US5045575A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of reducing voids in thermoset resin products
Assignee: Raytheon Co
•
Filing: 1989-12-18
•
Granted: 1991-09-03
•
Expires: 2009-12-18
Abstract
Abstract A method of improving the flowability and reducing voids in liquid synthetic thermosetting resins precursor compositions used to pot structures such as a honeycomb core or electronic parts and assemblies. Up to about 0.50 weight percent of a suitable titanate coupling agent is mixed with the liquid resin precursor, preferably in a vacuum or an inert atmosphere, any necessary hardener is added later to the premixed resin with the agent, then the resin is poured into a mold holding the structure to be potted. The titanate coupling agents have the general formula: ##STR1## where: R is an alkoxy, alkyl, alkenyl, alkynyl or aralkyl group having from 1 to about 30 carbon atoms or a substituted derivative thereof; M is zirconium or titanium; and R is independently an aryl, aralkyl, alkaryl, alkyl or alkeno group having from 1 to about 30 carbon atoms.
Inventors
- 👤 Solomon M. Gabayson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:49
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/0091; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
112 words
The method of preparing a resin mixture suitable for potting structures which when used is substantially free from voids and discoloration which comprise the steps of: providing a quantity of a liquid synthetic resin precursor; mixing therewith from about 0.1 to 0.5 weight percent, based on resin precursor weight of a titanate or zirconate coupling agent having the general formula: ##STR7## where: R is an alkoxy, alkyl, alkenyl, alkynyl or aralkyl L group having from 1 to about 30 carbon atoms or a substituted derivative thereof; M is zirconium or titanium; and R 1 is independently an aryl, aralkyl, alkaryl, alkyl or alkeno group having from 1 to about 30 carbon atoms.
Claim 2
Independent Claim
112 words
The method of preparing a resin mixture suitable for potting structures which when used is substantially free from voids and discoloration which comprise the steps of: providing a quantity of a liquid synthetic resin precursor; mixing therewith from about 0.1 to 0.5 weight percent, based on resin precursor weight of a titanate or zirconate coupling agent having the general formula: ##STR7## where: R is an alkoxy, alkyl, alkenyl, alkynyl or aralkyl L group having from 1 to about 30 carbon atoms or a substituted derivative thereof; M is zirconium or titanium; and R 1 is independently an aryl, aralkyl, alkaryl, alkyl or alkeno group having from 1 to about 30 carbon atoms.
Claim 3
Dependent Claim
22 words
The method according to claim 1 further including maintaining vacuum or an inert gas atmosphere over said resin precursor during said mixing.
Claim 4
Dependent Claim
46 words
The method according to claim 1 wherein said coupling agent is selected from the group consisting of tetra (2,2 diallyloxymethyl butyl di (ditridecyl) phosphito titanate, tetra (2,2 diallyloxymethyl) butyl di (ditridecyl) phosphito zirconate, tetraisopropyl di (dioctyl) phosphito titanate, tetraoctyl di (ditridecyl) phosphito titanate, and mixtures thereof.
Claim 5
Dependent Claim
19 words
The method according to claim 1 wherein said coupling agent is tetra (2,2 diallyloxymethyl) butyl di (ditridecyl) phosphito titanate.
Claim 6
Dependent Claim
13 words
The method according to claim 1 wherein said resin is an epoxy resin.
Claim 7
Dependent Claim
93 words
A resin mixture suitable for potting structures which comprises: a quantity of a liquid synthetic resin precursor; mixed therewith from about 0.1 to 0.5 weight percent, based on resin precursor weight, of a titanate or zirconate coupling agent having the general formula: ##STR8## where: R is an alkoxy, alkyl, alkenyl, alkynyl or aralkyl group having from 1 to about 30 carbon atoms or a substituted derivative thereof; M is zirconium or titanium; and R 1 is independently an aryl, aralkyl, alkaryl, alkyl or alkeno group having from 1 to about 30 carbon atoms.
