Method of making high strength articles from forged powder steel alloys
Assignee: BOARD OF CONTROL OF MICHIGAN TECHNOLOGICAL UNIVERSITY A BODY CORPORATE OF MI
•
Filing: 1990-06-08
•
Granted: 1991-04-23
•
Expires: 2010-06-08
Abstract
Abstract High strength steel parts or articles are made from a powder alloy by compacting the powder into a preform, sintering the preform in a sintering furnace or the like under a highly-reducing atmosphere and at a temperature of at least 1150 DEG C., cooling the preform, preheating the sintered preform in a highly-reducing atmosphere, such as an inert gas-based atmosphere containing hydrogen or pure hydrogen, to a temperature of at least 1000 DEG C. and transferring the preheated preform to an impact forging device and impacting the preform at a peak averaging forging pressure of at least about 1000 MPa to obtain a forged part or article. The time period between removal of the preheated preform from the preheater and the first forging impact is no more than about 8 seconds. The sintering and preheating steps can be combined with the sintered preform being cooled to the preheating temperature in the sintering furnace and transferred directly from the sintering furnace to the impact forging device.
Inventors
- 👤 Alfred A. Hendrickson
- 👤 Darrell W. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:41
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0264; B; B22; B22F; B22F3/00; B22F3/17; B22F2998/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
150 words
A method for producing a high strength article from forged powder steel alloys comprising the steps of: (a) compacting said powder into a coherent preform; (b) heating said preform in a sintering means in a substantially dry, highly-reducing atmosphere and at a temperature of at least 1150° C. to sinter said preform and allowing said sintered preform to cool; (c) preheating said sintered preform in a preheating means in the presence of a substantially dry, highly reducing atmosphere to a preheating temperature of at least 1000° C.; and (d) transferring said preheated, sintered preform from the preheating means to an impact forging device and impacting said preform therein at a peak average forging pressure of at least about 1000 MPa to obtain a forged article, the time period between removing said preheated, sintered preform from the preheating means and the first forging impact being no more than about 8 seconds.
Claim 2
Independent Claim
150 words
A method for producing a high strength article from forged powder steel alloys comprising the steps of: (a) compacting said powder into a coherent preform; (b) heating said preform in a sintering means in a substantially dry, highly-reducing atmosphere and at a temperature of at least 1150° C. to sinter said preform and allowing said sintered preform to cool; (c) preheating said sintered preform in a preheating means in the presence of a substantially dry, highly reducing atmosphere to a preheating temperature of at least 1000° C.; and (d) transferring said preheated, sintered preform from the preheating means to an impact forging device and impacting said preform therein at a peak average forging pressure of at least about 1000 MPa to obtain a forged article, the time period between removing said preheated, sintered preform from the preheating means and the first forging impact being no more than about 8 seconds.
Claim 3
Dependent Claim
20 words
A method according to claim 1 wherein said sintering temperature in step (b) is about 1250° to about 1400° C.
Claim 4
Dependent Claim
22 words
A method according to claim 1 wherein the atmosphere in step (c) is an inert gas-based atmosphere containing hydrogen or pure hydrogen.
Claim 5
Dependent Claim
20 words
A method according to claim 1 wherein said preheating temperature in step (c) is about 1100° to about 1200° C.
Claim 6
Dependent Claim
42 words
A method according to claim 1 wherein steps (b) and (c) are combined and said sintered preform is allowed to cool in the sintering means to said preheating temperature and then transferred directly from the sintering means to the impact forging device.
Claim 7
Dependent Claim
19 words
A method according to claim 1 wherein said peak average forging pressure is about 1000 to about 2000 MPa.
Claim 8
Dependent Claim
25 words
A method according to claim 1 wherein said preform is compressed to a density up to about 90% of the theoretical density in step (a).
Claim 9
Dependent Claim
29 words
A method according to claim 1 wherein the article has a hardness of about 50 to about 60 HRC and a tensile strength of about 1700 to 1900 MPa.
Claim 10
Dependent Claim
22 words
A method according to claim 1 where the density of the forged article is at least about 99.5% of the theoretical density.
Claim 11
Independent Claim
160 words
A method for producing high strength articles from forged powder steel alloys comprising the steps of: (a) compacting said powder into a coherent preform; (b) heating said preform in a sintering means in a substantially dry, highly-reducing atmosphere and at a temperature of about 1250° to about 1400° C. to sinter said preform and allowing said sintered preform to cool; (c) preheating said sintered preform in a preheating means in the presence of an inert gas based atmosphere containing hydrogen or substantially pure hydrogen to a preheating temperature of at least about 1000° C.; and (d) transferring said preheated, sintered preform from the preheating means to an impact forging device and impacting said preform therein at a peak average forging pressure of at least about 1000 to about 2000 MPa to obtain a forged article, the time period between removing said preheated, sintered preform from the preheating means and the first forging impact being no more than about 8 seconds.
Claim 12
Independent Claim
160 words
A method for producing high strength articles from forged powder steel alloys comprising the steps of: (a) compacting said powder into a coherent preform; (b) heating said preform in a sintering means in a substantially dry, highly-reducing atmosphere and at a temperature of about 1250° to about 1400° C. to sinter said preform and allowing said sintered preform to cool; (c) preheating said sintered preform in a preheating means in the presence of an inert gas based atmosphere containing hydrogen or substantially pure hydrogen to a preheating temperature of at least about 1000° C.; and (d) transferring said preheated, sintered preform from the preheating means to an impact forging device and impacting said preform therein at a peak average forging pressure of at least about 1000 to about 2000 MPa to obtain a forged article, the time period between removing said preheated, sintered preform from the preheating means and the first forging impact being no more than about 8 seconds.
Claim 13
Dependent Claim
20 words
A method according to claim 10 wherein said preheating temperature in step (c) is about 1100° to about 1200° C.
Claim 14
Dependent Claim
42 words
A method according to claim 10 wherein steps (b) and (c) are combined and said sintered preform is allowed to cool in the sintering means to said preheating temperature and is transferred directly from the sintering means to the impact forging device.
Claim 15
Dependent Claim
25 words
A method according to claim 10 wherein said preform is compressed to a density up to about 90% of the theoretical density in step (a).
Claim 16
Dependent Claim
29 words
A method according to claim 10 wherein the article has a hardness of about 50 to about 60 HRC and a tensile strength of about 1700 to 1900 MPa.
Claim 17
Dependent Claim
22 words
A method according to claim 14 wherein the density of the forged article is at least about 99.5% of the theoretical density.
References Cited (Backward Citations)
US3837068A
Cited
US4002471A
Cited
US3992763A
Cited
US4165243A
Cited
US4756677A
Cited
US4587096A
Cited
US4693864A
Cited
US4879091A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-22 | 1994-10-22 | 1995-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-22 | 1998-10-22 | 1999-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-22 | 2002-10-22 | 2003-04-23 | $7700.00 | Window Closed / Lapsed |