Dry film photoresist for forming a conformable mask and method of application to a printed circuit board or the like
Assignee: Eternal Technology Corp
•
Filing: 1988-10-28
•
Granted: 1991-02-12
•
Expires: 2008-10-28
Abstract
Abstract A dry film for forming a solder mask includes a cover sheet, a photoimageable composition layer which is curable to form a solder mask and a top coat interposed between the cover sheet and the photoimageable composition layer which is selectively adherent to the photoimageable composition layer. The dry film is applied to a surface of a printed circuit board with a minor portion of the area of the photoimageable composition layer tacked to the printed circuit board. The cover sheet is peeled away. With heat and vacuum, the photoimageable composition layer is laminated to the irregular surface of the printed circuit board, conforming the photoimageable composition layer to the contours thereof and leaving the top coat as a protective covering over the photoimageable composition layer. The photoimageable composition layer is exposed to patterned actinic radiation, developed and cured to form a hard, permanent solder mask.
Inventors
- 👤 Frederick J. Axon
- 👤 James J. Briguglio
- 👤 Amedeo Candore
- 👤 Lawson Lightfoot
- 👤 Clancy P. Crooks
- 👤 Leo Roos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:21
CPC Classifications
B; B32; B32B; B32B37/00; B32B37/02; B30; B30B; B30B15/00; B30B15/06; B30B15/061; B32B37/10; B32B37/1018; G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/092; G03F7/16; G03F7/161; H; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K3/281; B32B2457/00; B32B2457/08; H05K2203/00; H05K2203/06; H05K2203/066; H05K2203/068; H05K2203/08; H05K2203/085; H05K2203/11; H05K2203/1105; H05K3/0073; H05K3/0079
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
128 words
A method of forming a photoimaged layer on an uneven substrate surface, the method comprising: (A) providing a dry film comprising a cover sheet and a layer of photoimageable composition on said cover sheet; (B) tacking said photoimageable composition layer to said substrate surface; (C) removing said cover sheet from said photoimageable composition layer, leaving said photoimageable composition layer tacked to said substrate surface; (D) causing a heated roller to pass across said photoimageable composition layer applying pressure thereto, thereby causing said photoimageable layer to conform to said substrate surface; (E) exposing said photoimageable composition layer to patterned actinic radiation; and (F) developing said photoimageable composition to remove either exposed or unexposed portions from said substrate surface, leaving either unexposed or exposed portions remaining on said substrate surface.
Claim 2
Independent Claim
128 words
A method of forming a photoimaged layer on an uneven substrate surface, the method comprising: (A) providing a dry film comprising a cover sheet and a layer of photoimageable composition on said cover sheet; (B) tacking said photoimageable composition layer to said substrate surface; (C) removing said cover sheet from said photoimageable composition layer, leaving said photoimageable composition layer tacked to said substrate surface; (D) causing a heated roller to pass across said photoimageable composition layer applying pressure thereto, thereby causing said photoimageable layer to conform to said substrate surface; (E) exposing said photoimageable composition layer to patterned actinic radiation; and (F) developing said photoimageable composition to remove either exposed or unexposed portions from said substrate surface, leaving either unexposed or exposed portions remaining on said substrate surface.
Claim 3
Dependent Claim
21 words
A method according to claim 1 wherein said heated roller applies a pressure of between about 1 and about 6 bars.
Claim 4
Dependent Claim
22 words
A method according to claim 1 wherein said roller is heated to a temperature of between about 40° and about 100° C.
Claim 5
Dependent Claim
25 words
A method according to claim 1 wherein the surface of said roller is resilient material of between about 60 and about 80 Shore A hardness.
