Assignee: National Aeronautics and Space Administration
•
Filing: 1989-05-04
•
Granted: 1991-04-16
•
Expires: 2009-05-04
Abstract
Abstract A method for etching or removing polymers, photoresists, and organic contaminants from a substrate is disclosed. The method includes creating a more reactive gas species by producing a plasma discharge in a reactive gas such as oxygen and contacting the resulting gas species with a sacrificial solid organic material (13A) such as polyethylene or poly(vinyl fluoride), producing a highly reactive gas species, which in turn etches the starting polymer, organic contaminant, or photoresist (13). The sample to be etched is located away from the plasma glow discharge region (11) so as to avoid damaging the substrate by exposure to high-energy particles and electric fields encountered in that region. Greatly increased etching rates are obtained. This method is highly effective for etching polymers such as polyimides and photoresists that are otherwise difficult or slow to etch downstream from an electric discharge in a reactive gas.
Inventors
- 👤 Narcinda R. Lerner
- 👤 Theodore J. Wydeven, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 00:12
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
196 words
A method for etching a sample which is a polymer or photoresist deposited on a semiconductor substrate thereof to remove said polymer or photoresist without damaging said substrate, which method comprises the steps of: (a) locating said sample in the etching region of a plasma reactor having both a plasma region and a separate etching region spaced apart from said plasma region; (b) locating in the etching region of said reactor a sacrificial organic solid material that has a substantially higher reactivity with the plasma-energized reactive gas generated in said plasma region than the polymer or photoresist being etched from said sample; (c) producing a plasma in a reactive gas in said plasma region at a reactor pressure of from 0.1 to 10.0 Torr whereby said plasma-energized gas is formed; (d) contacting said plasma-energized gas with said sacrificial organic solid material whereby a highly reactive gas is formed said highly reactive gas having a substantially higher reaction rate with said polymer or photoresist than said plasma-energized gas; and (e) contacting the sample with the resulting highly reactive gas at a sufficient concentration and for a sufficient time to etch said polymer or photoresist of said sample.
Claim 2
Independent Claim
196 words
A method for etching a sample which is a polymer or photoresist deposited on a semiconductor substrate thereof to remove said polymer or photoresist without damaging said substrate, which method comprises the steps of: (a) locating said sample in the etching region of a plasma reactor having both a plasma region and a separate etching region spaced apart from said plasma region; (b) locating in the etching region of said reactor a sacrificial organic solid material that has a substantially higher reactivity with the plasma-energized reactive gas generated in said plasma region than the polymer or photoresist being etched from said sample; (c) producing a plasma in a reactive gas in said plasma region at a reactor pressure of from 0.1 to 10.0 Torr whereby said plasma-energized gas is formed; (d) contacting said plasma-energized gas with said sacrificial organic solid material whereby a highly reactive gas is formed said highly reactive gas having a substantially higher reaction rate with said polymer or photoresist than said plasma-energized gas; and (e) contacting the sample with the resulting highly reactive gas at a sufficient concentration and for a sufficient time to etch said polymer or photoresist of said sample.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein said etching region is spaced apart from said plasma region a distance of 5 to 50 cm.
Claim 4
Dependent Claim
32 words
The method of claim 2 wherein the reactive gas in said plasma region is selected from oxygen, fluorine, chlorine, nitrogen, nitrous oxide, nitric oxide, nitrogen dioxide, hydrogen, water vapor, or mixtures thereof.
Claim 5
Dependent Claim
15 words
The method of claim 3 wherein said reactive gas in said plasma region comprises oxygen.
Claim 6
Dependent Claim
15 words
The method of claim 3 wherein said sacrificial organic solid material comprises an organic polymer.
Claim 7
Dependent Claim
31 words
The method of claim 5 wherein polymer is the sacrificial selected from poly(vinyl fluoride), polyethylene, polypropylene, cis-polybutadiene, trans 1, 4-polybutadiene, polyacrylonitrile, poly(vinyl chloride), poly(vinyl bromide), cellulose acetate, cellulose butyrate or polystyrene.
