretching the material uniaxially or biaxially to obtain a sheet of polystyrene foam having a bulk density of 0.15 to 0.7 g/cm 3 , a thickness of 0.3 to 1.0 mm, 5 to 20 cell membranes widthwise of the sheet and a draw ratio of up to 1.25 and containing 0.03 to 0.3 mole/kg of the residual gas of the blowing agent, and subsequently thermoforming the resulting sheet into the desired shape with heating substantially without aging the sheet.
Claim 3
Dependent Claim
82 words
The process of claim 1 in which the polystyrene resin in the polystyrene resin composition is a polymer of a styrene vinyl monomer, such as styrene, methylstyrene or dimethylstyrene, or a copolymer of such a monomer and another vinyl monomer, such as acrylic acid, methacrylic acid, and ester of such an acid, acrylonitrile, acrylamide, methacrylnitrile or maleic anhydride, which have a weight average molecular weight of about 5×10 4 to about 70×10 4 as determined by the Gel Permeation Chromatograph (GPC) method.
Claim 4
Dependent Claim
19 words
The process of claim 1 in which the rubber as a blend is butadiene, ethylene-propylene, styrene-butadiene or polyethylene rubber.
Claim 5
Dependent Claim
18 words
The process of claim 1 in which the rubber as a copolymer component is butadiene, isoprene or chloroprene.
Claim 6
Dependent Claim
18 words
The process of claim 1 in which the polystyrene resin composition contains 0.1-15% by weight of a rubber.
Claim 7
Dependent Claim
18 words
The process of claim 1 or 3 in which said composition contains 0.3-5% by weight of a rubber.
Claim 8
Dependent Claim
49 words
The process of claim 1 in which the blowing agent is a volatile blowing agent such as propane, butane, pentane, trichloromonofluoromethane, dichlorodifluoromethane or 1,2-dichlorotetrafluoroethane, or mixture thereof and is used in a quantity of 0.03 to 0.4 mole per Kg of the polystyrene resin in the polystyrene resin composition.
Claim 9
Dependent Claim
28 words
The process of claim 1 in which the polystyrene resin composition contain a nucleating agent such as talc, sodium hydrogencarbonate, ammonium hydrogencarbonate, calcium carbonate, clay or citric acid.
Claim 10
Dependent Claim
18 words
The process of claim 1 in which the die has a slit thickness of 0.15 to 0.6 mm.
Claim 11
Dependent Claim
52 words
The process of claim 1 in which a thermoplastic resin film is further laminated to at least one surface of the foamed material to be formed within the die of an extruder or laminated to at least one surface of the foamed material extruded from the die, to obtain a composite sheet.
Claim 12
Dependent Claim
17 words
The process of claim 10 in which a confluent die such as cross head die is used.
Claim 13
Dependent Claim
22 words
The process of claim 11 in which the resin for the thermoplastic resin film is polystyrene, high-density polyethylene or high impact polystyrene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-16 | 1987-07-18 | 1988-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-16 | 1991-07-18 | 1992-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-16 | 1995-07-18 | 1996-01-17 | $7700.00 | Window Closed / Lapsed |