Method for manufacturing superconducting ceramics in a magnetic field
Assignee: Semiconductor Energy Laboratory Co Ltd
•
Filing: 1988-09-20
•
Granted: 1990-09-11
•
Expires: 2008-09-20
Abstract
Abstract A method and an apparatus for fabricating single crystals of superconducting ceramics are described. A powedered row oxide mixture is placed and molten in a melting pot. The surface of the molten mixture is approximately at the freezing point of the mixture. From the surface, a single crystal is pulled in accordance with the known pulling crystal technique. The pulled mixture is subjected to a magnetic field normal to the pulling direction. By virtue of the magnetic field, single crystal superconducting oxide ceramics can be obtained without twin crystals.
Inventors
- 👤 Shunpei Yamazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:41
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; Y; Y10; Y10S; Y10S420/00; Y10S420/901; Y10S505/00; Y10S505/725; Y10S505/729; Y10T; Y10T117/00; Y10T117/10; Y10T117/1024; Y10T117/1032
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
53 words
A method of fabricating single crystals of superconducting ceramics comprising: melting a magnetic copper based oxide mixture conforming to a composition required for superconduction; applying a magnetic field to said molten oxide mixture in a fixed direction; freezing said molten mixture in said magnetic field and then forming a superconducting ceramic single crystal.
Claim 2
Independent Claim
53 words
A method of fabricating single crystals of superconducting ceramics comprising: melting a magnetic copper based oxide mixture conforming to a composition required for superconduction; applying a magnetic field to said molten oxide mixture in a fixed direction; freezing said molten mixture in said magnetic field and then forming a superconducting ceramic single crystal.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein said freezing step is carried out in accordance with the pulling crystal technique.
Claim 4
Dependent Claim
18 words
The method of claim 1 further comprising the step of aggitating said molten mixture during said freezing step.
Claim 5
Dependent Claim
20 words
The method of claim 2 wherein said magnetic field is applied across the pulled crystal in a perpendicular direction thereto.
Claim 6
Dependent Claim
19 words
The method of claim 2 wherein said magnetic field is perpendicular to the C plane of said single crystal.
Claim 7
Dependent Claim
18 words
The method of claim 2 wherein the direction of said magnetic field is rotated about the pulling direction.
Claim 8
Dependent Claim
16 words
The method of claim 2 further comprising the step of supplying oxygen into said molten mixture.
Claim 9
Dependent Claim
32 words
The method of claim 2 wherein the seed crystal used for said pulling crystal technique is oriented so that the growth direction of said superconducting crystal is normal to the C plane.
Claim 10
Dependent Claim
21 words
The method of claim 3 wherein said aggitating step is performed by applying a rotating magnetic field to the molten mixture.
References Cited (Backward Citations)
JPS51690A
Cited
US4622211A
Cited
GB2109267A
Cited
US4592895A
Cited
US4565671A
Cited
US4830703A
Cited
US4659423A
Cited
JPH03210092A
Cited
JPH075188A
Cited
JPH08990A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-10 | 1994-03-12 | 1994-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-10 | 1998-03-12 | 1998-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-10 | 2002-03-12 | 2002-09-11 | $7700.00 | Window Closed / Lapsed |