Antireflection solution for optical parts and method for antireflection treatment using said solution
Assignee: Itoh Optical Industrial Co Ltd
•
Filing: 1987-10-24
•
Granted: 1991-09-17
•
Expires: 2007-10-24
Abstract
Abstract This invention is directed to an antireflection solution having as a main film-forming component thereof a hydrolytic derivative of a silicic ester and to a method for the treatment with the antireflection solution. The antireflection solution and the method for the treatment therewith are characterized by the fact that the hydrolytic derivative of silicic ester is obtained by causing a mixture consisting of the silicic ester and hydrolyzing water added thereto in an amount exceeding the chemical equivalent relative to the silicic ester to be hydrolyzed in the presence of a solvent compatible with both of the components of the mixture and further subjecting the resultant hydrolyzate to conversion into a colloid solution under the condition of pH 3 to 7. Owing to the characteristics mentioned above, the present invention permits the antireflection film produced by thermally solidifying an applied layer of the antireflection solution at a low temperature in the neighborhood of 100° C. to acquire notable improvement in film properties such as resistance to defilement and adhesiveness to the substrate.
Inventors
- 👤 Hirohisa Kato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:59
CPC Classifications
G; G02; G02B; G02B1/00; G02B1/10; G02B1/11; G02B1/111
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
183 words
A solution for making an optical part non-reflecting comprising: a) a hydrolytic derivative of a silicic ester of the formula Si(OR) 4 , wherein R is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group, said hydrolytic derivative having been obtained by hydrolyzing 1 mole of the silicic ester with 5-60 mols of water in the presence of a solvent compatible with both the silicic ester and water to form a hydrolyzate and heating the hydrolyzate at a pH of 3-7; b) a hydrolyzate of a silicon compound of the formula ##STR5## wherein R 1 is an alkyl group of 1 to 6 carbon atoms, a vinyl group, an epoxy group, a methacryloxy group or a phenyl group; R 2 is an alkyl group of 1 to 6 carbon atoms or a halogenated alkyl group; R 3 is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group; and a and b each are 0, 1, or 2, provided that a+b is 1, 2, or 3; and c) colloidal silica.
Claim 2
Dependent Claim
183 words
A solution for making an optical part non-reflecting comprising: a) a hydrolytic derivative of a silicic ester of the formula Si(OR) 4 , wherein R is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group, said hydrolytic derivative having been obtained by hydrolyzing 1 mole of the silicic ester with 5-60 mols of water in the presence of a solvent compatible with both the silicic ester and water to form a hydrolyzate and heating the hydrolyzate at a pH of 3-7; b) a hydrolyzate of a silicon compound of the formula ##STR5## wherein R 1 is an alkyl group of 1 to 6 carbon atoms, a vinyl group, an epoxy group, a methacryloxy group or a phenyl group; R 2 is an alkyl group of 1 to 6 carbon atoms or a halogenated alkyl group; R 3 is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group; and a and b each are 0, 1, or 2, provided that a+b is 1, 2, or 3; and c) colloidal silica.
Claim 3
Independent Claim
210 words
A method for making an optical part non-reflecting which comprises contacting the surface of the optical part with a solution comprising: a) a hydrolytic derivative of a silicic ester of the formula Si(OR) 4 , wherein R is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group, said hydrolytic derivative having been obtained by hydrolyzing 1 mole of the silicic ester with 5-60 moles of water in the presence of a solvent compatible with the silicic ester and water to form a hydrolyzate and heating the hydrolyzate at a pH of 3-7; b) a hydrolyzate of a silicon compound of the formula ##STR6## wherein R 1 is an alkyl group of 1 to 6 carbon atoms, a vinyl group, an epoxy group, a methacryloxy group or a phenyl group; R 2 is an alkyl group of 1 to 6 carbon atoms or a halogenated alkyl group; R 3 is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group; and a and b each are 0, 1, or 2, provided that a+b is 1, 2 or 3; and c) colloidal silica; and heating the solution to form a non-reflecting film on the surface of the optical part.
Claim 4
Independent Claim
210 words
A method for making an optical part non-reflecting which comprises contacting the surface of the optical part with a solution comprising: a) a hydrolytic derivative of a silicic ester of the formula Si(OR) 4 , wherein R is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group, said hydrolytic derivative having been obtained by hydrolyzing 1 mole of the silicic ester with 5-60 moles of water in the presence of a solvent compatible with the silicic ester and water to form a hydrolyzate and heating the hydrolyzate at a pH of 3-7; b) a hydrolyzate of a silicon compound of the formula ##STR6## wherein R 1 is an alkyl group of 1 to 6 carbon atoms, a vinyl group, an epoxy group, a methacryloxy group or a phenyl group; R 2 is an alkyl group of 1 to 6 carbon atoms or a halogenated alkyl group; R 3 is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group; and a and b each are 0, 1, or 2, provided that a+b is 1, 2 or 3; and c) colloidal silica; and heating the solution to form a non-reflecting film on the surface of the optical part.
Claim 5
Dependent Claim
154 words
A method according to claim 2, comprising the additional step of treating the non-reflecting film with a solution containing a silicon compound of the formula ##STR7## wherein R 4 is an alkyl group of 1 to 4 carbon atoms, an alkyoxyalkyl group; or an acyl group; a is an integer of 1 to 4; and b is an integer of 1 to 7; ##STR8## wherein R 5 and R 6 are each an alkoxy group of 1 to 4 carbon atoms, a hydroxyl group, an amino group, a vinyl group, a methacryloxy group, an epoxy group or a carboxyl group; and a is an integer of 0 to 10; or F.sub.3 C--(CF.sub.2).sub.a --(R.sup.7)--Si--(OR.sup.8).sub.3 wherein R 7 is an alkylene group of 1 to 4 carbon atoms; R 8 is an alkyl group of 1 to 4 carbon atoms, an alkoxyalkyl group or an acyl group; and a is an integer of 1 to 10.
Claim 6
Dependent Claim
46 words
A method according to claim 2, wherein the optical part is made of a transparent plastic material selected from the group consisting of polydiethylene glycol bisallyl carbonate, polymethylmethacrylate and polycarbonate hard coated with a polysiloxane, an acrylic polymer, a melamine polymer, a polyester or a polyurethane.
Claim 7
Dependent Claim
16 words
A method according to claim 2, wherein the optical part is made of an inorganic glass.
References Cited (Backward Citations)
US4211823A
Cited
US4361598A
Cited
US4272588A
Cited
US4374158A
Cited
US4547397A
Cited
US4551361A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-16 | 1995-03-18 | 1995-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-16 | 1999-03-18 | 1999-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-16 | 2003-03-18 | 2003-09-17 | $7700.00 | Window Closed / Lapsed |