Method for producing compound semiconductor single crystal substrates
Assignee: Eneos Corp
•
Filing: 1990-07-03
•
Granted: 1991-09-10
•
Expires: 2010-07-03
Abstract
Abstract A method for producing compound semiconductor single crystal substrates which comprises the following steps, wafers of a compound semiconductor single crystal grown by the LEC method are installed in an evacuated and sealed quartz ampoule and subjected to a first annealing step at the predetermined temperature for the predetermined period, then the wafers are gradually cooled down to room temperature at the predetermined cooling speed, the cooled wafers are then subjected to etching, the etched wafers are subjected to a second annealing step at the predetermined temperature for the predetermined period in a non-oxidizing atmosphere, and finally, the wafers are gradually cooled down to room temperature.
Inventors
- 👤 Hiromasa Yamamoto
- 👤 Masayuki Mori
- 👤 Osamu Oda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:09
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/10; C30B29/40; C30B29/42; C30B33/00; Y; Y10; Y10S; Y10S148/00; Y10S148/065; Y10S438/00; Y10S438/974
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
131 words
A method for producing compound semiconductor single crystal substrates comprising: a first annealing step including installing wafers of a grown compound semiconductor single crystal into an evacuated and sealed quartz ampoule and subjecting the wafers to a first heat-treatment at a temperature higher than 1100° C. and lower than the melting point of the single crystal for at least 30 minutes; a first cooling step, for gradually cooling the heat-treated wafers to room temperature at a cooling rate from 1° to 30° C./min; etching the cooled wafers; a second annealing step including subjecting the etched wafers to a second heat-treatment at temperatures between 750° C. and 1100° C. for at least 20 minutes in a non-oxidizing atmosphere; and a second cooling step, for cooling the heat-treated wafers gradually to room temperature.
Claim 2
Independent Claim
131 words
A method for producing compound semiconductor single crystal substrates comprising: a first annealing step including installing wafers of a grown compound semiconductor single crystal into an evacuated and sealed quartz ampoule and subjecting the wafers to a first heat-treatment at a temperature higher than 1100° C. and lower than the melting point of the single crystal for at least 30 minutes; a first cooling step, for gradually cooling the heat-treated wafers to room temperature at a cooling rate from 1° to 30° C./min; etching the cooled wafers; a second annealing step including subjecting the etched wafers to a second heat-treatment at temperatures between 750° C. and 1100° C. for at least 20 minutes in a non-oxidizing atmosphere; and a second cooling step, for cooling the heat-treated wafers gradually to room temperature.
Claim 3
Dependent Claim
61 words
The method according to claim 1, including cutting from a single crystal grown by a pulling-up technique, said single crystal being grown by applying the vapor pressure of a high dissociation pressure element put into an inner container set in a high pressure chamber, and whose microscopic defect density revealed by AB etchant is less than 2×10 5 cm -2 .
Claim 4
Dependent Claim
13 words
The method of claim 2, wherein said wafers are GaAs single crystal wafers.
Claim 5
Dependent Claim
32 words
The method according to claim 1, including carrying out said annealing step in a non-oxidizing atmosphere such as nitrogen gas, hydrogen gas, AsH 3 gas, inert gas, Ar gas, or a vacuum.
Claim 6
Dependent Claim
18 words
The method of claim 1 wherein said compound is selected from the group consisting of group III-V compounds.
Claim 7
Dependent Claim
22 words
The method of claim 1 wherein the second annealing step is carried out at a temperature between 900° C. and 1000° C.
Claim 8
Dependent Claim
16 words
The method of claim 1 wherein the second annealing is run for at least 1 hour.
Claim 9
Dependent Claim
26 words
The method of claim 1 wherein said heated quartz ampoule is supplied with arsenic gas up to an arsenic pressure of 1 atm at 1150° C.
Claim 10
Dependent Claim
77 words
The method according to claim 1, wherein said etching step includes installing said wafers into a container containing an etchant, said container being made of Teflon, quartz, or a commercially produced etching apparatus; and including carrying out the etching treatment for 20 minutes by moving said wafers in the container to apply the etching treatment to etch both surfaces of each of said wafers to remove soils attached on their surfaces that are formed by cutting work.
