US4292414A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the preparation of modified block copolymers
Assignee: Asahi Kasei Corp
•
Filing: 1979-10-29
•
Granted: 1981-09-29
•
Expires: 1999-10-29
Abstract
Abstract A process for preparing a modified block copolymer by graft-reacting at least one maleic acid compound with an aromatic vinyl compound/conjugated diene compound block copolymer containing at least one polymer block mainly composed of a conjugated diene compound and at least one polymer block mainly composed of an aromatic vinyl compound, the aromatic vinyl compound/conjugated diene compound weight ratio being within the range of 5/95 to 97/3, characterized in that said graft-reaction is carried out under conditions wherein the generation of radicals can be substantially inhibited. According to this process, it is possible to prevent gelation of the product in the graft-reaction, and the modified block copolymer obtained has excellent appearance characteristics, mechanical properties, and transparency.
Inventors
- 👤 Akira Saito
- 👤 Akio Yamori
- 👤 Toshio Ibaragi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:31
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/46
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
158 words
A process for preparing a modified block copolymer by graft-reacting at least one maleic acid compound with an aromatic vinyl compound-conjugated diene compound block copolymer containing at least one polymer block mainly composed of a conjugated diene compound at least one polymer block mainly composed of an aromatic vinyl compound, the aromatic vinyl compound/conjugated diene compound weight ratio being within the range of from 5/95 to 97/3, characterized in that said graft reaction is carried out by melt-mixing said block copolymer and maleic acid compound in the presence of a radical inhibitor without using any radical initiator while adjusting reaction temperatures and times wherein the generation of radicals can be substantially inhibited to obtain a modified block copolymer grafted with a maleic acid compound having a toluene insolubles content of not more than 1% by weight, and a ratio of melt flow index of said modified block copolymer to that of the block copolymer before modification of 0.025-2.0.
Claim 2
Dependent Claim
158 words
A process for preparing a modified block copolymer by graft-reacting at least one maleic acid compound with an aromatic vinyl compound-conjugated diene compound block copolymer containing at least one polymer block mainly composed of a conjugated diene compound at least one polymer block mainly composed of an aromatic vinyl compound, the aromatic vinyl compound/conjugated diene compound weight ratio being within the range of from 5/95 to 97/3, characterized in that said graft reaction is carried out by melt-mixing said block copolymer and maleic acid compound in the presence of a radical inhibitor without using any radical initiator while adjusting reaction temperatures and times wherein the generation of radicals can be substantially inhibited to obtain a modified block copolymer grafted with a maleic acid compound having a toluene insolubles content of not more than 1% by weight, and a ratio of melt flow index of said modified block copolymer to that of the block copolymer before modification of 0.025-2.0.
Claim 3
Dependent Claim
41 words
A process according to claim 1, wherein the aromatic vinyl compound-conjugated diene compound block copolymer contains at least two polymer blocks mainly composed of an aromatic vinyl compound and at least one polymer block mainly composed of a conjugated diene compound.
Claim 4
Dependent Claim
38 words
A process according to claim 1, wherein the weight ratio of the aromatic vinyl compound to the conjugated diene compound in the aromatic vinyl compound-conjugated diene compound block copolymer is within the range of from 10/90 to 90/10.
Claim 5
Dependent Claim
38 words
A process according to claim 1, wherein the weight ratio of the aromatic vinyl compound to the conjugated diene compound in the aromatic vinyl compound-conjugated diene compound block copolymer is within the range of from 20/80 to 85/15.
Claim 6
Dependent Claim
29 words
A process according to claim 1, wherein the number average molecular weight of the aromatic vinyl compound-conjugated diene compound block copolymer is within the range of 10,000 to 1,000,000.
Claim 7
Dependent Claim
28 words
A process according to claim 1, wherein the number-average molecular weight of the aromatic vinyl compound-conjugated diene compound block copolymer is within the range of 20,000 to 300,000.
Claim 8
Dependent Claim
20 words
A process according to claim 1, wherein the aromatic vinyl compound-conjugated diene compound block copolymer is a styrene-butadiene block copolymer.
Claim 9
Dependent Claim
38 words
A process according to claim 1, wherein the graft-reaction is carried out in the presence of a radical inhibitor in an amount of 0.001 to 5 parts by weight per 100 parts by weight of the block copolymer.
Claim 10
Dependent Claim
38 words
A process according to claim 1, wherein the graft-reaction is carried out in the presence of a radical inhibitor in an amount of 0.05 to 2 parts by weight per 100 parts by weight of the block copolymer.
Claim 11
Dependent Claim
34 words
A process according to claim 1, wherein the radical inhibitor is at least one member selected from the group consisting of phenol compounds, phosphorus compounds, naphthol compounds, amine compounds, quinone compounds and sulfur compounds.
Claim 12
Dependent Claim
33 words
A process according to claim 1, wherein the radical inhibitor is a combination of at least two compounds selected from phenol compounds, phosphorus compounds, naphthol compounds, amine compounds, quinone compounds and sulfur compounds.
Claim 13
Dependent Claim
37 words
A process according to claim 1, wherein the radical inhibitor is a combination of one compound selected from phenol compounds and phosphorus compounds with one compound selected from naphtol compounds, amine compounds, quinone compounds and sulfur compounds.
Claim 14
Dependent Claim
40 words
A process according to claim 1, wherein the radical inhibitor is a combination of one compound selected from phenol compounds, one compound selected from phosphorus compounds and one compound selected from naphthol compounds, quinone compounds, amine compounds and sulfur compounds.
Claim 15
Dependent Claim
34 words
A process according to claim 10, 11, 12 or 13, wherein the amine compound is selected from the group consisting of naphthylamine compounds, phenylenediamine compounds, mercaptoalkylamine compounds, N-nitrosoamine compounds, quinoline compounds and phenothiazine compounds.
Claim 16
Dependent Claim
16 words
A process according to claim 10, 11, 12 or 13, wherein the amine compound is phenothiazine.
Claim 17
Dependent Claim
17 words
A process according to claim 9, wherein the graft reaction is carried out in a screw extruder.
Claim 18
Dependent Claim
11 words
A modified block copolymer prepared by the process of claim 1.
Claim 19
Dependent Claim
11 words
A modified block copolymer prepared by the process of claim 2.
Claim 20
Dependent Claim
11 words
A modified block copolymer prepared by the process of claim 3.
Claim 21
Dependent Claim
11 words
A modified block copolymer prepared by the process of claim 5.
Claim 22
Dependent Claim
11 words
A modified block copolymer prepared by the process of claim 7.
Claim 23
Dependent Claim
11 words
A modified block copolymer prepared by the process of claim 12.
Claim 24
Dependent Claim
11 words
A modified block copolymer prepared by the process of claim 13.
References Cited (Backward Citations)
US3714295A
Cited
US4033888A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-28 | 1985-03-30 | 1985-09-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-28 | 1989-03-30 | 1989-09-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-28 | 1993-03-30 | 1993-09-29 | $7700.00 | Window Closed / Lapsed |