Method of producing a thin silicon on insulator layer by wafer bonding and chemical thinning
Assignee: Lockheed Martin Energy Systems Inc
•
Filing: 1990-05-07
•
Granted: 1991-06-18
•
Expires: 2010-05-07
Abstract
Abstract A method for forming a thin crystal layer of silicon on top of a insulating layer that is supported by a silicon wafer used for electronic device applications. Carbon ions are implanted in a silicon wafer in order to form an etch stop. Said wafer is bonded to a supporting wafer that has an insulating surface layer of silicon oxide or silicon nitride. The silicon substrate of the implanted wafer is removed using an alkaline etching solution or grinding and alkaline etching. The remaining carbon implanted layer forms the thin silicon layer.
Inventors
- 👤 Ulrich M. Goesele
- 👤 Volker E. Lehmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:24
CPC Classifications
H; H10; H10P; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10P90/1914; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10P30/21; H10P30/28; H10P50/00; H10P50/60; H10P50/64; H10P50/642; H10P50/644; H10P52/00; H10P52/40; H10P52/402; Y; Y10; Y10S; Y10S438/00; Y10S438/97
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
109 words
A method of forming a thin silicon layer upon which semiconductor devices can subsequently be formed, comprising the steps of: implanting carbon ions into a silicon substrate, to form an implanted layer; bonding said silicon substrate to a mechanical support, to form a bonded wafer pair, such that the said implanted layer is adjacent said mechanical support; annealing of said bonded wafer pair at such low temperatures that carbon remains in solid solution in silicon and no buried layer of silicon carbide is formed; removing said silicon substrate without removing the implanted layer; whereby said underlaying implanted layer remain on said mechanical support to form the thin silicon layer.
Claim 2
Independent Claim
109 words
A method of forming a thin silicon layer upon which semiconductor devices can subsequently be formed, comprising the steps of: implanting carbon ions into a silicon substrate, to form an implanted layer; bonding said silicon substrate to a mechanical support, to form a bonded wafer pair, such that the said implanted layer is adjacent said mechanical support; annealing of said bonded wafer pair at such low temperatures that carbon remains in solid solution in silicon and no buried layer of silicon carbide is formed; removing said silicon substrate without removing the implanted layer; whereby said underlaying implanted layer remain on said mechanical support to form the thin silicon layer.
Claim 3
Dependent Claim
22 words
The method as recited in claim 1, wherein said step of bonding said silicon substrate is carried out in a micro-cleanroom set-up.
Claim 4
Dependent Claim
23 words
The method as recited in claim 1, wherein said silicon substrate and said mechanical support are annealed at approximately 850° C. after bonding.
Claim 5
Dependent Claim
21 words
The method as recited in claim 1, wherein said mechanical support is made of silicon and is oxidized prior to bonding.
Claim 6
Dependent Claim
46 words
The method as recited in claim 1, wherein said step of removing the silicon substrate comprises the steps of: mechanically removing a portion of said silicon substrate; etching the remaining part of said silicon substrate with an etchant that does not appreciably attack said implanted layer.
Claim 7
Dependent Claim
24 words
The method as recited in claim 5, wherein said etchant comprises a solution selected from the group consisting of ethylene-diamine-pyrocatecol, ethelene-piperidine-pyrocatechol, and potassium hydroxide.
Claim 8
Dependent Claim
34 words
The method as recited in claim 1, wherein said carbon ions are implanted at doses and energies that will produce a maximum carbon concentration of about 1.5×10 21 /cm 3 in said silicon substrate.
Claim 9
Dependent Claim
28 words
The method as recited in claim 1, wherein said thin silicon layer layer is subsequently annealed at a temperature in the range of 900° C. to 1300° C.
Claim 10
Independent Claim
128 words
A method of forming a thin silicon layer upon which semiconductor devices can subsequently be formed, comprising the steps of: implanting carbon ions into a silicon substrate, to form an implanted layer; growing of an epitaxial silicon layer on said silicon substrate; bonding said silicon substrate to a mechanical support, to form a bonded wafer pair, such that the said epitaxial layer is adjacent said mechanical support; annealing of the bonded wafers at such low temperatures that carbon remains in solid solution in silicon and no buried layer of silicon carbide is formed; removing said silicon substrate without removing the implanted layer; removing said carbon implanted layer without removing the epitaxial layer; whereby said underlaying epitaxial layer remains on said mechanical support to form a thin silicon layer.
Claim 11
Independent Claim
128 words
A method of forming a thin silicon layer upon which semiconductor devices can subsequently be formed, comprising the steps of: implanting carbon ions into a silicon substrate, to form an implanted layer; growing of an epitaxial silicon layer on said silicon substrate; bonding said silicon substrate to a mechanical support, to form a bonded wafer pair, such that the said epitaxial layer is adjacent said mechanical support; annealing of the bonded wafers at such low temperatures that carbon remains in solid solution in silicon and no buried layer of silicon carbide is formed; removing said silicon substrate without removing the implanted layer; removing said carbon implanted layer without removing the epitaxial layer; whereby said underlaying epitaxial layer remains on said mechanical support to form a thin silicon layer.
Claim 12
Dependent Claim
22 words
The method as recited in claim 9, wherein said step of bonding said silicon substrate is carried out in a micro-cleanroom set-up.
Claim 13
Dependent Claim
23 words
The method as recited in claim 9, wherein said silicon substrate and said mechanical support are annealed at approximately 850° C. after bonding.
Claim 14
Dependent Claim
21 words
The method as recited in claim 9, wherein said mechanical support is made of silicon and is oxidized prior to bonding.
Claim 15
Dependent Claim
46 words
The method as recited in claim 9, wherein said step of removing the silicon substrate comprises the steps of: mechanically removing a portion of said silicon substrate; etching the remaining part of said silicon substrate with an etchant that does not appreciably attack said implanted layer.
Claim 16
Dependent Claim
24 words
The method as recited in claim 13, wherein said etchant comprises a solution selected from the group consisting of ethelene-diamine-pyrocatecol, ethelene-piperidine-pyrocatechol, and potassium hydroxide.
Claim 17
Dependent Claim
34 words
The method as recited in claim 9, wherein said carbon ions are implanted at doses and energies that will produce a maximum carbon concentration of about 1.5×10 21 /cm 3 in said silicon substrate.
Claim 18
Dependent Claim
26 words
The method as recited in claim 9, wherein said carbon implanted layer is removed by an etchant consisting of hydrofluoric acid, nitric acid and acetic acid.
Claim 19
Dependent Claim
38 words
The method as recited in claim 9, wherein said carbon implanted layer is removed by oxidizing the carbon implanted layer at a temperature in the range of 900° C. to 1300° C. and subsequent etching in hydrofluoric acid.
References Cited (Backward Citations)
US3721593A
Cited
US4601779A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-17 | 1994-12-17 | 1995-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-17 | 1998-12-17 | 1999-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-17 | 2002-12-17 | 2003-06-18 | $7700.00 | Window Closed / Lapsed |