Claim 6
Independent Claim
190 words
A method of forming a solder mask on the surface of a printed circuit board, the method comprising: (A) providing a dry film comprising (1) a cover sheet, and (2) a layer of photoimageable composition on said cover sheet, which photoimageable composition is curable after exposure and development to provide a hard, permanent solder mask overlying the printed circuit board; (B) tacking said photoimageable composition layer to the surface of said printed circuit board; (C) removing said cover sheet from said photoimageable composition layer, leaving said photoimageable composition layer tacked to the surface of said circuit board; (D) causing a heated roller to pass across said photoimageable composition layer applying pressure thereto, thereby causing said photoimageable composition layer to conform to the surface of said printed circuit board; (E) exposing said photoimageable composition layer to patterned actinic radiation; (F) developing said photoimageable composition to remove either exposed or unexposed portions from said printed circuit board, leaving either unexposed or exposed portions remaining on said printed circuit board; and (G) curing said remaining portions of said photoimageable composition layer to form a hard, permanent solder mask protecting said printed circuit board.
Claim 7
Independent Claim
190 words
A method of forming a solder mask on the surface of a printed circuit board, the method comprising: (A) providing a dry film comprising (1) a cover sheet, and (2) a layer of photoimageable composition on said cover sheet, which photoimageable composition is curable after exposure and development to provide a hard, permanent solder mask overlying the printed circuit board; (B) tacking said photoimageable composition layer to the surface of said printed circuit board; (C) removing said cover sheet from said photoimageable composition layer, leaving said photoimageable composition layer tacked to the surface of said circuit board; (D) causing a heated roller to pass across said photoimageable composition layer applying pressure thereto, thereby causing said photoimageable composition layer to conform to the surface of said printed circuit board; (E) exposing said photoimageable composition layer to patterned actinic radiation; (F) developing said photoimageable composition to remove either exposed or unexposed portions from said printed circuit board, leaving either unexposed or exposed portions remaining on said printed circuit board; and (G) curing said remaining portions of said photoimageable composition layer to form a hard, permanent solder mask protecting said printed circuit board.
Claim 8
Independent Claim
184 words
A method of forming a photoimaged layer on an uneven substrate surface, the method comprising: (A) providing a dry film comprising (1) a cover sheet, (2) a top coat on said cover sheet, and (3) a layer of photoimageable composition on said top coat; said top coat being selectively adherent to said photoimageable composition relative to its adherence to said cover sheet; (B) tacking said photoimageable composition layer to said substrate surface; (C) laminating said photoimageable composition layer to said substrate surface using heat, vacuum and mechanical pressure; (D) removing said cover sheet from said top coat, leaving said photoimageable composition layer tacked to said substrate surface with said top coat covering and protecting said photoimageable composition layer; (E) causing a heated roller to pass across said photoimageable composition layer applying pressure thereto and causing said photoimageable composition layer to conform to said substrate surface; (F) exposing said photoimageable composition layer to patterned actinic radiation; and (G) developing said photoimageable composition layer to remove either exposed or unexposed portions from said substrate surface, leaving either unexposed or exposed portions remaining on said substrate surface.
Claim 9
Independent Claim
184 words
A method of forming a photoimaged layer on an uneven substrate surface, the method comprising: (A) providing a dry film comprising (1) a cover sheet, (2) a top coat on said cover sheet, and (3) a layer of photoimageable composition on said top coat; said top coat being selectively adherent to said photoimageable composition relative to its adherence to said cover sheet; (B) tacking said photoimageable composition layer to said substrate surface; (C) laminating said photoimageable composition layer to said substrate surface using heat, vacuum and mechanical pressure; (D) removing said cover sheet from said top coat, leaving said photoimageable composition layer tacked to said substrate surface with said top coat covering and protecting said photoimageable composition layer; (E) causing a heated roller to pass across said photoimageable composition layer applying pressure thereto and causing said photoimageable composition layer to conform to said substrate surface; (F) exposing said photoimageable composition layer to patterned actinic radiation; and (G) developing said photoimageable composition layer to remove either exposed or unexposed portions from said substrate surface, leaving either unexposed or exposed portions remaining on said substrate surface.
