Tintable scratch resistant coating
Assignee: Techneglas LLC
•
Filing: 1985-03-25
•
Granted: 1985-10-15
•
Expires: 2005-03-25
Abstract
Abstract A tintable coating is applied to a transparent substrate such as a polycarbonate lens. The coating is made from a coating solution of (1) a further curable organopolysiloxane preferably made by hydrolyzing ethyl ortho silicate with methacryloxytrimethoxy silane and/or vinyltriethoxy silane with phenylphosphonic acid, and an (2) organic solvent for the organopolysiloxane. The coating is cured, an azo dye applied to the cured coating to provide a highly tinted coating without sacrificing scratch resistance. The cured coating can be tinted with an improved tinting speed and the resultant cured tinted coating has improved abrasion resistance.
Inventors
- 👤 Alfred J. Burzynski
- 👤 James J. Tillman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 16:00
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/04; C09D183/06; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/046; G02B1/105; G; G02; G02B; G02B1/00; G02B1/10; G02B1/14; C08J2369/00; C08J2483/00; C08J2483/04; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31507; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
101 words
A composition for providing a scratch resistant, tintable cured coating for a substrate, the composition comprising (A) a further curable, solvent soluble organopolysiloxane that is a hydrolysis reaction product of methacryloxypropyltrimethoxy silane, ethyl ortho silicate, and water; (B) phenylphosphonic acid as an additive to part (A) before coating the substrate or used in the hydrolysis as a starting ingredient to obtain the reaction product of (A); and (C) an organic solvent for (A) and (B), the solution being adapted for coating and curing to form a scratch resistant azo dye tintable cured coating that has improved abrasion resistance and improved tintability.
Claim 2
Dependent Claim
101 words
A composition for providing a scratch resistant, tintable cured coating for a substrate, the composition comprising (A) a further curable, solvent soluble organopolysiloxane that is a hydrolysis reaction product of methacryloxypropyltrimethoxy silane, ethyl ortho silicate, and water; (B) phenylphosphonic acid as an additive to part (A) before coating the substrate or used in the hydrolysis as a starting ingredient to obtain the reaction product of (A); and (C) an organic solvent for (A) and (B), the solution being adapted for coating and curing to form a scratch resistant azo dye tintable cured coating that has improved abrasion resistance and improved tintability.
Claim 3
Dependent Claim
25 words
A composition as defined in claim 1 in which the amount of water used is about 1.5 moles to 7 moles per mole of silane.
Claim 4
Dependent Claim
30 words
A composition as defined in claim 1 in which the amount of phenylphosphonic acid used is about 1 to 4 parts by weight per 100 parts of silane starting material.
Claim 5
Dependent Claim
39 words
A composition as defined in claim 1 in which about 5 to 40 parts by weight of vinyltriethoxysilane and about 5 to 40 parts of ethyl ortho silicate per 100 parts total silane is used with the methacryloxypropyltrimethoxy silane.
Claim 6
Dependent Claim
38 words
A composition as defined in claim 1 in which the silane starting material is about 40 parts by weight of vinyltriethoxysilane, about 20 parts by weight of ethyl ortho silicate and 40 parts by weight of methacryloxypropyltrimethoxy silane.
Claim 7
Dependent Claim
20 words
A composition as defined in claim 1 in which about 2.3 moles of water is used per mole of silane.
Claim 8
Dependent Claim
14 words
A composition as defined in claim 1 in which the organic solvent is n-butanol.
Claim 9
Dependent Claim
22 words
A composition as defined in claim 1 in which the azo dye is a mixture of azo dyes including Congo Red ##STR2##
Claim 10
Dependent Claim
21 words
A composition as directed in claim 1 in which the azo dye is a mixture of dyes including Orange 11 ##STR3##
Claim 11
Independent Claim
112 words
A method of producing a scratch resistant, cured, tintable coating on a transparent substrate without reducing the tinting absorbency at the expense of greater adhesion and scratch resistance, the method comprising the steps of: (A) hydrolyzing methacryloxypropyltrimethoxy silane, ethyl ortho silicate and vinyltriethoxy silane with 1 to 7 moles of water and phenylphosphonic acid to provide a solvent soluble, further curable organopolysiloxane; (B) dissolving the organopolysiloxane of step (A) in an organic solvent; (C) adding phenylphosphonic acid to the solution of (B) and dissolving the same; (D) coating a transparent substrate with the solution of (C); (E) heating the coating to cure the organopolysiloxane and provide a tintable, cured, scratch resistant coating.
Claim 12
Independent Claim
112 words
A method of producing a scratch resistant, cured, tintable coating on a transparent substrate without reducing the tinting absorbency at the expense of greater adhesion and scratch resistance, the method comprising the steps of: (A) hydrolyzing methacryloxypropyltrimethoxy silane, ethyl ortho silicate and vinyltriethoxy silane with 1 to 7 moles of water and phenylphosphonic acid to provide a solvent soluble, further curable organopolysiloxane; (B) dissolving the organopolysiloxane of step (A) in an organic solvent; (C) adding phenylphosphonic acid to the solution of (B) and dissolving the same; (D) coating a transparent substrate with the solution of (C); (E) heating the coating to cure the organopolysiloxane and provide a tintable, cured, scratch resistant coating.
Claim 13
Dependent Claim
34 words
A method as defined in claim 10 including the further step of (F) applying an azo dye to the cured coating of step (E) to provide a tinted, scratch resistant coating on the substrate.