Claim 11
Dependent Claim
27 words
The method of claim 9 wherein said etchant is essentially composed of NaOH 25 g, H 2 O 2 100 cc, and H 2 O 2000 cc.
Claim 12
Dependent Claim
29 words
The method of claim 9 wherein said etchant is essentially composed of H 2 SO:H 2 O 2 :H 2 O, having a volume ratio from 1:1:1 to 10:1:1.
Claim 13
Dependent Claim
27 words
The method of claim 9 wherein said etchant is essentially composed of HCl:H 2 O 2 :H 2 O, having a volume ratio from 1:1:1 to 10:1:1.
Claim 14
Dependent Claim
27 words
The method of claim 9 wherein said etchant is essentially composed of Br 2 :methanol with a volume ratio of Br 2 of from 0.5 to 10%.
Claim 15
Dependent Claim
31 words
The method of claim 9 wherein said etchant is essentially composed of H 3 PO 4 :H 2 O 2 :H 2 O, having a volume ratio from 1:1:1 to 10:1:1.
Claim 16
Dependent Claim
29 words
The method of claim 9 wherein said etchant is essentially composed of NH 4 OH:H 2 O 2 :H 2 O, having a volume ratio from 1:1:1 to 10:1:1.
Claim 17
Dependent Claim
32 words
The method of claim 9, including cleaning said wafers four times with water for five minutes in a supersonic cleaning machine and dried by blowing with N 2 gas at room temperature.
Claim 18
Dependent Claim
27 words
The method of claim 9 wherein said etching treatment is used to remove arsenic deposited on said wafer and to remove soils attached on the wafer surfaces.
Claim 19
Dependent Claim
118 words
The method of claim 1, wherein said compound is selected from the group consisting of group III-V compounds and said etchant is selected from the group consisting of NaOH 25 g, H 2 O 2 100 cc, and H 2 O 2000 cc; H 2 SO 4 :H 2 O 2 :H 2 O, volume ratio from 1:1:1 to 10:1:1; HCl:H 2 O 2 :H 2 O, volume ratio from 1:1:1 to 10:1:1; Br 2 :methanol, volume ratio of Br 2 is from 0.5 to 10%; H 3 PO 4 :H 2 O 2 :H 2 O, volume ratio from 1:1:1 to 10:1:1; NH 4 OH;H 2 O 2 :H 2 O, volume ratio from 1:1:1 to 10:1:1.
Claim 20
Independent Claim
118 words
A method for producing Group III-V compound semiconductor single crystal substrates having a uniform cathodoluminescent image, comprising the steps of installing wafers of a grown compound semiconductor single crystal in an evacuated sealed quartz ampoule; subjecting the wafers to a first annealing at a temperature higher than 1100° C. and lower than the melting point of the single crystal for at least 30 minutes; cooling the wafers to room temperature at a cooling rate of from 1° to 30° C./min; etching both surfaces of the wafers; subjecting the wafers to a second annealing at temperatures from 750° C. to 1100° C. for at least 20 minutes in a non-oxidizing atmosphere; and cooling the wafers gradually to room temperature.
Claim 21
Independent Claim
118 words
A method for producing Group III-V compound semiconductor single crystal substrates having a uniform cathodoluminescent image, comprising the steps of installing wafers of a grown compound semiconductor single crystal in an evacuated sealed quartz ampoule; subjecting the wafers to a first annealing at a temperature higher than 1100° C. and lower than the melting point of the single crystal for at least 30 minutes; cooling the wafers to room temperature at a cooling rate of from 1° to 30° C./min; etching both surfaces of the wafers; subjecting the wafers to a second annealing at temperatures from 750° C. to 1100° C. for at least 20 minutes in a non-oxidizing atmosphere; and cooling the wafers gradually to room temperature.
References Cited (Backward Citations)
JPS5273673A
Cited
US4157497A
Cited
US4357180A
Cited
GB2137524A
Cited
US4636280A
Cited
US4713354A
Cited
US4752592A
Cited
US4889493A
Cited
US4851358A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-09 | 1995-03-11 | 1995-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-09 | 1999-03-11 | 1999-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-09 | 2003-03-11 | 2003-09-10 | $7700.00 | Window Closed / Lapsed |