Method of making a macroscopic stepped structure on a vicinally cut crystal
Assignee: Iconectiv LLC
•
Filing: 1989-06-02
•
Granted: 1991-01-22
•
Expires: 2009-06-02
Abstract
Abstract A semiconductor structure having a face with macroscopic parallel steps and its method of making. The structure is formed by cutting a face on a crystal at a vicinal angle, that is, being misoriented from a major crystal face by a few degrees. Atomic sized microsteps are formed in the vicinal face. Parallel grooves or other regular irregularities are etched in the vicinal face. Subsequent epitaxial growth causes the microsteps to coalesce into macroscopic steps. Alternatively, etching or annealing can accomplish the same coalescing. Novel electronic structures can be fabricated on the stepped structure.
Inventors
- 👤 Etienne G. Colas
- 👤 Herbert M. Cox
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:55
CPC Classifications
B; B82; B82Y; B82Y10/00; H; H10; H10P; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2909; H10P14/24; H10P14/2911; H10P14/2924; H10P14/2925; H10P14/32; H10P14/3202; H10P14/3214; H10P14/3221; H10P14/3242; H10P14/3244; H10P14/3251; H10P14/3252; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3421; H10P52/00; Y; Y10; Y10S; Y10S117/00; Y10S117/901; Y10S117/902; Y10S148/00; Y10S148/095; Y10S438/00; Y10S438/962
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
72 words
A method of fabricating macroscopic steps in a crystal, comprising the steps of: providing a crystal of a material with a vicinal surface oriented at a vicinal angle to a major crystalline face of said crystal, microsteps thereby being formed in said vicinal surface; forming at least two parallel lines of similar irregularities in said vicinal surface; and coalescing a substantial number of said microsteps between said lines into a macroscopic step.
Claim 2
Independent Claim
72 words
A method of fabricating macroscopic steps in a crystal, comprising the steps of: providing a crystal of a material with a vicinal surface oriented at a vicinal angle to a major crystalline face of said crystal, microsteps thereby being formed in said vicinal surface; forming at least two parallel lines of similar irregularities in said vicinal surface; and coalescing a substantial number of said microsteps between said lines into a macroscopic step.
Claim 3
Dependent Claim
22 words
A method as recited in claim 1, wherein said coalescing comprises permitting epitaxial surface atoms on said vicinal surface to rearrange themselves.
Claim 4
Dependent Claim
23 words
A method as recited in claim 2, wherein said permitting step comprises annealing said crystal having said vicinal surface formed with said lines.
Claim 5
Dependent Claim
23 words
A method as recited in claim 2, wherein said permitting step comprises epitaxially depositing atoms on said vicinal surface formed with said lines.
Claim 6
Dependent Claim
15 words
A method as recited in claim 4, wherein said depositing step comprises vapor levitation epitaxy.
Claim 7
Dependent Claim
15 words
A method as recited in claim 4, wherein said depositing step comprises chemical vapor deposition.
Claim 8
Dependent Claim
24 words
A method as recited in claim 4, wherein said coalescing steps coalesces substantially all of said microsteps between said lines into said macroscopic step.
Claim 9
Dependent Claim
32 words
A method as recited in claim 4, wherein said lines of irregularities comprise grooves formed in said vicinal surface and wherein said forming step comprises etching said grooves in said vicinal surface.
Claim 10
Dependent Claim
22 words
A method as recited in claim 4, wherein said irregularities comprise a two-dimensional array of said irregularities protruding from said vicinal surface.
Claim 11
Dependent Claim
42 words
A method as recited in claim 9, wherein said two-dimensional array is a square array arranged along orthogonal axes and a normal to said vicinal surface and a normal to said major face lie in a plane substantially bisecting said orthogonal axes.
Claim 12
Dependent Claim
24 words
A method as recited in claim 4, further comprising fabricating an opto-electronic structure above a surface of said crystal formed with said macroscopic steps.
Claim 13
Dependent Claim
16 words
A method as recited in claim 4, wherein said vicinal angle is between 0.1° and 20°.
Claim 14
Dependent Claim
16 words
A method as recited in claim 12, wherein said vicinal angle is between 0.1° and 10°.
Claim 15
Dependent Claim
30 words
A method as recited in claim 1, wherein said providing step comprises cutting said crystal along a plane inclined at said vicinal angle with respect to said major crystalline face.
Claim 16
Independent Claim
78 words
A method of fabricating a macroscopic step, comprising the steps of: providing a crystalline semiconductor substrate having a vicinal surface oriented at a vicinal angle to a major face of a crystal structure of said substrate; forming at least one groove in said vicinal surface; and epitaxially growing a semiconductor material having said crystal structure on said substrate formed with said groove to thereby form a macroscopic step in said semiconductor material in a vicinity of said groove.
Claim 17
Independent Claim
78 words
A method of fabricating a macroscopic step, comprising the steps of: providing a crystalline semiconductor substrate having a vicinal surface oriented at a vicinal angle to a major face of a crystal structure of said substrate; forming at least one groove in said vicinal surface; and epitaxially growing a semiconductor material having said crystal structure on said substrate formed with said groove to thereby form a macroscopic step in said semiconductor material in a vicinity of said groove.
Claim 18
Dependent Claim
36 words
A method as recited in claim 15, wherein said semiconductor substrate and said semiconductor material comprise multicomponent semiconductors having a zincblende crystal structure as said crystal structure and said vicinal angle is between 0.1° and 20°.
Claim 19
Dependent Claim
26 words
A method as recited in claim 16, further comprising forming an opto-electronic device over said grown epitaxial semiconductor material in a vicinity of said macroscopic step.
Claim 20
Dependent Claim
83 words
A semiconductor structure, comprising: a semiconductor body formed of a semiconducting material having a major crystal face; a vicinal planar surface formed on said semiconductor body, said vicinal surface having a normal separated from a normal of said major crystal face by an angle between 0.1° and 20°; and at least three macroscopic steps formed in said vicinal surface, separated by substantially equal distances, a step height of said steps being substantially equal and being a plurality of atomic distances of said crystal.
Claim 21
Dependent Claim
83 words
A semiconductor structure, comprising: a semiconductor body formed of a semiconducting material having a major crystal face; a vicinal planar surface formed on said semiconductor body, said vicinal surface having a normal separated from a normal of said major crystal face by an angle between 0.1° and 20°; and at least three macroscopic steps formed in said vicinal surface, separated by substantially equal distances, a step height of said steps being substantially equal and being a plurality of atomic distances of said crystal.
Claim 22
Dependent Claim
17 words
A semiconductor structure as recited in claim 18, wherein said vicinal angle is between 0.1° and 10°.
Claim 23
Dependent Claim
17 words
A semiconductor structure as recited in claim 18, wherein said semiconducting material comprises a multicomponent zincblende semiconductor.
Claim 24
Dependent Claim
19 words
A semiconductor structure as recited in claim 20, further comprising an opto-electronic device epitaxially formed over said macroscopic steps.
Claim 25
Dependent Claim
15 words
A semiconductor structure as recited in claim 21, wherein said device includes a quantum wire.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-21 | 1994-07-23 | 1995-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-21 | 1998-07-23 | 1999-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-21 | 2002-07-23 | 2003-01-22 | $7700.00 | Window Closed / Lapsed |