Claim 8
Dependent Claim
16 words
The method of claim 6 wherein said sacrificial organic solid material comprises polyethylene or poly(vinyl fluoride).
Claim 9
Independent Claim
210 words
A method for removing polymeric material or photoresist from a semiconductor substrate coated with the same comprising: providing a plasma region and an etching region in a plasma reactor, said regions being spaced apart and in communication with one another through communication means including a corner or bend portion preventing movement of gases between said regions in a straight path; locating a sample of the polymer or photoresist coated substrate in said etching region; locating a sacrificial solid organic material in the etching region of said reactor, said sacrificial material having a substantially higher reactivity to plasma-energized gas generated in said plasma region than the polymeric material or photoresist being etched from said substrate; introducing a reactive gas into said plasma region and producing a plasma therein at a reactor pressure of from 0.1 to 10.0 Torr whereby said plasma-energized gas is formed; contacting the plasma-energized gas with said sacrificial solid organic material whereby a highly reactive gas is formed, said highly reactive gas having a substantially higher reaction rate with said polymeric material or photoresist than said plasma-energized gas; and contacting the coated sustrate with the highly reactive gas in said etching region at a sufficient concentration and for a sufficient time to remove said polymeric material or photoresist.
Claim 10
Independent Claim
210 words
A method for removing polymeric material or photoresist from a semiconductor substrate coated with the same comprising: providing a plasma region and an etching region in a plasma reactor, said regions being spaced apart and in communication with one another through communication means including a corner or bend portion preventing movement of gases between said regions in a straight path; locating a sample of the polymer or photoresist coated substrate in said etching region; locating a sacrificial solid organic material in the etching region of said reactor, said sacrificial material having a substantially higher reactivity to plasma-energized gas generated in said plasma region than the polymeric material or photoresist being etched from said substrate; introducing a reactive gas into said plasma region and producing a plasma therein at a reactor pressure of from 0.1 to 10.0 Torr whereby said plasma-energized gas is formed; contacting the plasma-energized gas with said sacrificial solid organic material whereby a highly reactive gas is formed, said highly reactive gas having a substantially higher reaction rate with said polymeric material or photoresist than said plasma-energized gas; and contacting the coated sustrate with the highly reactive gas in said etching region at a sufficient concentration and for a sufficient time to remove said polymeric material or photoresist.
Claim 11
Dependent Claim
18 words
The method of claim 8 wherein said regions are spaced apart a distance of 5 to 50 cm.
Claim 12
Dependent Claim
22 words
The method of claim 9 wherein said communication means includes a corner or bend providing an angle of 30° to 120° therein.
Claim 13
Dependent Claim
32 words
The method of claim 8 wherein the reactive gas in said plasma region is selected from oxygen, fluorine, chlorine, nitrogen, nitrous oxide, nitric oxide, nitrogen dioxide, hydrogen, water vapor, or mixtures thereof.
Claim 14
Dependent Claim
15 words
The method of claim 11 wherein said reactive gas in said plasma region comprises oxygen.
Claim 15
Dependent Claim
34 words
The method of claim 11 wherein said sacrificial solid organic material comprises a polymer selected from poly(vinyl fluoride), polyethylene, polypropylene, cis-polybutadiene, trans 1,4-polybutadiene, polyacrylonitrile, poly(vinyl chloride), poly(vinyl bromide), cellulose acetate, cellulose butyrate or polystyrene.
Claim 16
Dependent Claim
16 words
The method of claim 13 wherein said sacrificial solid organic material comprises polyethylene or poly(vinyl fluoride).
References Cited (Backward Citations)
US3692655A
Cited
US4175235A
Cited
US4243476A
Cited
US4412119A
Cited
US4368092A
Cited
US4595570A
Cited
US4612099A
Cited
US4554047A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-15 | 1994-10-15 | 1995-04-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-15 | 1998-10-15 | 1999-04-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-15 | 2002-10-15 | 2003-04-16 | $7700.00 | Window Closed / Lapsed |