Pressure sensitive adhesives and manufactured articles
Assignee: Rohm and Haas Co
•
Filing: 1989-11-08
•
Granted: 1991-10-01
•
Expires: 2009-11-08
Abstract
Abstract There are disclosed normally tacky, pressure-sensitive adhesive compositions comprising one or more normally tacky polymers having a T g of about 0° C. or less and containing pendant functional groups attached to the backbone and having the formula: ##STR1## in which R 1 is a divalent organic radical at least 3 atoms in length, and X is organoacyl or cyano, the polymers preferably also being normally tacky when cured. Such polymers have markedly improved cohesive strength (shear holding value) with little or no detriment to adhesive tack or adhesion (peel resistance), and these improvements are realized without the necessity of incorporating cross-linking monomers such as N-methylolamides or other cross-linking agents. Pressure-sensitive adhesive, water-based emulsions containing such polymers and pressure-sensitive adhesive articles comprising a substrate having at least a portion of one surface thereof coated with the adhesive compositions are also disclosed. In a preferred embodiment, the adhesive compositions further include a polyacid component for further improving cohesive strength, particularly at acidic pH.
Inventors
- 👤 Lon T. Spada
- 👤 Joseph J. Wilczynski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:52
CPC Classifications
C; C08; C08F; C08F220/00; C08F220/02; C08F220/10; C08F220/12; C09; C09J; C09J157/00; C09J157/04; C09J7/00; C09J7/30; C09J7/38; C09J7/381; C09J7/385; Y; Y10; Y10S; Y10S526/00; Y10S526/931
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
114 words
A mixture comprising (I) a polyacid component selected from the group consisting of (a) aminopolyphosphonic acids, (b) hydroxypolyphosphonic acids, (c) aminopolycarboxylic acids, (d) mixtures of (a), (b), and (c), and (e) salts of (a), (b), (c), and (d), and (II) two or more monomers which are polymerizable to produce a copolymer containing at least one pendant functional group of formula B: ##STR9## in which R 1 is a divalent organic radical of at least 3 atoms in length and X is --CO--R 4 or --CN wherein R 4 is hydrogen or a monovalent organic radical, wherein the mixture, upon polymerization, forms a pressure sensitive adhesive composition and the polyacid is free of carbon-to-carbon unsaturation.
Claim 2
Dependent Claim
114 words
A mixture comprising (I) a polyacid component selected from the group consisting of (a) aminopolyphosphonic acids, (b) hydroxypolyphosphonic acids, (c) aminopolycarboxylic acids, (d) mixtures of (a), (b), and (c), and (e) salts of (a), (b), (c), and (d), and (II) two or more monomers which are polymerizable to produce a copolymer containing at least one pendant functional group of formula B: ##STR9## in which R 1 is a divalent organic radical of at least 3 atoms in length and X is --CO--R 4 or --CN wherein R 4 is hydrogen or a monovalent organic radical, wherein the mixture, upon polymerization, forms a pressure sensitive adhesive composition and the polyacid is free of carbon-to-carbon unsaturation.
Claim 3
Dependent Claim
22 words
The mixture of claim 1 wherein the polyacid component is present in an amount effective for increasing cohesive strength under acidic conditions.
Claim 4
Dependent Claim
20 words
The mixture of claim 1 comprising at least about 0.1 weight percent polyacid based on the weight of the polymer.
Claim 5
Dependent Claim
21 words
The mixture of claim 1 comprising about 0.1 to about 20 weight percent polyacid based on the weight of the polymer.
Claim 6
Dependent Claim
21 words
The mixture of claim 1 comprising about 0.5 to about 10 weight percent polyacid based on the weight of the polymer.
Claim 7
Dependent Claim
21 words
The mixture of claim 1 comprising about 0.5 to about 5 weight percent polyacid based on the weight of the polymer.
Claim 8
Dependent Claim
12 words
The mixture of claim 1 wherein the polyacid is an aminopolycarboxylic acid.
Claim 9
Dependent Claim
46 words
The mixture of claim 1 wherein the polyacid is an aminopolycarboxylic acid selected from the group consisting of ethylenediaminetetraacetic acid, N-hydroxyethylethylenediaminetriacetic acid, nitrilotriacetic acid, iminodiacetic acid, methyliminodiacetic acid, diethylenetriaminepentaacetic acid, and 1,2-diaminocyclohexanetetraacetic acid or salt thereof or (b) at least one aminopolyphosphonic acid or salt thereof.
Claim 10
Dependent Claim
22 words
The mixture of claim 1 wherein the polyacid is selected from the group consisting of ethylenediaminetetraacetic acid and the tetrasodium salt thereof.
Claim 11
Dependent Claim
36 words
The mixture of claim 1 wherein the polyacid is an aminopolycarboxylic acid or salt thereof and is present in an amount of about 0.5 to about 5 weight percent based on the weight of the polymer.