Claim 10
Independent Claim
243 words
A method of forming a solder mask on the surface of a printed circuit board, the method comprising: (A) providing a dry film comprising (1) a cover sheet; (2) a top coat on said cover sheet, and (3) a layer of photoimageable composition on said top coat, which photoimageable composition is curable after exposure and development to provide a hard, permanent solder mask overlying the printed circuit board; said top coat being selectively adherent to said photoimageable composition relative to its adherence to said cover sheet; (B) tacking said photoimageable composition layer to the surface of said printed circuit board; (C) laminating said photoimageable layer to the surface of said printed circuit board using heat, vacuum and mechanical pressure; (D) removing said cover sheet from said top coat, leaving said photoimageable composition layer tacked to the surface of said circuit board with said top coat covering and protecting the same; (E) causing a heated roller to pass across said photoimageable composition layer applying pressure thereto and causing said photoimageable composition layer to conform to the surface of said printed circuit board; (F) exposing said photoimageable composition layer to patterned actinic radiation; (G) developing said photoimageable composition to remove either exposed or unexposed portions from said printed circuit board, leaving either unexposed or exposed portions remaining on said printed circuit board; and (H) curing said remaining portions of said photoimageable composition layer to form a hard, permanent solder mask protecting said printed circuit board.
Claim 11
Independent Claim
243 words
A method of forming a solder mask on the surface of a printed circuit board, the method comprising: (A) providing a dry film comprising (1) a cover sheet; (2) a top coat on said cover sheet, and (3) a layer of photoimageable composition on said top coat, which photoimageable composition is curable after exposure and development to provide a hard, permanent solder mask overlying the printed circuit board; said top coat being selectively adherent to said photoimageable composition relative to its adherence to said cover sheet; (B) tacking said photoimageable composition layer to the surface of said printed circuit board; (C) laminating said photoimageable layer to the surface of said printed circuit board using heat, vacuum and mechanical pressure; (D) removing said cover sheet from said top coat, leaving said photoimageable composition layer tacked to the surface of said circuit board with said top coat covering and protecting the same; (E) causing a heated roller to pass across said photoimageable composition layer applying pressure thereto and causing said photoimageable composition layer to conform to the surface of said printed circuit board; (F) exposing said photoimageable composition layer to patterned actinic radiation; (G) developing said photoimageable composition to remove either exposed or unexposed portions from said printed circuit board, leaving either unexposed or exposed portions remaining on said printed circuit board; and (H) curing said remaining portions of said photoimageable composition layer to form a hard, permanent solder mask protecting said printed circuit board.
Claim 12
Independent Claim
188 words
A method of forming a photoimaged layer on an uneven substrate surface, the method comprising: (A) providing a dry film comprising (1) a cover sheet; (2) a top coat on said cover sheet, and (3) a layer of photoimageable composition on said top coat; said top coat being selectively adherent to said photoimageable composition layer relative to its adherence to said cover sheet; (B) tacking said photoimageable composition layer to said substrate surface; (C) laminating said photoimageable composition layer to said substrate surface using heat, vacuum and mechanical pressure; (D) removing said cover sheet from said top coat, leaving said photoimageable composition layer tacked to said substrate surface with said top coat covering and protecting said photoimageable composition layer; (E) laminating said photoimageable composition layer to said substrate surface, using heat, vacuum and mechanical pressure to conform said photoimageable composition layer and said top coat to said substrate surface; (F) exposing said photoimageable composition layer to patterned actinic radiation; and (G) developing said photoimageable composition layer to remove either exposed or unexposed portions from said substrate surface, leaving either unexposed or exposed portions remaining on said substrate surface.
Claim 13
Independent Claim
188 words
A method of forming a photoimaged layer on an uneven substrate surface, the method comprising: (A) providing a dry film comprising (1) a cover sheet; (2) a top coat on said cover sheet, and (3) a layer of photoimageable composition on said top coat; said top coat being selectively adherent to said photoimageable composition layer relative to its adherence to said cover sheet; (B) tacking said photoimageable composition layer to said substrate surface; (C) laminating said photoimageable composition layer to said substrate surface using heat, vacuum and mechanical pressure; (D) removing said cover sheet from said top coat, leaving said photoimageable composition layer tacked to said substrate surface with said top coat covering and protecting said photoimageable composition layer; (E) laminating said photoimageable composition layer to said substrate surface, using heat, vacuum and mechanical pressure to conform said photoimageable composition layer and said top coat to said substrate surface; (F) exposing said photoimageable composition layer to patterned actinic radiation; and (G) developing said photoimageable composition layer to remove either exposed or unexposed portions from said substrate surface, leaving either unexposed or exposed portions remaining on said substrate surface.
