Assignee: Ford Motor Co
•
Filing: 1987-08-10
•
Granted: 1991-04-02
•
Expires: 2007-08-10
Abstract
Abstract There is disclosed herein, as a new article of manufacutre, a glass substrate coated with tin oxide and a method of making the same. According to the method, in order to produce the new article of manufacture, a glass substrate with a selected surface is heated to a temperature sufficiently hot so that a heat decomposable, tin-containing material coming into the vicinity of the selected surface will be heat decomposed permitting the tin contained in the tin-containing material to be oxidized and deposited as tin oxide on the selected surface. The tin-containing material, which is applied to the heated glass surface is a coating material containing alkyltin alkoxides of the general formula RSn(OR 1 ) 3 where R and R 1 are organo groups containing from 1-6 carbon atoms, whereby a thicker coating film of oxidized tin is deposited on the selected surface of the glass substrate than can be deposited by previously used tin coating materials under the same application and temperature conditions. The new product of manufacture has particular utility when used as a "Low E" glass product for building glazings which reflect infrared radiation back into a building in which such glazings are installed thereby to keep the building warmer.
Inventors
- 👤 Franklin I. Brown
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:22
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; C03C17/253; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/211; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/112
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
146 words
In a method of applying a tin oxide coating to a selected surface of a glass substrate in which said selected surface of said glass substrate is heated to a temperature sufficiently hot so that a heat decomposable tin-containing material coming into the vicinity of said selected surface will be heat decomposed permitting said tin contained in said tin-containing material to be oxidized and deposited as tin oxide on said selected surface, and in which a tin-containing material is applied in an oxygen containing ambient to said heated selected surface of said glass substrate, the improvement comprising: forming said tin-containing material of a coating material containing alkyltin alkoxides of the general formula RSn(OR 1 ) 3 where R and R 1 are alkyl groups containing from 1-6 carbon atoms, whereby a coating film of oxidized tin is deposited on said selected surface of said glass substrate.
Claim 2
Dependent Claim
146 words
In a method of applying a tin oxide coating to a selected surface of a glass substrate in which said selected surface of said glass substrate is heated to a temperature sufficiently hot so that a heat decomposable tin-containing material coming into the vicinity of said selected surface will be heat decomposed permitting said tin contained in said tin-containing material to be oxidized and deposited as tin oxide on said selected surface, and in which a tin-containing material is applied in an oxygen containing ambient to said heated selected surface of said glass substrate, the improvement comprising: forming said tin-containing material of a coating material containing alkyltin alkoxides of the general formula RSn(OR 1 ) 3 where R and R 1 are alkyl groups containing from 1-6 carbon atoms, whereby a coating film of oxidized tin is deposited on said selected surface of said glass substrate.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein: said selected surface of said glass substrate is heated to a temperature in a range from 900° to 1200° F.
Claim 4
Dependent Claim
12 words
The method of claim 1 wherein: said alkyltin alkoxide is butyltin methoxide.
Claim 5
Dependent Claim
12 words
The method of claim 1 wherein: said alkyltin alkoxide is butyltin butoxide.
Claim 6
Dependent Claim
25 words
The method of claim 1 wherein: said coating material is a tin-containing material which contains from about 10% to about 25% by weight of tin.
Claim 7
Independent Claim
78 words
A method of making a coated glass product including: heating a glass substrate; applying a heat decomposable tin-containing material to said heated glass substrate, said material containing alkyltin alkoxides of the general formula RSn(OR 1 ) 3 where R and R 1 are alkyl groups containing from 1-6 carbon atoms; said tin-containing material being applied to said glass substrate in an oxygen containing ambient whereby said material decomposes to form a tin oxide coating on said glass substrate.
Claim 8
Independent Claim
78 words
A method of making a coated glass product including: heating a glass substrate; applying a heat decomposable tin-containing material to said heated glass substrate, said material containing alkyltin alkoxides of the general formula RSn(OR 1 ) 3 where R and R 1 are alkyl groups containing from 1-6 carbon atoms; said tin-containing material being applied to said glass substrate in an oxygen containing ambient whereby said material decomposes to form a tin oxide coating on said glass substrate.
Claim 9
Dependent Claim
164 words
In a method of applying a tin oxide coating to a selected surface of a glass substrate in which said selected surface of said glass substrate is heated to a temperature in a range from 900° F. to 1200° F. so that a heat decomposable tin-containing material coming into the vicinity of said selected surface will be heat decomposed permitting said tin contained in said tin-containing material to be oxidized and deposited as tin oxide on said selected surface, and in which a tin-containing material is applied in an oxygen containing ambient to said heated selected surface of said glass substrate, the improvement comprising: forming said tin-containing material so as to contain from about 10% to 25% by weight of tin in the form of alkyltin alkoxides of the general formula RSn(OR 1 ) 3 where R and R 1 are alkyl groups containing 1-6 carbon atoms, whereby a coating film of oxidized tin is deposited on said selected surface of said glass substrate.
Claim 10
Dependent Claim
164 words
In a method of applying a tin oxide coating to a selected surface of a glass substrate in which said selected surface of said glass substrate is heated to a temperature in a range from 900° F. to 1200° F. so that a heat decomposable tin-containing material coming into the vicinity of said selected surface will be heat decomposed permitting said tin contained in said tin-containing material to be oxidized and deposited as tin oxide on said selected surface, and in which a tin-containing material is applied in an oxygen containing ambient to said heated selected surface of said glass substrate, the improvement comprising: forming said tin-containing material so as to contain from about 10% to 25% by weight of tin in the form of alkyltin alkoxides of the general formula RSn(OR 1 ) 3 where R and R 1 are alkyl groups containing 1-6 carbon atoms, whereby a coating film of oxidized tin is deposited on said selected surface of said glass substrate.
References Cited (Backward Citations)
US3827871A
Cited
US3811918A
Cited
US4140814A
Cited
US4191587A
Cited
US4252838A
Cited
US4707383A
Cited
US4530857A
Cited
JPS6096591A
Cited
US4590096A
Cited
US4725452A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-01 | 1994-10-01 | 1995-04-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-01 | 1998-10-01 | 1999-04-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-01 | 2002-10-01 | 2003-04-02 | $7700.00 | Window Closed / Lapsed |