Preceramic compositions and ceramic products
Assignee: Albemarle Corp
•
Filing: 1989-09-18
•
Granted: 1991-04-09
•
Expires: 2009-09-18
Abstract
Abstract Low density silicon nitride ceramics having improved bending an specific strengths over known silicon nitride ceramics derived from silicon nitride powder and polysilazane precursors are prepared by (A) intimately mixing about 50-80% by weight of silicon nitride powder with about 15-50% by weight of perceramic polysilazane binder, (B) pulverizing the mixture to form particles having a particle size smaller than 105 micrometers, (C) separating from those particles any particles having a particle size larger than about 105 micrometers, (D) molding the resultant composition having a particle size not larger than about 105 micrometers, and (E) pyrolyzing the molded composition in an inert atmosphere to a temperature of about 1200°-1450° C.; said preceramic binder being at least one polysilazane prepared by reacting an organodihalosilane with ammonia, treating the ammonolysis product with a basic catalyst which is capable of deprotonating an NH group that is adjacent to an SiH group, and quenching the resultant product with an electrophilic quenching reagent.
Inventors
- 👤 John Semen
- 👤 John J. Rogers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:11
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/6316; C04B35/515; C04B35/58; C04B35/584; C04B35/589
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
124 words
A process for preparing a ceramic which comprises (A) molding a sintering aid-free preceramic composition having a particle size not larger than about 105 micrometers and comprising an intimate mixture of (1) about 50-85% by weight of silicon nitride powder and (2) about 15-50% by weight of a preceramic polysilazane binder at a temperature of about 60°-225° C., said binder consisting essentially of at least one polysilazane prepared by reacting an organodihalosilane with ammonia, treating the ammonolysis product with a basic catalyst which is capable of deprotonating an NH group that is adjacent to an SiH group, and quenching the resultant product with an electrophilic quenching reagent, and (B) pyrolyzing the molded composition in an inert atmosphere to a temperature of about 1200°-1450° C.
Claim 2
Dependent Claim
124 words
A process for preparing a ceramic which comprises (A) molding a sintering aid-free preceramic composition having a particle size not larger than about 105 micrometers and comprising an intimate mixture of (1) about 50-85% by weight of silicon nitride powder and (2) about 15-50% by weight of a preceramic polysilazane binder at a temperature of about 60°-225° C., said binder consisting essentially of at least one polysilazane prepared by reacting an organodihalosilane with ammonia, treating the ammonolysis product with a basic catalyst which is capable of deprotonating an NH group that is adjacent to an SiH group, and quenching the resultant product with an electrophilic quenching reagent, and (B) pyrolyzing the molded composition in an inert atmosphere to a temperature of about 1200°-1450° C.
Claim 3
Dependent Claim
65 words
The process of claim 1 wherein the pyrolysis is accomplished by heating the molded composition to 1300° C. at rates of 60° C./hour from room temperature to 60° C., 30° C./hour from 60° C. to 260° C., 120° C./hour from 260° C. to 1260° C., and 60° C./hour from 1260° C. to 1300° C., maintaining the temperature at 1300° C. for one hour, and cooling.
Claim 4
Dependent Claim
18 words
The process of claim 1 wherein the binder content of the preceramic composition is about 20-30% by weight.
Claim 5
Dependent Claim
35 words
The process of claim 1 wherein the binder consists essentially of at least one polysilazane prepared by reacting methyldichlorosilane with ammonia, treating the ammonolysis product with potassium hydride, and quenching the resultant product with dimethylchlorosilane.
Claim 6
Dependent Claim
19 words
The process of claim 1 wherein the silicon nitride powder has a mean particle size of about 0.1-1.0 micrometer.
Claim 7
Dependent Claim
159 words
A process for preparing a ceramic which comprises (A) molding a sintering aid-free preceramic composition having a particle size not larger than about 105 micrometers and comprising an intimate mixture of (1) about 70-80% by weight of silicon nitride powder having a mean particle size of about 0.1-1.0 micrometer and (B) about 20-30% by weight of a preceramic polysilazane binder at a temperature of about 60°-225° C., said binder consisting essentially of at least one polysilazane prepared by reacting methyldichlorosilane with ammonia, treating the ammonolysis product with potassium hydride, and quenching the resultant product with dimethylchlorosilane, and (B) pyrolyzing the molded composition in an inert atmosphere by heating it to 1300° C. at rates of 60° C./hour from room temperature to 60° C., 30° C./hour from 60° C. to 260° C., 120° C./hour from 260° C. to 1260° C., and 60° C./hour from 1260° C. to 1300° C., maintaining the temperature at 1300° C. for one hour, and cooling.
Claim 8
Dependent Claim
159 words
A process for preparing a ceramic which comprises (A) molding a sintering aid-free preceramic composition having a particle size not larger than about 105 micrometers and comprising an intimate mixture of (1) about 70-80% by weight of silicon nitride powder having a mean particle size of about 0.1-1.0 micrometer and (B) about 20-30% by weight of a preceramic polysilazane binder at a temperature of about 60°-225° C., said binder consisting essentially of at least one polysilazane prepared by reacting methyldichlorosilane with ammonia, treating the ammonolysis product with potassium hydride, and quenching the resultant product with dimethylchlorosilane, and (B) pyrolyzing the molded composition in an inert atmosphere by heating it to 1300° C. at rates of 60° C./hour from room temperature to 60° C., 30° C./hour from 60° C. to 260° C., 120° C./hour from 260° C. to 1260° C., and 60° C./hour from 1260° C. to 1300° C., maintaining the temperature at 1300° C. for one hour, and cooling.
References Cited (Backward Citations)
US4543344A
Cited
US4482669A
Cited
US4594330A
Cited
US4612383A
Cited
US4645807A
Cited
US4650837A
Cited
US4659850A
Cited
US4891340A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-08 | 1994-10-08 | 1995-04-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-08 | 1998-10-08 | 1999-04-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-08 | 2002-10-08 | 2003-04-09 | $7700.00 | Window Closed / Lapsed |