Process for using a composition for a solder mask

Claim 2

A process for forming a directly solderable printed circuit article comprising: (1) providing a release surface; (2) applying a solder mask over the release surface and drying the solder mask wherein the solder mask comprises polyhydroxyether, melamine formaldehyde, solvent, filler and flow control agent; (3) applying an ink comprising a thixotropic thermosetting resin composition containing a desired amount of an electrically conductive metal powder and high surface area metal flake to the release surface over the mask in the configuration of a solderable electric circuit element and drying the ink; (4) printing in registration with the ink circuit element and mask a reactive thixotropic adhesive interface capable of interacting with the thermosetting resin composition of step (3) and with a thermosetting dielectric surface and drying the adhesive; (5) bringing together the release surface and the thermoplastic dielectric surface so that the solderable electrical circuit element is facing the dielectric surface and is separated therefrom by the adhesive interface; and (6) applying sufficient heat and pressure to form a composite structure whereby the thermosetting resin is cured and the adhesive is interacted whereby the electrical circuit element is transferred from the release surface and bonded to the thermoplastic dielectric surface.

Claim 3

A process for forming a directly solderable printed circuit article comprising: (1) providing a release surface; (2) applying a solder mask over the release surface and drying the solder mask wherein the solder mask comprises polyhydroxyether, melamine formaldehyde, solvent, filler and flow control agent; (3) applying an ink comprising a thixotropic thermosetting resin composition containing a desired amount of an electrically conductive metal powder and high surface area metal flake to the release surface over the mask in the configuration of a solderable electric circuit element and drying the ink; (4) printing in registration with the ink circuit element and mask a reactive thixotropic adhesive interface capable of interacting with the thermosetting resin composition of step (3) and with a thermoplastic dielectric surface and drying the adhesive; (5) bringing together the release surface and the thermoplastic dielectric surface so that the solderable electrical circuit element is facing the dielectric surface and is separated therefrom by the adhesive interface; and (6) applying sufficient heat and pressure to form a composite structure whereby the thermosetting resin is cured and the adhesive is interacted whereby the electrical circuit element is transferred from the release surface and bonded to the thermoplastic dielectric surface; wherein the solder mask comprises about 12% polyhydroxyether, about 60% diethylene glycol monobutyl ether acetate, about 3% melamine formaldehyde, about 3% phthalo cyanine green, about 18% mica, about 2% epoxy resin, about 3% silica, and a reaction promoting concentration of dinonylnaphthalene sulfonate ester, all percentages by weight of the composition.

Claim 4

A process for forming a directly solderable printed circuit article comprising: (1) providing a release surface; (2) applying a solder mask over the release surface and drying the solder mask wherein the solder mask comprises polyhydroxyether, melamine formaldehyde, solvent, filler and flow control agent; (3) applying an ink comprising a thixotropic thermosetting resin composition containing a desired amount of an electrically conductive metal powder and high surface area metal flake to the release surface over the mask in the configuration of a solderable electric circuit element and drying the ink; (4) printing in registration with the ink circuit element and mask a reactive thixotropic adhesive interface capable of interacting with the thermosetting resin composition of step (3) and with a thermoplastic dielectric surface and drying the adhesive; (5) bringing together the release surface and the thermoplastic dielectric surface so that the solderable electrical circuit element is facing the dielectric surface and is separated therefrom by the adhesive interface; and (6) applying sufficient heat and pressure to form a composite structure whereby the thermosetting resin is cured and the adhesive is interacted whereby the electrical circuit element is transferred from the release surface and bonded to the thermoplastic dielectric surface; wherein the solder mask comprises about 12% polyhydroxyether, about 60% diethylene glycol monobutyl ether acetate, about 3% melamine formaldehyde, about 3% phthalo cyanine green, about 18% mica, about 2% epoxy resin, about 3% silica, and a reaction promoting concentration of dinonylnaphthalene sulfonate ester, all percentages by weight of the composition.

Claim 5

The process according to claim 1, wherein the solder mask comprises about 10 to 16 weight percent polyhydroxyether, about 2 to 7 weight percent melamine formaldehyde, about 37 to 70 weight percent solvent having a boiling point between about 230° C. to 250° C., about 14 to 27 weight percent filler, and about 2.5 to 4.5 weight percent flow control agent, all percentages by weight of the composition.

Claim 6

The process according to claim 1, wherein the solder mask comprises about 12% polyhydroxyether, about 60% diethylene glycol monobutyl ether acetate, about 3% melamine formaldehyde, about 3% phthalo cyanine green, about 18% mica, about 2% epoxy resin, about 3% silica, and a reaction promoting concentration of dinonylnaphthalene sulfonate ester, all percentages by weight of the composition.