US5023398A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Aluminum alloy semiconductor packages
Assignee: Advanced Technology Interconnect Inc
•
Filing: 1990-04-04
•
Granted: 1991-06-11
•
Expires: 2010-04-04
Abstract
Abstract The present invention relates to a package adapted to house an electronic device, such as a semiconductor integrated circuit. The package components are comprised of aluminum based alloy. At least a portion of the surfaces of the package components are anodized to enhance corrosion resistance and increase bond strength. The aluminum based packages are characterized by lighter weight than copper based packages and better thermal conductivity than plastic based packages.
Inventors
- 👤 Deepak Mahulikar
- 👤 James M. Popplewell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 04:28
CPC Classifications
H; H10; H10W; H10W76/00; H10W76/10; H10W76/12; H10W76/15; H10W76/157; H10W70/00; H10W70/60; H10W70/67; H10W70/68; H10W70/6875; H10W76/17; H10W76/60; H10W70/682; H10W72/00; H10W72/851; H10W72/874; H10W72/884; H10W90/00; H10W90/701; H10W90/731; H10W90/734; H10W90/751; H10W90/756
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
171 words
A package for encasing an electronic device, comprising: a base component formed from aluminum or an aluminum alloy; a window frame component formed from aluminum or an aluminum alloy and having first and second surfaces; said base component and said window frame component defining a cavity; a leadframe disposed between and adapted to be bonded to said base component and to the first surface of said window frame component, said leadframe bonded to said base component and to said first surface of said window frame component by a sealing glass having a coefficient of thermal expansion within about 20% of the coefficient of thermal expansion of said base component; a cover component adapted to be bonded to the second surface of said window frame component; and an anodization layer having a thickness in the range of from about 10 to about 2000 micro inches and covering at least those portions of said base and window frame components exposed to the atmosphere, as well as those portions bonded to said sealing glass.
Claim 2
Dependent Claim
171 words
A package for encasing an electronic device, comprising: a base component formed from aluminum or an aluminum alloy; a window frame component formed from aluminum or an aluminum alloy and having first and second surfaces; said base component and said window frame component defining a cavity; a leadframe disposed between and adapted to be bonded to said base component and to the first surface of said window frame component, said leadframe bonded to said base component and to said first surface of said window frame component by a sealing glass having a coefficient of thermal expansion within about 20% of the coefficient of thermal expansion of said base component; a cover component adapted to be bonded to the second surface of said window frame component; and an anodization layer having a thickness in the range of from about 10 to about 2000 micro inches and covering at least those portions of said base and window frame components exposed to the atmosphere, as well as those portions bonded to said sealing glass.
Claim 3
Dependent Claim
100 words
The package of claim 1 wherein said sealing glass consists essentially of at least 40 molar percent SiO 2 , from about 5 to about 25% BaO, from about 15 to about 45% of an alkaline oxide component comprising at least two oxides selected from the group consisting of Li 2 O, K 2 O, Rb 2 O 3 and Cs 2 O 3 , from about 0.1 to 5% of a nucleating agent, up to about 15% ZnO, up to about 10% PbO, up to about 5% Al 2 O 3 and up to about 10% of an additive.
Claim 4
Dependent Claim
58 words
The package of claim 1 wherein said glass has the composition by weight of 32-50% SiO 2 , 4%-27% Na 2 O, 4%-27% K 2 O, up to 5% Li 2 O, 2%-8% BaO, 2%-8% SrO, 4%-30% TiO 2 , up to 7% ZnO, up to 2% ZrO 2 and up to 2% Al 2 O 3 .
Claim 5
Dependent Claim
15 words
A package of claim 3 wherein the SiO 2 concentration is less than about 45%.
Claim 6
Dependent Claim
30 words
The package of claim 1 wherein said cover component is formed from aluminum or an aluminum alloy having an anodization layer covering at least those portions exposed to the atmosphere.
Claim 7
Dependent Claim
21 words
The package of claim 5 wherein the thickness of said anodization layer is from about 1000 to about 2000 micro inches.
Claim 8
Dependent Claim
24 words
The package of claim 5 wherein substantially the entire surface of the base component and the cover component are covered with an anodization layer.
Claim 9
Dependent Claim
40 words
The package of claim 5 wherein substantially the entire surface of the base component and of the cover component, except for the surface of said base component to be bonded to said electronic device is covered with an anodization layer.
Claim 10
Dependent Claim
37 words
The package of claim 5 wherein substantially the entire surface of the base component and of the cover component except for the surface of said cover component enclosed within said cavity is covered with an anodization layer.
Claim 11
Dependent Claim
30 words
The package of claim 1 wherein said sealing glass has a coefficient of thermal expansion within about 10% of the coefficient of thermal expansion of said anodized aluminum based component.
Claim 12
Dependent Claim
34 words
The package of claim 10 wherein the composition of said sealing glass is about 40 molar percent Na 2 O, 10% BaO, 1% Al 2 O 3 and 49% P 2 O 5 .
Claim 13
Dependent Claim
113 words
The package of claim 1 wherein said sealing glass is a composite comprising a first component consisting essentially of a glass matrix selected from the group consisting lead borate, lead-zinc borate, lead-borate silicate and lead-zinc borate silicate glasses, said vitreous glass matrix having a coefficient of thermal expansion in excess of about 80×10 -7 in/in/°C. (from ambient to glass transition temperature) and a second component mixed into said first component to increase the effective coefficient of thermal expansion of the resulting glass composite to be close to that of said aluminum substrate, said second component consisting essentially of an effective amount up to about 30 weight percent of calcium fluoride and barium fluoride.
Claim 14
Dependent Claim
111 words
The package of claim 1 wherein said sealing glass is comprised of a homogenious mixture of Oxides consisting essentially of at least 50 molar percent SiO 2 , from about 12 to 15% BaO, from about 20 to 30% of an alkaline oxide component comprised of at least two alkaline oxides selected from the group consisting of Na 2 O, K 2 O, and Li 2 O, from about 0.5 to about 5% Al 2 O 3 and up to about 10% of an additive selected from the group consisting of B 2 O 3 , P 2 O 5 , MgO, CaO, GeO 2 , SrO, PbO and mixtures thereof.
References Cited (Backward Citations)
GB817636A
Cited
US3871018A
Cited
US4105861A
Cited
US4202700A
Cited
US4410927A
Cited
US4461924A
Cited
US4594770A
Cited
US4480262A
Cited
US4656499A
Cited
US4521469A
Cited
US4525422A
Cited
US4582556A
Cited
US4524238A
Cited
US4498121A
Cited
US4707724A
Cited
US4542259A
Cited
US4775647A
Cited
US4711826A
Cited
US4769345A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-10 | 1994-12-10 | 1995-06-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-10 | 1998-12-10 | 1999-06-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-10 | 2002-12-10 | 2003-06-11 | $7700.00 | Window Closed / Lapsed |