Claim 8
Dependent Claim
93 words
A resin mixture suitable for potting structures which comprises: a quantity of a liquid synthetic resin precursor; mixed therewith from about 0.1 to 0.5 weight percent, based on resin precursor weight, of a titanate or zirconate coupling agent having the general formula: ##STR8## where: R is an alkoxy, alkyl, alkenyl, alkynyl or aralkyl group having from 1 to about 30 carbon atoms or a substituted derivative thereof; M is zirconium or titanium; and R 1 is independently an aryl, aralkyl, alkaryl, alkyl or alkeno group having from 1 to about 30 carbon atoms.
Claim 9
Dependent Claim
46 words
The mixture according to claim 6 wherein said coupling agent is selected from the group consisting of tetra (2,2 diallyloxymethyl butyl di (ditridecyl) phosphito titanate, tetra (2,2 diallyloxymethyl) butyl di (ditridecyl) phosphito zirconate, tetraisopropyl di (dioctyl) phosphito titanate, tetraoctyl di (ditridecyl) phosphito titanate, and mixtures thereof.
Claim 10
Dependent Claim
19 words
The mixture according to claim 6 wherein said coupling agent is tetra (2,2 diallyloxymethyl) butyl di (ditridecyl) phosphito titanate.
Claim 11
Dependent Claim
13 words
The mixture according to claim 6 wherein said resin is an epoxy resin.
Claim 12
Independent Claim
122 words
The method of potting a structure in a resin which is substantially free from voids and discoloration, which comprises the steps of: providing a quantity of a liquid synthetic resin precursor; mixing therewith from about 0.1 to 0.5 weight percent, based on resin precursor weight, of a titanate or zirconate coupling agent having the general formula: ##STR9## where: R is an alkoxy, alkyl, alkenyl, alkynyl or aralkyl group having from 1 to about 30 carbon atoms or a substituted derivative thereof; M is zirconium or titanium; R 1 is independently an aryl, aralkyl, alkaryl, alkyl or alkeno group having from 1 to about 30 carbon atoms; surrounding a structure to be potted with said resin precursor or mixture; and curing said resin.
Claim 13
Independent Claim
122 words
The method of potting a structure in a resin which is substantially free from voids and discoloration, which comprises the steps of: providing a quantity of a liquid synthetic resin precursor; mixing therewith from about 0.1 to 0.5 weight percent, based on resin precursor weight, of a titanate or zirconate coupling agent having the general formula: ##STR9## where: R is an alkoxy, alkyl, alkenyl, alkynyl or aralkyl group having from 1 to about 30 carbon atoms or a substituted derivative thereof; M is zirconium or titanium; R 1 is independently an aryl, aralkyl, alkaryl, alkyl or alkeno group having from 1 to about 30 carbon atoms; surrounding a structure to be potted with said resin precursor or mixture; and curing said resin.
Claim 14
Dependent Claim
25 words
The method according to claim 10 further including maintaining vacuum or an inert gas atmosphere over said resin precursor during said mixing and surrounding steps.
Claim 15
Dependent Claim
46 words
The method according to claim 10 wherein said coupling agent is selected from the group consisting of tetra (2,2 diallyloxymethyl butyl di (ditridecyl) phosphito titanate, tetra (2,2 diallyloxymethyl) butyl di (ditridecyl) phosphito zirconate, tetraisopropyl di (dioctyl) phosphito titanate, tetraoctyl di (ditridecyl) phosphito titanate, and mixtures thereof.
Claim 16
Dependent Claim
19 words
The method according to claim 10 wherein said coupling agent is tetra 2,2 diallyloxymethyl) butyl di (ditridecyl) phosphito titanate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-02 | 1995-03-04 | 1995-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-02 | 1999-03-04 | 1999-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-02 | 2003-03-04 | 2003-09-03 | $7700.00 | Window Closed / Lapsed |