Non-consumable anode for molten salt electrolysis
Assignee: Moltech Invent SA
•
Filing: 1988-08-30
•
Granted: 1990-09-11
•
Expires: 2008-08-30
Abstract
Abstract A non-consumable anode of the type comprising an oxide ceramic coating on a metal substrate, for molten salt electrolysis, namely the electrowinning of metals such as aluminum, has an electronically-conductive oxygen barrier layer between the oxide ceramic coating and the substrate, the oxygen barrier layer containing chromium oxide. Usually, the oxygen barrier layer is a surface film integral with a chromium-containing alloy substrate, comprising 10 to 30% by weight of chromium, 55 to 90% of nickel, cobalt and/or iron and up to 15% of aluminum, titanium, zirconium, yttrium, hafnium or niobium. The ceramic oxide coating may comprise copper oxide in solid solution with at least one further oxide; nickel ferrite; copper oxide and nickel ferrite; doped, non-stoichiometric or partially substituted spinels; or rare earth metal oxides or oxyfluorides.
Inventors
- 👤 Thinh Nguyen
- 👤 Abdelkrim Lazouni
- 👤 Kim S. Doan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:06
CPC Classifications
C; C25; C25C; C25C7/00; C25C7/06; C23; C23C; C23C26/00; C25C3/00; C25C3/06; C25C3/08; C25C3/12; C25C7/02; C25C7/025
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
102 words
An anode for electrowinning aluminum from molten salt electrolytes, and which, in use, is a substrate for a coating formed or maintained in-situ in the molten electrolyte, the anode comprising an oxide ceramic coating applied on a metal, alloy or cermet substrate, and an electronically-conductive oxygen barrier layer between the oxide ceramic coating and the substrate, the oxygen barrier layer containing chromium oxide, and the oxide ceramic coating which swerves as anchorage for said in-situ coating comprising copper oxide in solid solution with at least one further oxide; nickel ferrite; copper oxide and nickel ferrite; or doped, non-stoichiometric or partially substituted spinel.
Claim 2
Dependent Claim
102 words
An anode for electrowinning aluminum from molten salt electrolytes, and which, in use, is a substrate for a coating formed or maintained in-situ in the molten electrolyte, the anode comprising an oxide ceramic coating applied on a metal, alloy or cermet substrate, and an electronically-conductive oxygen barrier layer between the oxide ceramic coating and the substrate, the oxygen barrier layer containing chromium oxide, and the oxide ceramic coating which swerves as anchorage for said in-situ coating comprising copper oxide in solid solution with at least one further oxide; nickel ferrite; copper oxide and nickel ferrite; or doped, non-stoichiometric or partially substituted spinel.
Claim 3
Dependent Claim
21 words
The anode of claim 1, in which the oxygen barrier layer is a surface film integral with a chromium-containing alloy substrate.
Claim 4
Dependent Claim
44 words
The anode of claim 2, in which the substrate is an alloy comprising 10 to 30% by weight of chromium, 55 to 90% of one or more of nickel, cobalt or iron and up to 15% of aluminum, titanium, zirconium, yttrium, hafnium or niobium.
Claim 5
Dependent Claim
29 words
The anode of claim 1, in which the oxygen barrier layer is a separate layer of chromium oxide applied to the surface of the metal, alloy or cermet substrate.
Claim 6
Dependent Claim
34 words
The anode of claim 1, in which the oxide ceramic coating contains an oxidized metal which is present in the substrate, in combination with an oxidized metal which is not present in the substrate.
Claim 7
Dependent Claim
27 words
The anode of claim 1, in which the oxide ceramic coating comprises copper oxide in solid solution with an oxide of nickel or an oxide of manganese.
Claim 8
Dependent Claim
31 words
The anode of claim 1, in which the oxide ceramic coating further contains at least one non-oxidized precious metal in an amount of up to 30% by weight of the coating.
Claim 9
Dependent Claim
92 words
A method of manufacturing the anode of claim 1 comprising: (a) providing on the metal, alloy or cermet substrate a surface layer containing one or more of chromium metal or chromium oxide; (b) applying to said surface layer the oxide ceramic coating, or a precursor of the oxide ceramic coating of claim 1; and (c) heating the resulting anode in an oxidizing atmosphere when needed to convert chromium metal in said surface layer to chromium oxide or the convert the ceramic oxide precursor into the ceramic oxide coating, or to convert both.
Claim 10
Dependent Claim
58 words
The method of claim 8, in which the oxygen barrier layer containing chromium oxide is produced by in-situ oxidation of a surface layer of a metal, alloy or cermet substrate containing chromium metal by heating in an oxidizing atmosphere after application to said surface layer of the oxide ceramic coating or a precursor of the oxide ceramic coating.
Claim 11
Dependent Claim
32 words
The method of claim 8, in which a protective layer of cerium oxyfluoride is applied to the oxide ceramic coating by polarizing the anode in a molten electrolyte containing a cerium species.
Claim 12
Dependent Claim
15 words
A method of electrowinning aluminum from molten salt electrolytes using the anode of claim 1.
Claim 13
Dependent Claim
21 words
A cell for electrowinning a metal from a molten salt electrolyte, comprising at least one anode as claimed in claim 1.
References Cited (Backward Citations)
US2548514A
Cited
US4024294A
Cited
US4157943A
Cited
WO1981002027A1
Cited
US4374050A
Cited
US4374761A
Cited
US4399008A
Cited
US4478693A
Cited
EP0114085A2
Cited
US4614569A
Cited
US4620905A
Cited
EP0257708A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-10 | 1994-03-12 | 1994-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-10 | 1998-03-12 | 1998-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-10 | 2002-03-12 | 2002-09-11 | $7700.00 | Window Closed / Lapsed |