Method of manufacturing josephson junctions
Assignee: Riken Corp
•
Filing: 1990-01-01
•
Granted: 1991-01-15
•
Expires: 2010-01-01
Abstract
Abstract A method of manufacturing Josephson junctions includes steps of high Tc superconductor thin films on a substrates by chemical vapor deposition using raw materials, which includes at least yttrium, barium and copper, serving as vapor generating sources, and fabricating the high Tc superconductor thin films into micro-bridges to produce Josephson junctions.
Inventors
- 👤 Hideyuki Kurosawa
- 👤 Toshio Hirai
- 👤 Hisanori Yamane
- 👤 Tsutomu Yamashita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 14:26
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/10; H10N60/12; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0436; H10N60/0464; H10N60/0912; H10N60/0941; Y; Y10; Y10S; Y10S505/00; Y10S505/80; Y10S505/815; Y10S505/816; Y10S505/817; Y10S505/818; Y10S505/819; Y10S505/82
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
149 words
A method of manufacturing a thin film Josephson junction, comprising the steps of: heating β-diketonate complexes of yttrium, borium, and copper elements each in a separate raw material vessel to a temperature corresponding to the vapor phase temperature of the respective elements; heating a substrate in a reaction vessel to a temperature corresponding to a temperature suitable for decomposing and polymerizing said vapors; supplying an inert carrier gas to each raw material vessel at a predetermined flow rate; mixing in the reaction vessel the inert carrier gas and vapors from each of the raw material vessels with oxygen; subjecting the heating substrate to the mixture of the vapors and inert gas and oxygen for a time period in accordance with the desired thickness of the thin film; cooling the substrate at a predetermined rate; and forming a micro bridge pattern in said thin film to provide the Josephson junction.
Claim 2
Independent Claim
149 words
A method of manufacturing a thin film Josephson junction, comprising the steps of: heating β-diketonate complexes of yttrium, borium, and copper elements each in a separate raw material vessel to a temperature corresponding to the vapor phase temperature of the respective elements; heating a substrate in a reaction vessel to a temperature corresponding to a temperature suitable for decomposing and polymerizing said vapors; supplying an inert carrier gas to each raw material vessel at a predetermined flow rate; mixing in the reaction vessel the inert carrier gas and vapors from each of the raw material vessels with oxygen; subjecting the heating substrate to the mixture of the vapors and inert gas and oxygen for a time period in accordance with the desired thickness of the thin film; cooling the substrate at a predetermined rate; and forming a micro bridge pattern in said thin film to provide the Josephson junction.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein the step of forming the micro-bridge pattern includes etching a pattern having a width in the range of one to ten microns.
Claim 4
Dependent Claim
28 words
The method of claim 1 wherein the step of forming the micro-bridge pattern includes providing a crystalline grain boundary at a junction of the micro-bridge and thin film.
Claim 5
Dependent Claim
47 words
The method of claim 1 wherein the step of heating the substrate includes heating the substrate to a temperature in the range of 700° to 850° C., and the step of mixing in the reaction vessel includes reducing the pressure in the reaction vessel a selected amount.
Claim 6
Dependent Claim
73 words
The method according to claim 1 wherein the step of heating the substrate includes heating an MgO (100) single-crystal substrate the step of subjecting the heating substrate to the vapor mixture includes selecting a time period for providing a thin film having a thickness of one-half to one micron, and the step of forming the micro-bridge pattern includes etching a pattern having a length of one micron and a width of one micron.
Claim 7
Dependent Claim
25 words
The method of claim 1 wherein the step of subjecting the heating substrate to the mixture includes depositing a thin film having a c-axis orientation.
Claim 8
Dependent Claim
60 words
The method of claim 1 wherein the step of heating the β-diketonate includes heating Y (C 11 H 19 O 2 ) to approximately 133° C. to 134° C., Ba (C 11 H 19 O 2 ) 2 to approximately 248° C. to 252° C., Cu(C 11 H 19 O 2 ) 2 to approximately 130° C. to 133° C.
Claim 9
Dependent Claim
31 words
The method of claim 1 wherein the step of heating the substrate includes heating a crystalline substrate having a coefficient of expansion approximating the coefficient of expansion of the thin film.
Claim 10
Dependent Claim
35 words
The method of claim 8 wherein the step of heating the substrate includes heating a substrate composed of one of the materials selected from the group consisting of strontium titanate, stabilized zirconia, and lanthanum aluminate.
Claim 11
Dependent Claim
32 words
The method of claim 1 wherein the step of mixing with oxygen in the reaction vessel includes introducing the oxygen into the reaction vessel separate from the vapor and the inert gas.
Claim 12
Dependent Claim
57 words
The method of claim 1 wherein the step of subjecting the heated substrate to the mixture of oxygen and inert gas and vapor for a selected time further includes controlling the composition of the thin film by varying the temperatures of the elements in the raw material vessels and the flow rate of the inert carrier gas.
Claim 13
Dependent Claim
44 words
The method of claim 1 wherein the step of mixing the inert gas and vapors with oxygen in the reaction vessel includes supplying three parts of β-diketonate of copper and two parts of β-diketonate of barium for very one part of β-diketonate of yttrium.
Claim 14
Dependent Claim
32 words
The method of claim 1 wherein the step of cooling includes cooling the thin film and substrate at a rate in the range of approximately 1° C. to 30° C. per minute.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-14 | 1994-07-16 | 1995-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-14 | 1998-07-16 | 1999-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-14 | 2002-07-16 | 2003-01-15 | $7700.00 | Window Closed / Lapsed |