Modified block copolymer composition
Assignee: Asahi Kasei Corp
•
Filing: 1989-02-07
•
Granted: 1990-11-20
•
Expires: 2009-02-07
Abstract
Abstract A modified block copolymer composition comprising a thermoplastic polymer and a modified block copolymer consisting essentially of a base block copolymer of a monovinyl substituted aromatic hydrocarbon polymer block and an olefin compound polymer block having an ethylenic unsaturation degree not exceeding 20%, the base block copolymer having a molecular unit containing a carboxylic acid group and/or a group derived therefrom grafted thereto. The modified block copolymer composition of the present invention is a resinous composition excellent in impact resistance, adhesion, paint adhesion, weatherability, resistance to thermal deterioration, transparency and gloss or a rubbery or leather-like composition excellent in heat resistance, abrasion resistance, compression set resistance, adhesion, transparency, oil resistance, weatherability and resistance to heat aging.
Inventors
- 👤 Toshinori Shiraki
- 👤 Fusakazu Hayano
- 👤 Hideo Morita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:04
CPC Classifications
C; C08; C08F; C08F287/00; C08F8/00; C08F8/04; C08F8/46; C08L; C08L51/00; C08L51/006; C08L77/00; C08F2810/00; C08F2810/20
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
134 words
A modified block copolymer composition comprising: (a) at least one thermoplastic polymer selected from the group consisting of thermoplastic polyesters, polyvinyl alcohols, polyvinyl esters, ionomers, polyoxymethylenes, polycarbonates, modified polycarbonates, polysulfones, modified polysulfones, polyphenylene ethers, modified polyphenylene ethers, polyarylene sulfides and modified polyarylene sulfides; and (b) at least one modified block copolymer comprising: a base block copolymer of at least two monovinyl substituted aromatic hydrocarbon polymer blocks (A) and at least one olefin compound polymer block (B) having an ethylenic unsaturation degree not exceeding 20%; and at least one molecular unit grafted to said base block copolymer, said molecular unit containing at least one member selected from units of acrylic acid, acrylic esters, acrylic amide, methacrylic acid, methacrylic esters and methacrylic amide; wherein said polar thermoplastic polymers are exclusive of said modified block copolymer (b).
Claim 2
Dependent Claim
134 words
A modified block copolymer composition comprising: (a) at least one thermoplastic polymer selected from the group consisting of thermoplastic polyesters, polyvinyl alcohols, polyvinyl esters, ionomers, polyoxymethylenes, polycarbonates, modified polycarbonates, polysulfones, modified polysulfones, polyphenylene ethers, modified polyphenylene ethers, polyarylene sulfides and modified polyarylene sulfides; and (b) at least one modified block copolymer comprising: a base block copolymer of at least two monovinyl substituted aromatic hydrocarbon polymer blocks (A) and at least one olefin compound polymer block (B) having an ethylenic unsaturation degree not exceeding 20%; and at least one molecular unit grafted to said base block copolymer, said molecular unit containing at least one member selected from units of acrylic acid, acrylic esters, acrylic amide, methacrylic acid, methacrylic esters and methacrylic amide; wherein said polar thermoplastic polymers are exclusive of said modified block copolymer (b).
Claim 3
Dependent Claim
45 words
The composition according to claim 1, wherein said modified polycarbonates, said modified polysulfones, said modified polyphenylene ethers and said modified polyarylene sulfides are respectively blends of polycarbonates, polysulfones, polyphenylene ethers and polyarylene sulfides with an alkenyl aromatic hydrocarbon polymer and/or an alkenyl aromatic hydrocarbon copolymer.
Claim 4
Dependent Claim
45 words
The composition according to claim 1, wherein said ionomers are substrate copolymers of α,β-unsaturated carboxylic acids and other monomer, each ionomer having carboxylic acid groups ionically crosslinked through at least one metal ion selected from the group consisting of monovalent, divalent and trivalent metal ions.
Claim 5
Dependent Claim
59 words
The composition according to claim 1, wherein said molecular unit containing at least one member selected from units of acrylic acid, acrylic esters, acrylic amide, methacrylic acid, methacrylic esters and methacrylic amide is grafted to said base block copolymer in an amount of 0.05 to 30 parts by weight, per 100 parts by weight of said base block copolymer.
Claim 6
Dependent Claim
34 words
The composition according to claim 1, wherein said monovinyl substituted aromatic hydrocarbon is contained in said base block copolymer in an amount of 5 to 95% by weight, based on said base block copolymer.
Claim 7
Dependent Claim
35 words
The composition according to claim 5, wherein said monovinyl substituted aromatic hydrocarbon is contained in said base block copolymer in an amount of 5 to 60% inclusive by weight, based on said base block copolymer.
Claim 8
Dependent Claim
39 words
The composition according to claim 5, wherein said monovinyl substituted aromatic hydrocarbon is contained in said base block copolymer in an amount of over 60% by weight up to 95% inclusive by weight, based on said base block copolymer.
