Electrodeposited eutectic tin-bismuth alloy on a conductive substrate
Assignee: AUTOTECH DEUTSCHLAND GmbH
•
Filing: 1990-04-12
•
Granted: 1991-08-13
•
Expires: 2010-04-12
Abstract
Abstract An electroplating bath, cell and method for the electrodeposition of a wide range of tin-bismuth alloys onto a conductive substrate comprises tin and bismuth ion in aqueous solution, and an alkyl sulfonic or polysulfonic acid or salt as the electrolyte. The sulfonic component is present in amounts sufficient to maintain the bismuth in solution. In the operation of the method of the invention, electroplated tin-bismuth eutectic alloys of controlled composition are obtained. The alloys of tin and bismuth contain amounts of both metals such that the plated alloy has a melting point substantially lower than that of either metal alone, and a melting point lower than that of a tin-lead alloy.
Inventors
- 👤 Harold P. Wilson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:25
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/26; B23K35/264; B23K35/262; C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/60; H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3473; H05K3/346; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12556; Y10T428/12569; Y10T428/12681; Y10T428/12708
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
135 words
An article of manufacture comprising at least one PWB with at least one conductive surface, having a tin-bismuth alloy deposited on at least a portion of the surface, the alloy being deposited from an electroplating bath comprising bismuth and tin ion in aqueous solution, wherein the bismuth and the tin ion are present in the bath in amounts sufficient to deposit the tin-bismuth alloy onto the conductive surface of the PWB in a weight ratio relative to each other selected to provide a controlled bismuth content of the tin-bismuth alloy on the conductive surface of the PWB in an amount of greater than about 10 wt. % bismuth, the bath having an electrolyte comprising at least one alkyl sulfonic acid or salt thereof in an amount sufficient to inhibit hydrolytic precipitation of the bismuth ion.
Claim 2
Dependent Claim
135 words
An article of manufacture comprising at least one PWB with at least one conductive surface, having a tin-bismuth alloy deposited on at least a portion of the surface, the alloy being deposited from an electroplating bath comprising bismuth and tin ion in aqueous solution, wherein the bismuth and the tin ion are present in the bath in amounts sufficient to deposit the tin-bismuth alloy onto the conductive surface of the PWB in a weight ratio relative to each other selected to provide a controlled bismuth content of the tin-bismuth alloy on the conductive surface of the PWB in an amount of greater than about 10 wt. % bismuth, the bath having an electrolyte comprising at least one alkyl sulfonic acid or salt thereof in an amount sufficient to inhibit hydrolytic precipitation of the bismuth ion.
Claim 3
Dependent Claim
16 words
The article of claim 1 wherein the bismuth content is greater than about 20 wt. %.
Claim 4
Dependent Claim
18 words
The article of claim 1 wherein the bismuth content is between about 20 and about 80 wt. %.
Claim 5
Dependent Claim
12 words
The article of claim 1 wherein the alloy comprises the tin-bismuth eutectic.
Claim 6
Dependent Claim
10 words
The article of claim 1 comprising a plurality of PWBs.
Claim 7
Dependent Claim
16 words
The article of claim 1 wherein the tin-bismuth alloy is deposited on a plurality of surfaces.
Claim 8
Dependent Claim
37 words
An article comprising a PWB and an electrodeposited eutectic tin-bismuth alloy thereon, the alloy having a melting point of about 138° C. and an alloy composition of about 42 wt. % tin and 58 wt. % bismuth.
Claim 9
Dependent Claim
37 words
An article comprising a PWB and an electrodeposited eutectic tin-bismuth alloy thereon, the alloy having a melting point of about 138° C. and an alloy composition of about 42 wt. % tin and 58 wt. % bismuth.
Claim 10
Dependent Claim
14 words
An article according to claim 7 in which the PWB has metallic conductors thereon.
References Cited (Backward Citations)
SU305208A1
Cited
US3198877A
Cited
US3360446A
Cited
US3663384A
Cited
SU467145A1
Cited
SU463747A1
Cited
JPS53123327A
Cited
SU697610A1
Cited
US4252618A
Cited
US4331518A
Cited
US4565610A
Cited
US4717460A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-12 | 1995-02-11 | 1995-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-12 | 1999-02-11 | 1999-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-12 | 2003-02-11 | 2003-08-13 | $7700.00 | Window Closed / Lapsed |