Claim 12
Dependent Claim
18 words
The mixture of claim 1 wherein the pressure sensitive adhesive composition has a pH less than about 6.5.
Claim 13
Dependent Claim
18 words
The mixture of claim 1 wherein the pressure sensitive adhesive composition has a pH less than about 6.
Claim 14
Dependent Claim
40 words
The mixture of claim 1 wherein the polyacid is an aminopolycarboxylic acid or salt thereof and is present in an amount effective for increasing cohesive strength of the pressure sensitive adhesive composition at a pH of about 6.5 or less.
Claim 15
Dependent Claim
52 words
The mixture of claim 1 wherein the pressure sensitive adhesive composition has a pH of about 6 or less, the polyacid is the tetrasodium salt of ethylenediaminetetraacetic acid and is present in the mixture in an amount from about 0.5 to about 5 weight percent based on the weight of the polymer.
Claim 16
Dependent Claim
40 words
The mixture of claim 1 further comprising at least one olefinically unsaturated carboxylic acid ester monomer, the olefinically unsaturated carboxylic acid ester monomers being present in a concentration sufficient to constitute at least about 40 weight percent of the polymer.
Claim 17
Dependent Claim
81 words
The mixture of claim 1 further comprising at least one monoolefin monomer having up to about 4 carbon atoms and at least one alkenyl or alkenol ester of a saturated carboxylic acid monomer, the monoolefin monomers being present in a concentration sufficient to constitute at least about 1 weight percent of the polymer and the alkenyl and alkenol ester of saturated carboxylic acid monomers being present in a concentration sufficient to constitute at least about 40 weight percent of the polymer.
Claim 18
Dependent Claim
40 words
The mixture of claim 1 wherein at least one of the monomers has the formula A: ##STR10## in which R 5 and R 6 are independently selected from the group consisting of hydrogen, hydroxy, halo, amino and monovalent organic radicals.
Claim 19
Dependent Claim
11 words
The mixture of claim 1 wherein X is --CO--R 4 .
Claim 20
Dependent Claim
39 words
The mixture of claim 1 wherein R 1 is a divalent organic radical of about 3 to about 40 carbon atoms in length, and R 4 is hydrogen or an alkyl group having 1 to about 8 carbon atoms.
Claim 21
Dependent Claim
69 words
The mixture of claim 1 comprising at least about 0.1 weight percent polyacid based on the weight of the polymer, further comprising at least one olefinically unsaturated carboxylic acid ester monomer, the olefinically unsaturated carboxylic acid ester monomers being present in a concentration sufficient to constitute at least about 40 weight percent of the polymer, and wherein the pressure sensitive adhesive composition has a pH less than about 6.
Claim 22
Dependent Claim
70 words
The mixture of claim 1 comprising about 0.1 to about 20 weight percent polyacid based on the weight of the polymer, further comprising at least one olefinically unsaturated carboxylic acid ester monomer, the olefinically unsaturated carboxylic acid ester monomers being present in a concentration sufficient to constitute at least about 60 weight percent of the polymer, and wherein the pressure sensitive adhesive composition has a pH less than about 6.5.
Claim 23
Dependent Claim
96 words
The mixture of claim 21 wherein the olefinically unsaturated carboxylic acid ester monomer is selected from the group consisting of esters of acrylic acid and methacrylic acid having 4 to about 17 carbon atoms, the polymer has a T g of about -10° C. or less and comprises at least about 0.1 weight percent of a functional monomer the formula A: ##STR11## in which R 5 and R 6 are independently selected from the group consisting of hydrogen, hydroxy, halo, amino and monovalent organic radicals, and the pressure sensitive adhesive composition is normally tacky when cured.
Claim 24
Dependent Claim
77 words
The mixture of claim 22 wherein the functional monomer is selected from the group consisting of acetoacetoxyethyl methacrylate, acetoacetoxyethyl acrylate and combinations thereof, the functional monomer being present in an amount from about 0.1 to about 10 weight percent based on the weight of the polymer, and the polyacid is the tetrasodium salt of ethylenediaminetetraacetic acid and is present in a concentration of about 0.5 to about 5 weight percent based on the weight of the polymer.
References Cited (Backward Citations)
US3345336A
Cited
US3658878A
Cited
US3554987A
Cited
US3459790A
Cited
US3488708A
Cited
NL6707437A
Cited
GB1185216A
Cited
GB1144486A
Cited
US3607834A
Cited
GB1541909A
Cited
US4421889A
Cited
US4250070A
Cited
US4371659A
Cited
US4414275A
Cited
US4408018A
Cited
US4540739A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-30 | 1995-04-01 | 1995-10-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-30 | 1999-04-01 | 1999-10-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-30 | 2003-04-01 | 2003-10-01 | $7700.00 | Window Closed / Lapsed |