Claim 9
Dependent Claim
61 words
The composition according to claim 1, wherein said monovinyl substituted aromatic hydrocarbon is contained in said base block copolymer in an amount of over 60% by weight up to 95% inclusive by weight, based on said base block copolymer, and said thermoplastic polymer (a) is present in a weight ratio of 90:10 to 5:95 relative to said modified block copolymer (b).
Claim 10
Dependent Claim
60 words
The composition according to claim 1, wherein said monovinyl substituted aromatic hydrocarbon is contained in said base block copolymer in an amount of 5 to 60% inclusive by weight, based on said base block copolymer, and said thermoplastic polymer (a) is present in a weight ratio of over 50:50 up to 98:2 inclusive relative to said modified block copolymer (b).
Claim 11
Dependent Claim
60 words
The composition according to claim 1, wherein said monovinyl substituted aromatic hydrocarbon is contained in said base block copolymer in an amount of 5 to 60% inclusive by weight, based on the weight of said base block copolymer, and said thermoplastic polymer (a) is present in a weight ratio of 2:98 to 50:50 relative to said modified block copolymer (b).
Claim 12
Dependent Claim
73 words
The composition according to claim 1, wherein said modified block copolymer is one obtained by the reaction of a base block copolymer of at least two monovinyl substituted aromatic hydrocarbon polymer blocks and at least one olefin compound polymer block having an ethylenic unsaturation degree not exceeding 20% with at least one modifying agent selected from the group consisting of acrylic acid, acrylic esters, acrylic amide, methacrylic acid, methacrylic esters and methacrylic amide.
Claim 13
Dependent Claim
76 words
The composition according to claim 11, wherein said base block copolymer is one obtained by selectively hydrogenating a precursory block copolymer comprising at least two monovinyl substituted aromatic hydrocarbon polymer blocks and at least one polymer block composed mainly of a conjugated diene compound, wherein said selective hydrogenation is performed at the conjugated diene compound moiety of said polymer block to the extent that the ethylenic unsaturation degree of said polymer block is 20% or less.
Claim 14
Dependent Claim
25 words
The composition according to claim 12, wherein the conjugated diene compound moiety of said precursory block copolymer has a vinyl content of 10 to 80%.
Claim 15
Dependent Claim
14 words
The composition according to claim 13, wherein the vinyl content is 25 to 65%.
Claim 16
Dependent Claim
41 words
The composition according to claim 1, wherein said modified block copolymer is ionically crosslinked through at a least one metal ion selected from the group consisting of monovalent, divalent and trivalent metal ions to form an ionically crosslinked modified block copolymer.
Claim 17
Dependent Claim
51 words
The composition according to claim 15, wherein the ionically crosslinking of said modified block copolymer through said metal ion is made in a ratio of 0.1 to 3.0, said ratio being defined as a molar ratio of the metal ion relative to said molecular unit contained in said modified block copolymer.
Claim 18
Dependent Claim
30 words
The composition according to claim 15, wherein said metal ion is at least one member selected from the group consisting of lithium, sodium, potassium, magnesium, calcium, zinc and aluminum ions.
Claim 19
Dependent Claim
33 words
The composition according to claim 1, wherein said modified block copolymer (b) is a three block copolymer consisting essentially of two of said polymer blocks (A) and one of said polymer block (B).
Claim 20
Dependent Claim
33 words
The composition according to claim 1, wherein said modified block copolymer (b) is a four block copolymer consisting essentially of two of said polymer blocks (A) and two of said polymer blocks (B).
Claim 21
Dependent Claim
33 words
The composition according to claim 1, wherein said modified block copolymer (b) is a radial block copolymer consisting essentially of four of said polymer blocks (A) and four of said polymer blocks (B).
Claim 22
Dependent Claim
30 words
The molded product formed from the composition of claim 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17 18, 19 or 20.
References Cited (Backward Citations)
US3607977A
Cited
GB1260897A
Cited
US3668125A
Cited
JPS4862851A
Cited
JPS5085695A
Cited
US3985829A
Cited
US4007311A
Cited
JPS52117940A
Cited
JPS52150457A
Cited
US4033888A
Cited
US4077893A
Cited
JPS54122382A
Cited
JPS54144477A
Cited
JPS5513719A
Cited
JPS5513727A
Cited
US4282132A
Cited
US4292414A
Cited
JPS5560511A
Cited
US4429076A
Cited
JPS55165931A
Cited
JPS5651349A
Cited
JPS5662805A
Cited
US4359551A
Cited
US4264747A
Cited
US4427828A
Cited
US4480057A
Cited
US4508874A
Cited
US4578429A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-19 | 1994-05-21 | 1994-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-19 | 1998-05-21 | 1998-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-19 | 2002-05-21 | 2002-11-20 | $7700.00 | Window Closed / Lapsed |