Process for the leakproof joining of ceramic sealing disks to metallic attachments
Assignee: Ceramtec GmbH
•
Filing: 1989-03-23
•
Granted: 1990-09-11
•
Expires: 2009-03-23
Abstract
Abstract A process for the leakproof joining of a ceramic sealing disk, which regulates the passage of a fluid, and metallic attachments which are presented to the disk, wherein a roughly finished ceramic disk is metallized at the points that are to be joined to the metallic attachment (for example, a copper pipe with flanged-on collar) and soldered at the metallized points to the metallic attachment. The metallic attachment may also be joined to the ceramic sealing disk without prior metallization if an active solder is used. In one embodiment, the sliding and sealing face is produced on the side of the disk facing away from the metallic attachment by grinding and/or lapping and/or polishing. Alternatively, the sliding and sealing face can also be first produced on the roughly finished sealing disk by grinding and/or lapping and/or polishing and joined to the metallic attachment by applying the metallization and soldering, or by active soldering, and then cooling at a rate of more than 30 K/min.
Inventors
- 👤 Helmut Stuhler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:59
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/02; C04B37/023; C04B37/026; C04B2235/00; C04B2235/65; C04B2235/656; C04B2235/6565; C04B2237/00; C04B2237/02; C04B2237/12; C04B2237/122; C04B2237/123; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/40; C04B2237/405; C04B2237/406; C04B2237/407; C04B2237/50; C04B2237/70; C04B2237/704; C04B2237/708; C04B2237/72; C04B2237/76; C04B2237/765; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4935; Y10T29/49393; Y10T29/49405; Y10T29/49412; Y10T29/49416; Y10T29/49421
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
104 words
A process for the leakproof joining of a ceramic sealing disk having at least one opening with at least one metallic pipe having an opening, comprising the steps of: (A) contacting together with solder the metallic pipe and a first face of the roughly finished sealing disk such that the opening of the metallic pipe corresponds to the opening in the sealing disk; then (B) heating the pipe, disk and solder to the melting temperature of the solder; and (C) thereafter producing by grinding, lapping or polishing a sliding and sealing second face on the sealing disk opposite the first face contacting the pipe.
Claim 2
Dependent Claim
104 words
A process for the leakproof joining of a ceramic sealing disk having at least one opening with at least one metallic pipe having an opening, comprising the steps of: (A) contacting together with solder the metallic pipe and a first face of the roughly finished sealing disk such that the opening of the metallic pipe corresponds to the opening in the sealing disk; then (B) heating the pipe, disk and solder to the melting temperature of the solder; and (C) thereafter producing by grinding, lapping or polishing a sliding and sealing second face on the sealing disk opposite the first face contacting the pipe.
Claim 3
Dependent Claim
33 words
The process as claimed in claim 1, wherein prior to step (A) the first face of the roughly finished sealing disk is metallized in an area that is to contact the metallic pipe.
Claim 4
Dependent Claim
26 words
The process as claimed in claim 1, wherein the roughly finished sealing disk is soldered directly to the metallic pipe by means of an active solder.
Claim 5
Dependent Claim
22 words
The process as claimed in claim 2, wherein the metallic pipe is joined to the metallized ceramic sealing disk by soft soldering.
Claim 6
Dependent Claim
22 words
The process as claimed in claim 2, wherein the metallic pipe is joined to the metallized ceramic sealing disk by hard soldering.
Claim 7
Dependent Claim
19 words
The process as claimed in claim 1, wherein the metal of the metallic pipe is copper, iron-nickel or iron-nickel-cobalt.
Claim 8
Dependent Claim
23 words
The process as claimed in claim 1, wherein the metallic pipe has a collar-shaped flange at the end at which it is soldered.
Claim 9
Dependent Claim
23 words
The process as claimed in claim 1, wherein the metallic pipe has a collar-shaped flange at the end of which it is soldered.
Claim 10
Dependent Claim
30 words
The process as claimed in claim 1, wherein the roughly finished sealing disk is such that the sliding and sealing face is only roughly ground flat prior to step (A).
Claim 11
Dependent Claim
124 words
A process for the leakproof joining of a ceramic sealing disk having at least one opening with at least one metallic pipe having an opening, comprising the steps of: (A) producing by grinding, lapping or polishing a sliding and sealing first face on the roughly finished sealing disk; then (B) contacting together with solder the metallic pipe and a second face of the sealing disk opposite the sliding and sealing first face such that the opening of the metallic pipe corresponds to the opening in the sealing disk; then (C) heating the pipe, disk and solder to the melting temperature of the solder; and (D) thereafter cooling the pipe, disk and solder to ambient temperature at a rate of not more than 30 K/min.
Claim 12
Dependent Claim
124 words
A process for the leakproof joining of a ceramic sealing disk having at least one opening with at least one metallic pipe having an opening, comprising the steps of: (A) producing by grinding, lapping or polishing a sliding and sealing first face on the roughly finished sealing disk; then (B) contacting together with solder the metallic pipe and a second face of the sealing disk opposite the sliding and sealing first face such that the opening of the metallic pipe corresponds to the opening in the sealing disk; then (C) heating the pipe, disk and solder to the melting temperature of the solder; and (D) thereafter cooling the pipe, disk and solder to ambient temperature at a rate of not more than 30 K/min.
Claim 13
Dependent Claim
44 words
The process as claimed in claim 10, wherein prior to step (B) a metallization is applied to an area of the second face of the disk that is to contact the metallic pipe and the disk is cooled at not more than 30 K/min.
Claim 14
Dependent Claim
23 words
The process as claimed in claim 10, wherein the sealing disk is soldered to the metallic pipe by means of an active solder.
Claim 15
Dependent Claim
22 words
The process as claimed in claim 11, wherein the metallic pipe is joined to the metallized ceramic sealing disk by soft soldering.
Claim 16
Dependent Claim
22 words
The process as claimed in claim 11, wherein the metallic pipe is joined to the metallized ceramic sealing disk by hard soldering.
Claim 17
Dependent Claim
19 words
The process as claimed in claim 10, wherein the metal of the metallic pipe is copper, iron-nickel or iron-nickel-cobalt.
Claim 18
Dependent Claim
23 words
The process as claimed in claim 10, wherein the metallic pipe has a collar-shaped flange at the end at which it is soldered.
Claim 19
Dependent Claim
30 words
The process as claimed in claim 10, wherein the roughly finished sealing disk is such that the sliding and sealing face is only roughly ground flat prior to step (A).
References Cited (Backward Citations)
DE131145C
Cited
US3901772A
Cited
US3874635A
Cited
US4111178A
Cited
US4420142A
Cited
EP0110336A1
Cited
US4575047A
Cited
DE3509520A1
Cited
US4736772A
Cited
JPH021171A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-10 | 1994-03-12 | 1994-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-10 | 1998-03-12 | 1998-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-10 | 2002-03-12 | 2002-09-11 | $7700.00 | Window Closed / Lapsed |