Claim 2

A process for the preparation of a heat-curable resin system containing from about 1 to about 90 weight percent based upon the total resin system weight of at least one solid bismaleimide, and one or more comonomers, comprising: slurry mixing said solid bismaleimide in the form of particles having a mean size of less than about 30 μm into a liquid comonomer at a temperature such that a substantial portion of said solid bismaleimide does not dissolve in said liquid comonomer.

Claim 3

The process of claim 1 wherein said solid bismaleimide means particle size is less than about 10 μm.

Claim 4

The process of claim 1 wherein said solid bismaleimide mean particle size is less than about 5 μm.

Claim 5

The process of claim 1 wherein said liquid comonomer is selected from the group consisting of bismaleimide resins, epoxy resins, alkenylnadicimide resins, cyanate-functional resins, and alkenylphenol terminated resins, alkenyloxyphenyl-terminated resins.

Claim 6

The process of claim 2 wherein said liquid comonomer is selected from the group consisting of bismaleimide resins, epoxy resins, alkenylnadicimide resins, cyanate-functional resins, and alkenylphenol terminated resins, phenyl-terminated resins.

Claim 7

The process of claim 3 wherein said liquid comonomer is selected from the group consisting of bismaleimide resins, epoxy resins, alkenylnadicimide resins, cyanate-functional resins, and alkenylphenol terminated resins, alkenyloxyphenyl-terminated resins.

Claim 8

The process of claim 6 wherein said comonomer is an alkenylphenyl or alkenyloxyphenyl-terminated oligomer.

Claim 9

The process of claim 6 wherein said comonomer is selected from the group consisting of the dialkenylbisphenols.

Claim 10

The process of claim 8 wherein said dialkenylbisphenol is o,o'-diallylbisphenol A.

Claim 11

The process of claim 6 wherein said comonomer is selected from the group consisting of the alkenyloxyphenylated and alkenylphenylated dicyclopentadiene oligomers.

Claim 12

In a process for the preparation of heat-curable bismaleimide resin-containing systems wherein from 1 weight percent to about 90 weight percent of one or more bismaleimide monomers, based upon the total resin system weight, is combined with one or more comonomers and other resin system components, the improvement comprising: (a) employing as the comonomer a bismaleimide-incompatible comonomer; and (b) slurry mixing at least a portion of said bismaleimide into at least a portion of said resin system; such that the total resin system contains bismaleimide particles uniformly dispersed in said resin system, wherein the average particle size of said bismaleimide particles is about 20 μm or less, and wherein substantial crystallization of additional solid bismaleimide upon cooling is prevented.

Claim 13

In a process for the preparation of heat-curable bismaleimide resin-containing systems wherein from 1 weight percent to about 90 weight percent of one or more bismaleimide monomers, based upon the total resin system weight, is combined with one or more comonomers and other resin system components, the improvement comprising: (a) employing as the comonomer a bismaleimide-incompatible comonomer; and (b) slurry mixing at least a portion of said bismaleimide into at least a portion of said resin system; such that the total resin system contains bismaleimide particles uniformly dispersed in said resin system, wherein the average particle size of said bismaleimide particles is about 20 μm or less, and wherein substantial crystallization of additional solid bismaleimide upon cooling is prevented.

Claim 14

The process of claim 11, wherein said slurry mixing is performed by means of a high shear mixing apparatus.

Claim 15

The process of claim 11, wherein said incompatible comonomer is selected from the group consisting of alkenyl-group-containing comonomers or alkynl-group-containing comonomers having the formula ##STR2## wherein R is an organic diradical containing from 1 to about 40 carbon atoms, and wherein R 1 and R 2 are selected from the group consisting of hydrogen methallyl, allyl, propenyl, and propargyl groups, with the proviso that when R 1 is hydrogen, R 2 is not hydrogen, and where R 2 is hydrogen, R 1 is not hydrogen, and wherein R 3 is selected from C 1 -C 12 lower alkyl, halo, halogenated lower alkyl, and C 1 -C 12 lower alkoxy groups.

Claim 16

The process of claim 11 wherein a portion of said bismaleimide monomer is first dissolved in said incompatible comonomer, while the remainder is added by means of slurry mixing.

Claim 17

The process of claim 11 wherein said bismaleimide is added to said incompatible comonomer in the melt, and wherein the resukting mixture is cooled while being subjected to mixing under high-shear.

Claim 18

A bismaleimide-containing resin system prepared by the process of claim 1.

Claim 19

A bismaleimide-containing resin system prepared by the process of claim 3.

Claim 20

A bismaleimide-containing resin system prepared by the process of claim 6.

Claim 21

A bismaleimide-containing resin system prepared by the process of claim 11.