Claim 14
Independent Claim
120 words
A method of producing a cured, tinted, scratch resistant coating on a transparent substrate, the method comprising the steps of: (A) hydrolyzing methacryloxypropyltrimethoxy silane and ethyl ortho silicate with about 1 to 7 moles of water and phenylphosphonic acid to provide a solvent soluble, further curable organopolysiloxane; (B) dissolving the organopolysiloxane of step (A) in an organic solvent; (C) adding phenylphosphonic acid to the solution of (B) and dissolving the same; (D) coating a transparent substrate with the solution of (C); (E) heating the coating to cure the organopolysiloxane and provide a tintable, cured, scratch resistant coating; and (F) applying an azo dye to the cured coating of step (E) to provide a tinted, scratch resistant coating on the substrate.
Claim 15
Independent Claim
120 words
A method of producing a cured, tinted, scratch resistant coating on a transparent substrate, the method comprising the steps of: (A) hydrolyzing methacryloxypropyltrimethoxy silane and ethyl ortho silicate with about 1 to 7 moles of water and phenylphosphonic acid to provide a solvent soluble, further curable organopolysiloxane; (B) dissolving the organopolysiloxane of step (A) in an organic solvent; (C) adding phenylphosphonic acid to the solution of (B) and dissolving the same; (D) coating a transparent substrate with the solution of (C); (E) heating the coating to cure the organopolysiloxane and provide a tintable, cured, scratch resistant coating; and (F) applying an azo dye to the cured coating of step (E) to provide a tinted, scratch resistant coating on the substrate.
Claim 16
Independent Claim
120 words
A method of producing a cured, tinted, scratch resistant coating on a transparent substrate, the method comprising the steps of: (A) hydrolyzing vinyltriethoxy silane and ethyl ortho silicate with about 1 to 7 moles of water and phenylphosphonic acid to provide a solvent soluble, further curable organopolysiloxane; (B) dissolving the organopolysiloxane of step (A) in an organic solvent; (C) adding phenylphosphonic acid to the solution of (B) and dissolving the same; (D) coating a transparent substrate with the solution of (C); (E) heating the coating to cure the organopolysiloxane and provide a tintable, cured, scratch resistant coating; and (F) applying an azo dye to the cured coating of step (E) to provide a tinted, scratch resistant coating on the substrate.
Claim 17
Independent Claim
120 words
A method of producing a cured, tinted, scratch resistant coating on a transparent substrate, the method comprising the steps of: (A) hydrolyzing vinyltriethoxy silane and ethyl ortho silicate with about 1 to 7 moles of water and phenylphosphonic acid to provide a solvent soluble, further curable organopolysiloxane; (B) dissolving the organopolysiloxane of step (A) in an organic solvent; (C) adding phenylphosphonic acid to the solution of (B) and dissolving the same; (D) coating a transparent substrate with the solution of (C); (E) heating the coating to cure the organopolysiloxane and provide a tintable, cured, scratch resistant coating; and (F) applying an azo dye to the cured coating of step (E) to provide a tinted, scratch resistant coating on the substrate.
Claim 18
Dependent Claim
87 words
A composition for providing a scratch resistant, tintable cured coating for a transparent substrate, the composition comprising (A) a further curable, solvent soluble organopolysiloxane that is a hydrolysis reaction product of vinyltriethoxy silane, ethyl ortho silicate, and water; (B) phenylphosphonic acid as an additive to part (A) before coating the substrate or used in the hydrolysis as a starting ingredient; and (C) an organic solvent for (A) and (B), the solution being adapted for coating and curing to form a scratch resistant azo dye tintable cured coating.
Claim 19
Dependent Claim
87 words
A composition for providing a scratch resistant, tintable cured coating for a transparent substrate, the composition comprising (A) a further curable, solvent soluble organopolysiloxane that is a hydrolysis reaction product of vinyltriethoxy silane, ethyl ortho silicate, and water; (B) phenylphosphonic acid as an additive to part (A) before coating the substrate or used in the hydrolysis as a starting ingredient; and (C) an organic solvent for (A) and (B), the solution being adapted for coating and curing to form a scratch resistant azo dye tintable cured coating.
Claim 20
Dependent Claim
18 words
A cured, tinted, scratch resistant coating on a transparent substrate, the coating made as defined in claim 12.
Claim 21
Dependent Claim
12 words
A cured tinted scratch resistant coating made as defined in claim 13.
Claim 22
Dependent Claim
16 words
A tintable, scratch resistant coating on a substrate, the coating made as defined in claim 10.
Claim 23
Dependent Claim
96 words
A cured, tinted, scratch resistant coating for a polycarbonate substrate, the coating made by hydrolyzing methacryloxypropyltrimethoxy silane, ethyl ortho silicate, and vinyltriethoxy silane with about 2 to 3 moles of water per mole of silane with phenylphosphonic acid to provide a solvent soluble, further curable organopolysiloxane, the organopolysiloxane being dissolved in an organic solvent along with additional phenylphosphonic acid to form a coating solution that is applied to the polycarbonate surface and the resultant coating cured, an azo dye being applied to the cured coating and thereafter heated to form a tinted, cured, scratch resistant coating.
Claim 24
Dependent Claim
96 words
A cured, tinted, scratch resistant coating for a polycarbonate substrate, the coating made by hydrolyzing methacryloxypropyltrimethoxy silane, ethyl ortho silicate, and vinyltriethoxy silane with about 2 to 3 moles of water per mole of silane with phenylphosphonic acid to provide a solvent soluble, further curable organopolysiloxane, the organopolysiloxane being dissolved in an organic solvent along with additional phenylphosphonic acid to form a coating solution that is applied to the polycarbonate surface and the resultant coating cured, an azo dye being applied to the cured coating and thereafter heated to form a tinted, cured, scratch resistant coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-14 | 1989-04-15 | 1989-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-14 | 1993-04-15 | 1993-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-14 | 1997-04-15 | 1997-10-15 | $7700.00 | Window Closed / Lapsed |