Metallizing paste for circuit board having low thermal expansion coefficient
Assignee: Niterra Co Ltd
•
Filing: 1988-03-04
•
Granted: 1990-10-16
•
Expires: 2008-03-04
Abstract
Abstract Metallizing paste is composed, by weight, of 100 parts of Pt, 0.5 to 5 parts of Ag, 0.1 to 1 part of CuO, and 2 to 10 parts of a low thermal expansion fritt, which may also contain up to 100 parts of Au. Another metallizing paste is composed, by weight, of 100 parts of Pd, 0.5 to 4 parts of Ag, 0.1 to 1 part of CuO, and 1 to 10 parts of a low thermal expansion fritt, which may also contain up to 50 parts of Au. A low thermal expansion circuit board with multi-layers is made up to a low thermal expansion substrate such as crystallized glass, A1N, SiC, Si 3 N 4 etc. and metallized layers formed on the surface of the substrate based on the abovementioned metallizing pastes comprising crystallized glass type materials.
Inventors
- 👤 Kazuo Kondo
- 👤 Asao Morikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:55
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/60; H10W70/62; H10W70/66; H10W70/666; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
36 words
Metallizing paste consisting essentially of 100 parts of Pt, 0.5 to 5 parts of Ag, 0.1 to 1 part of CuO, and 2 to 10 parts of a low thermal expansion frit, all being by weight.
Claim 2
Dependent Claim
36 words
Metallizing paste consisting essentially of 100 parts of Pt, 0.5 to 5 parts of Ag, 0.1 to 1 part of CuO, and 2 to 10 parts of a low thermal expansion frit, all being by weight.
Claim 3
Dependent Claim
38 words
Metallizing paste as set forth in claim 1, wherein Ag ranges from 1 to 5 parts, CuO ranges from 0.3 to 0.7 part, and the low thermal expansion frit ranges from 3 to 8 parts, all by weight.
Claim 4
Dependent Claim
47 words
Metallizing paste for low thermal expansion substrates consisting essentially of 100 parts of Pt, 100 parts or below of Au, 0.5 to 5 parts of Ag, 0.1 to 1 part of CuO, and 2 to 10 parts of a low thermal expansion frit, all being by weight.
Claim 5
Dependent Claim
47 words
Metallizing paste for low thermal expansion substrates consisting essentially of 100 parts of Pt, 100 parts or below of Au, 0.5 to 5 parts of Ag, 0.1 to 1 part of CuO, and 2 to 10 parts of a low thermal expansion frit, all being by weight.
Claim 6
Dependent Claim
45 words
Metallizing paste as set forth in claim 3, wherein Au ranges from 10 to 50 parts, Ag ranges from 1 to 5 parts, CuO ranges from 0.3 to 0.7 part, and the low thermal expansion frit ranges from 3 to 8 parts, all by weight.
Claim 7
Dependent Claim
36 words
Metallizing paste consisting essentially of 100 parts of Pd, 0.5 to 4 parts of Ag, 0.1 to 1 part of CuO, and 1 to 10 parts of a low thermal expansion frit all being by weight.
Claim 8
Dependent Claim
36 words
Metallizing paste consisting essentially of 100 parts of Pd, 0.5 to 4 parts of Ag, 0.1 to 1 part of CuO, and 1 to 10 parts of a low thermal expansion frit all being by weight.
Claim 9
Dependent Claim
38 words
Metallizing paste as set forth in claim 5, wherein Ag ranges from 1 to 3 parts, CuO ranges from 0.3 to 0.7 part, and the low thermal expansion frit ranges from 3 to 8 parts, all by weight.
Claim 10
Dependent Claim
42 words
Metallizing paste consisting essentially of 100 parts of Pd, 50 parts or below of Au, 0.5 to 4 parts of Ag, 0.1 to 1 part of CuO, and 1 to 10 parts of a low thermal expansion frit, all being by weight.
Claim 11
Dependent Claim
42 words
Metallizing paste consisting essentially of 100 parts of Pd, 50 parts or below of Au, 0.5 to 4 parts of Ag, 0.1 to 1 part of CuO, and 1 to 10 parts of a low thermal expansion frit, all being by weight.
Claim 12
Dependent Claim
45 words
Metallizing paste as set forth in claim 7, wherein Au ranges from 10 to 30 parts, Ag ranges from 1 to 3 parts, CuO ranges from 0.3 to 0.7 part, and the low thermal expansion frit ranges from 3 to 8 parts, all by weight
Claim 13
Dependent Claim
60 words
Metallizing paste as set forth in claim 1 or 3, wherein the particle size of each powder material for the paste components ranges from 0.2 to 3.5 μm for Pt, from 0.2 to 3 μm for Au, from 2 to 10 μm for Ag, from 2 to 4 μm for CuO, and from 2 to 3 μm for the frit.
Claim 14
Dependent Claim
58 words
Metallizing paste as set forth in claim 5 or 7, wherein the particle size of each powder material for the paste components ranges from 0.2 to 10 μm for Pd, 0.2 to 3 μm for Au, 2 to 10 μm for Ag, from 2 to 4 μm for CuO, and from 2 to 3 μm for the frit.
Claim 15
Dependent Claim
48 words
Metallizing paste as set forth in any one of claims 1, 3, 5 and 7, wherein said low thermal expansion frit is a crystallized glass material or a composite material of a crystallized glass material and a ceramic material (both being referred to as "crystallized glass type material").
