Carbon-coated reinforcing fibers and composite ceramics made therefrom
Assignee: Corning Inc
•
Filing: 1989-02-23
•
Granted: 1991-08-13
•
Expires: 2009-02-23
Abstract
Abstract Fiber-reinforced ceramic matrix composite products are made by providing inorganic fiber reinforcement materials with pyrolytic carbon coatings, combining the carbon-coated fibers with a selected ceramic matrix material to make a composite preform, and consolidating the preform with heat and pressure to form the fiber-reinforced composite. Preferably, the peak consolidation temperature of the composite is moderated, with the retained pyrolytic carbon coating acting to preserve tough fracture behavior in the composite product notwithstanding the absence of the conventional graphitic fiber interface layer therefrom.
Inventors
- 👤 John L. Stempin
- 👤 Dale R. Wexell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 03:03
CPC Classifications
C; C03; C03C; C03C14/00; C03C14/002; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18; C04B35/622; C04B35/626; C04B35/628; C04B35/62844; C04B35/62857; C04B35/62873; C04B35/62886; C04B35/62897; C04B35/64; C04B35/645; C04B35/6455; C04B35/71; C04B35/78; C04B35/80; C03C2214/00; C03C2214/02; C03C2214/03; C03C2214/20; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/36; C04B2235/48; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/522; C04B2235/5228; C04B2235/524; C04B2235/5244; C04B2235/5264; C04B2235/70; C04B2235/96
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
110 words
A method for making a fiber-reinforced ceramic matrix composite article which comprises the steps of: selecting an inorganic fiber reinforcement material; providing a pyrolytic carbon coating on the surfaces of the inorganic fiber reinforcement material to produce a carbon-coated fiber material; combining the carbon-coated fiber material with a selected powdered glass or glass-ceramic matrix material to provide a preform for the fiber-reinforced composite article; and consolidating the preform to form the fiber-reinforced composite under a combination of heat and pressure at a temperature not exceeding about 1300° C., the combination being effective to achieve full densification of the powdered glass or glass-ceramic but insufficient to destroy the pyrolytic carbon coating.
Claim 2
Independent Claim
110 words
A method for making a fiber-reinforced ceramic matrix composite article which comprises the steps of: selecting an inorganic fiber reinforcement material; providing a pyrolytic carbon coating on the surfaces of the inorganic fiber reinforcement material to produce a carbon-coated fiber material; combining the carbon-coated fiber material with a selected powdered glass or glass-ceramic matrix material to provide a preform for the fiber-reinforced composite article; and consolidating the preform to form the fiber-reinforced composite under a combination of heat and pressure at a temperature not exceeding about 1300° C., the combination being effective to achieve full densification of the powdered glass or glass-ceramic but insufficient to destroy the pyrolytic carbon coating.
Claim 3
Dependent Claim
75 words
A method in accordance with claim 1 wherein the step of applying a pyrolytic carbon coating to the surfaces of the inorganic fiber reinforcement material comprises the steps of: applying to the surfaces of the fibers a liquid coating comprising an organic compound convertible on heating to pyrolytic carbon; and heating the fibers and organic compound under non-oxidizing conditions at a temperature and for a time sufficient to convert the organic compound to pyrolytic carbon.
Claim 4
Independent Claim
76 words
A method for treating an inorganic fiber reinforcement material comprising silicon carbide fibers to improve the pull-out characteristics thereof from a ceramic matrix material which comprises the steps of: applying to the surfaces of the fibers a liquid coating comprising an organic compound convertible on heating to pyrolytic carbon; and heating the fibers and organic compound under non-oxidizing conditions and at a temperature and for a time sufficient to convert the organic compound to pyrolytic carbon.
Claim 5
Independent Claim
76 words
A method for treating an inorganic fiber reinforcement material comprising silicon carbide fibers to improve the pull-out characteristics thereof from a ceramic matrix material which comprises the steps of: applying to the surfaces of the fibers a liquid coating comprising an organic compound convertible on heating to pyrolytic carbon; and heating the fibers and organic compound under non-oxidizing conditions and at a temperature and for a time sufficient to convert the organic compound to pyrolytic carbon.
Claim 6
Dependent Claim
102 words
In the method for making a ceramic matrix composite article wherein an inorganic fiber reinforcement material is combined with a ceramic matrix material or a precursor therefor and the combination of fiber reinforcement material and matrix material is consolidated with heat and pressure to provide a fiber-reinforced ceramic matrix composite, the improvement characterized in that: prior to combining the inorganic fiber reinforcement material with the ceramic matrix material or a precursor therefor the fiber reinforcement material is provided with a pyrolytic carbon coating; and the combination of fiber reinforcement material and matrix material is consolidated at a temperature not exceeding 1300° C.
Claim 7
Dependent Claim
102 words
In the method for making a ceramic matrix composite article wherein an inorganic fiber reinforcement material is combined with a ceramic matrix material or a precursor therefor and the combination of fiber reinforcement material and matrix material is consolidated with heat and pressure to provide a fiber-reinforced ceramic matrix composite, the improvement characterized in that: prior to combining the inorganic fiber reinforcement material with the ceramic matrix material or a precursor therefor the fiber reinforcement material is provided with a pyrolytic carbon coating; and the combination of fiber reinforcement material and matrix material is consolidated at a temperature not exceeding 1300° C.
Claim 8
Dependent Claim
52 words
A ceramic matrix composite article comprising a matrix selected from the group consisting of aluminosilicate glass-ceramics and aluminosilicate glasses and reinforcing fibers selected from the group consisting of silicon carbide fibers and oxide fibers, wherein the reinforcing fibers comprise a surface coating and wherein the surface coating comprises a pyrolytic carbon layer.
Claim 9
Dependent Claim
52 words
A ceramic matrix composite article comprising a matrix selected from the group consisting of aluminosilicate glass-ceramics and aluminosilicate glasses and reinforcing fibers selected from the group consisting of silicon carbide fibers and oxide fibers, wherein the reinforcing fibers comprise a surface coating and wherein the surface coating comprises a pyrolytic carbon layer.
Claim 10
Dependent Claim
28 words
A ceramic matrix composite article in accordance with claim 5 wherein the fibers are silicon carbide fibers, and wherein the surface coating is substantially free of graphitic carbon.
Claim 11
Dependent Claim
19 words
A ceramic matrix composite article in accordance with claim 5 wherein the surface coating consists essentially of pyrolytic carbon.
References Cited (Backward Citations)
US3790393A
Cited
US3949106A
Cited
US4178413A
Cited
US4397901A
Cited
US4376803A
Cited
US4376804A
Cited
US4464475A
Cited
US4589900A
Cited
US4748079A
Cited
US4752503A
Cited
US4722860A
Cited
US4615987A
Cited
US4626515A
Cited
US4735850A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-12 | 1995-02-11 | 1995-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-12 | 1999-02-11 | 1999-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-12 | 2003-02-11 | 2003-08-13 | $7700.00 | Window Closed / Lapsed |