Claim 14
Independent Claim
245 words
A method of forming a solder mask on the surface of a printed circuit board, the method comprising: (A) providing a dry film comprising (1) a cover sheet, (2) a top coat on said sheet, and (3) a layer of photoimageable composition on said top coat, which photoimageable composition is curable after exposure and development to provide a hard, permanent solder mask overlying the printed circuit board; said top coat being selectively adherent to said photoimageable composition relative to its adherence to said cover sheet; (B) tacking said photoimageable composition layer to the surface of said printed circuit board; (C) laminating said photoimageable layer to the surface of said printed circuit board using heat, vacuum and mechanical pressure; (D) removing said cover sheet from said top coat, leaving said photoimageable composition layer laminated to the surface of said circuit board with said top coat covering and protecting the same; (E) laminating said photoimageable composition layer to the surface of said printed circuit board, using heat, vacuum and mechanical pressure to conform said photoimageable composition layer and said top coat to the surface thereof; (F) exposing said photoimageable composition layer to patterned actinic radiation; (G) developing said photoimageable composition to remove either exposed or unexposed portions from said printed circuit board, leaving either unexposed or exposed portions remaining on said printed circuit board; and (H) curing said remaining portions of said photoimageable composition layer to form a hard, permanent solder mask protecting said printed circuit board.
Claim 15
Independent Claim
245 words
A method of forming a solder mask on the surface of a printed circuit board, the method comprising: (A) providing a dry film comprising (1) a cover sheet, (2) a top coat on said sheet, and (3) a layer of photoimageable composition on said top coat, which photoimageable composition is curable after exposure and development to provide a hard, permanent solder mask overlying the printed circuit board; said top coat being selectively adherent to said photoimageable composition relative to its adherence to said cover sheet; (B) tacking said photoimageable composition layer to the surface of said printed circuit board; (C) laminating said photoimageable layer to the surface of said printed circuit board using heat, vacuum and mechanical pressure; (D) removing said cover sheet from said top coat, leaving said photoimageable composition layer laminated to the surface of said circuit board with said top coat covering and protecting the same; (E) laminating said photoimageable composition layer to the surface of said printed circuit board, using heat, vacuum and mechanical pressure to conform said photoimageable composition layer and said top coat to the surface thereof; (F) exposing said photoimageable composition layer to patterned actinic radiation; (G) developing said photoimageable composition to remove either exposed or unexposed portions from said printed circuit board, leaving either unexposed or exposed portions remaining on said printed circuit board; and (H) curing said remaining portions of said photoimageable composition layer to form a hard, permanent solder mask protecting said printed circuit board.
Claim 16
Dependent Claim
25 words
A method according to claim 9 wherein said conforming laminating step E is carried out for about half the time as said laminating step (C).
Claim 17
Dependent Claim
27 words
A method according to claim 9 wherein in step B said photoimageable composition layer is tacked to the leading and trailing edges of the printed circuit board.
Claim 18
Dependent Claim
38 words
A method according to claim 9 wherein said lamination steps C and E are each carried out at a temperature of between about 40° C. and about 100° C. and a vacuum of at least about 1 millibar.
Claim 19
Dependent Claim
29 words
A method according to claim 9 wherein the thickness of said photoimageable layer is about equal to or less than the elevation of traces on said printed circuit board.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-11 | 1994-08-13 | 1995-02-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-11 | 1998-08-13 | 1999-02-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-11 | 2002-08-13 | 2003-02-12 | $7700.00 | Window Closed / Lapsed |