Claim 16
Dependent Claim
36 words
Metallizing paste as set forth in claim 11, wherein the thermal expansion coefficient of said crystallized glass type material is 5 to 45×10 -7 /° C. within a temperature range from room temperature to 400° C.
Claim 17
Dependent Claim
36 words
Metallizing paste as set forth in claim 12, wherein the thermal expansion coefficient of said crystallized glass type material is 15 to 45×10 -7 ° C. within a temperature range from room temperature to 400° C.
Claim 18
Dependent Claim
36 words
Metallizing paste as set forth in claim 13, wherein the thermal expansion coefficient of said crystallized glass type materials is 25 to 45×10 -7 /° C. within a temperature range from room temperature to 400° C.
Claim 19
Dependent Claim
36 words
Metallizing paste as set forth in claim 13, wherein the thermal expansion coefficient of said crystallized glass type materials is 15 to 35×10 -7 /° C. within a temperature range from room temperature to 400° C.
Claim 20
Dependent Claim
63 words
Metallizing paste as set forth in any one of claims 1, 3, 5 and 7 wherein said crystallized glass is selected from the group generally expressed by a formula RO--Al 2 O 3 --SiO 2 where RO represents ZnO, MgO, Li 2 O, Y 2 O 3 , ZrO 2 , CaO, BaO, B 2 O 3 or P 2 O 5 .
Claim 21
Dependent Claim
64 words
Metallizing paste as set forth in claim 16, wherein said crystallized glass in selected from the group consisting of ZnO--MgO--Al 2 O 3 --SiO 2 , Cao--B 2 O 3 --MgO--Al 2 O 3 --SiO 2 , Y 2 O 3 --MgO--Al 2 O 3 --SiO 2 , Li 2 O--A1 2 O 3 --SiO 2 and BaO--Al 2 O 3 --SiO 2 .
Claim 22
Dependent Claim
48 words
Metallizing paste as set forth in claim 16, wherein said crystallized glass is composed of, by weight, 57-63% SiO 2 , 20-28% Al 2 O 3 , 10-18% MgO, 2-6% ZnO and 0.1-6% of at least one of B 2 O 3 and P 2 O 5 .
Claim 23
Dependent Claim
42 words
Metallizing paste as set forth in claim 16, wherein said crystallized glass is composed of, by weight, 40-52% SiO 2 , 27-37% Al 2 O 3 , 10-20% MgO, 2-8% B 2 O 3 , 2-8% CaO, and 0.1-3% ZrO 2 .
Claim 24
Dependent Claim
52 words
Metallizing paste as set forth in claim 16, wherein said crystallized glass is composed of, by weight, 55-63% SiO 2 , 20-28% Al 2 O 3 , 1-8% Y 2 O 3 , 10-20% MgO and 0.1-5% of at least one of B 2 O 3 and P 2 O 5 .
Claim 25
Dependent Claim
32 words
Metallizing paste as set forth in claim 16, wherein said crystallized glass is of a ZnO--MgO--Al 2 O 3 --SiO 2 system and, when crystallized, has a major crystallite phase of cordierite.
Claim 26
Dependent Claim
29 words
Metallizing paste as set forth in claim 16, wherein said crystallized glass contains up to 60% by volume of fine ceramic particles coated with a thin SiO 2 film.
Claim 27
Dependent Claim
31 words
Metallizing paste as set forth in claim 22, wherein said ceramic particles are selected from the group consisting of Al 2 O 3 , BN and Si 3 N 4 .
Claim 28
Dependent Claim
29 words
Metallizing paste as set forth in claim 1, wherein Pd is further present in an amount such that the sum of Pt and Pd makes 100 parts by weight.
Claim 29
Dependent Claim
20 words
Metallizing paste as set forth in claim 1 or 3, wherein Ag is no more than 4 parts by weight.
Claim 30
Dependent Claim
41 words
A low thermal expansion circuit board comprising a low thermal expansion substrate and at least one metallized layer formed on the surface of said substrate based on the metallizing paste defined by any one of claims 1, 3, 5 and 7.
Claim 31
Dependent Claim
23 words
The circuit board as set forth in claim 26, wherein said metallized layer has a thickness of about 5 to about 40 μm.
Claim 32
Dependent Claim
23 words
The circuit board as set forth in claim 27, wherein said metallized layer has a thickness of about 10 to about 20 μm.
Claim 33
Dependent Claim
46 words
The low thermal expansion circuit board as set forth in claim 26, wherein said low thermal expansion substrate is made of one selected from the group consisting of crystallized glass materials, SiC, Si 3 N 4 , AlN and composite materials of crystallized glass and ceramics.
Claim 34
Dependent Claim
34 words
The low thermal expansion circuit board as set forth in claim 29, wherein said low thermal expansion substrate is made of the same material as the low thermal expansion frit of the metallizing paste.
Claim 35
Dependent Claim
25 words
The low thermal expansion circuit board as set forth in claim 26, wherein said metallized layer is bonded with lead wires through a brazing material.
Claim 36
Dependent Claim
22 words
The low thermal expansion circuit board as set forth in claim 31, wherein said brazing material is a high temperature brazing material.
Claim 37
Dependent Claim
23 words
The low thermal expansion circuit board as set forth in claim 32, wherein said high temperature brazing material is a pure silver braze.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-15 | 1994-04-16 | 1994-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-15 | 1998-04-16 | 1998-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-15 | 2002-04-16 | 2002-10-16 | $7700.00 | Window Closed / Lapsed |