Coating composition
Assignee: Sola International Inc
•
Filing: 1978-04-18
•
Granted: 1979-11-06
•
Expires: 1998-04-18
Abstract
Abstract A coating composition which results from hydrolyzing 40 to 70 weight per cent tetraethyl orthosilicate and 60 to 20 weight per cent of certain silane is useful for providing abrasion resisting coatings for plastics after curing. Optionally, up to 20 weight percent of a silane having a reactive polar site or, in the alternative, a small percentage of a surfactant may be used to provide a dyeable coated article.
Inventors
- 👤 Don H. Rotenberg
- 👤 Patricia M. Cuffe
- 👤 Bernard L. Laurin
- 👤 Peter R. Ramirez
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 07:46
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/04; C09D183/06; C09D183/08; G02B1/105; G; G02; G02B; G02B1/00; G02B1/10; G02B1/14; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31507
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
68 words
A coating composition which is curable to provide an optically clear abrasion resistant coating, which comprises a product of the hydrolysis of about 40 to 70 weight percent tetraethyl orthosilicate and 60 to 20 weight percent of a silane selected from the group consisting of methyltrimethoxysilane, methyltrietheoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane and mixtures thereof and up to 20 weight percent of a siloxane having a reactive polar site.
Claim 2
Dependent Claim
68 words
A coating composition which is curable to provide an optically clear abrasion resistant coating, which comprises a product of the hydrolysis of about 40 to 70 weight percent tetraethyl orthosilicate and 60 to 20 weight percent of a silane selected from the group consisting of methyltrimethoxysilane, methyltrietheoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane and mixtures thereof and up to 20 weight percent of a siloxane having a reactive polar site.
Claim 3
Dependent Claim
34 words
The coating composition according to claim 1 wherein about 60 weight percent tetraethyl orthosilicate and about 40 weight percent methyltrimethoxysilane were hydrolyzed with a mixture of water, alcohol and acetic acid and then aged.
Claim 4
Dependent Claim
33 words
The coating composition according to claim 1 wherein about 50 weight percent tetraethyl orthosilicate and 50 weight percent methyltrimethoxysilane were hydrolyzed with a mixture of water, alcohol and acetic acid and then aged.
Claim 5
Dependent Claim
18 words
The coating composition according to claim 1 further including at least 1.0 weight percent of a non-ionic surfactant.
Claim 6
Dependent Claim
22 words
The coating composition according to claim 4 wherein the surfactant is selected from the group consisting of Triton X-100 and Fluorad FC-430.
Claim 7
Dependent Claim
28 words
The coating composition according to claim 1 wherein the silane having the reactive polar site is selected from the group consisting of 3-chloropropyltrimethoxysilane, 3-glycidylpropyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, bis(2-hydroxyethyl)aminopropyltrimethoxysilane, and (3,4-epoxycyclohexyl)ethyltrimethoxysilane.
Claim 8
Dependent Claim
37 words
The coating composition according to claim 1 wherein about 60 weight percent tetraethyl orothosilicate, 30 weight percent methyltrimethoxysilane and 10 weight percent 3-methyacryloxypropyltrimethoxysilane were hydrolyzed with a mixture of water, alcohol and acetic acid and then aged.
Claim 9
Dependent Claim
39 words
The coating composition according to claim 1 wherein about 57 weight percent tetraethyl orthosilicate, about 28 weight percent methyltrimethoxysilane and about 15 weight percent bis(2-hydroxyethyl)aminopropyltriethoxysilane were hydrolyzed with a mixture of water, alcohol and acetic acid and then aged.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-05 | 1983-05-07 | 1983-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-05 | 1987-05-07 | 1987-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-05 | 1991-05-07 | 1991-11-06 | $7700.00 | Window Closed / Lapsed |