Composite alloy steel powder and sintered alloy steel
Assignee: JFE Steel Corp
•
Filing: 1988-09-30
•
Granted: 1990-09-04
•
Expires: 2008-09-30
Abstract
Abstract Provided herein are high-strength high-toughness sintered alloy steel and composite alloy steel powder useful for the production thereof. The sintered alloy steel contains, as the alloy components in the final product, Ni, Mo, and/or W, and C, if necessary, said alloy being composed of 0.50-3.50 wt % of Ni, 0.65-3.50 wt % of Mo+1/2W, (and 0.3-0.8 wt % of C, if necessary), and the remainder of Fe and inevitable impurities, and has a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering. The composite alloy steel powder is composed of iron powder particles and powdery alloy components attached by diffusion to part of the surface of the iron powder particles, with the content of Ni and the content of Mo+1/2W in the steel powder of particle diameter smaller than 45 ∞m being in the range of 2.0-4.2 times the average content in the entire steel powder. The sintered alloy steel has high strength and high toughness despites its comparatively low alloy composition and can be produced without any special equipment. The heat-treated sintered steel meets the requirements for automotive parts and the like.
Inventors
- 👤 Shigeaki Takajo
- 👤 Osamu Furukimi
- 👤 Kuniaki Ogura
- 👤 Keiichi Maruta
- 👤 Teruyoshi Abe
- 👤 Ichio Sakurada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:22
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0264; C22C33/0207; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12181
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
106 words
A composite alloy steel powder for powder metallurgy composed of iron powder particles and powdery alloy components attached by diffusion to parts of the surfaces of the iron powder particles, which comprises Ni and Mo as alloy components, said alloy powder comprising 0.05-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo, and the remainder of Fe and inevitable impurities, wherein the content of Ni and the content of Mo in the particles of alloy steel powder which have particle diameters smaller than 45 μm are in the range of 2.0-4.2 times the average content of Ni and of Mo in the entire alloy steel powder.
Claim 2
Dependent Claim
106 words
A composite alloy steel powder for powder metallurgy composed of iron powder particles and powdery alloy components attached by diffusion to parts of the surfaces of the iron powder particles, which comprises Ni and Mo as alloy components, said alloy powder comprising 0.05-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo, and the remainder of Fe and inevitable impurities, wherein the content of Ni and the content of Mo in the particles of alloy steel powder which have particle diameters smaller than 45 μm are in the range of 2.0-4.2 times the average content of Ni and of Mo in the entire alloy steel powder.
Claim 3
Dependent Claim
71 words
A high-strength sintered alloy steel which comprises Ni and Mo together with Fe as alloy components in the final product, said alloy steel being composed of 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo, and the remainder of Fe, C, and inevitable impurities, and said sintered alloy steel having a density higher than 7.09 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 4
Dependent Claim
71 words
A high-strength sintered alloy steel which comprises Ni and Mo together with Fe as alloy components in the final product, said alloy steel being composed of 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo, and the remainder of Fe, C, and inevitable impurities, and said sintered alloy steel having a density higher than 7.09 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 5
Dependent Claim
75 words
A high-strength high-toughness sintered alloy steel which comprises C, Ni and Mo as alloy components together with Fe in the final product, said alloy being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo, and the remainder of Fe and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 6
Dependent Claim
75 words
A high-strength high-toughness sintered alloy steel which comprises C, Ni and Mo as alloy components together with Fe in the final product, said alloy being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo, and the remainder of Fe and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 7
Dependent Claim
80 words
A high-strength sintered alloy steel produced from the composite alloy steel powder defined in claim 1, which comprises Fe and Ni and Mo as alloy components in the final product, said alloy being composed of 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo, and the remainder of Fe, C, and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after carburizing quenching and tempering.
Claim 8
Dependent Claim
85 words
A high-strength high-toughness sintered alloy steel produced from the composite alloy steel powder defined in claim 1, which comprises Fe, C, Ni, and Mo as alloy components in the final product, said alloy steel being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo, and the remainder of Fe and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching or tempering.
Claim 9
Dependent Claim
103 words
A composite alloy steel powder for powder metallurgy composed of iron powder particles and powdery alloy components attached by diffusion to parts of the surfaces of the iron powder particles, which powder comprises Ni, Mo, and W as alloy components, said alloy being composed of 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo+1/2W, and the remainder of Fe and inevitable impurities, wherein the content of Ni and the content of Mo+1/2W in steel powder having particle diameters smaller than 45 μm are in the range of 2.0-4.2 times the average content of Ni and of Mo+1/2W in the entire steel powder.
Claim 10
Dependent Claim
103 words
A composite alloy steel powder for powder metallurgy composed of iron powder particles and powdery alloy components attached by diffusion to parts of the surfaces of the iron powder particles, which powder comprises Ni, Mo, and W as alloy components, said alloy being composed of 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo+1/2W, and the remainder of Fe and inevitable impurities, wherein the content of Ni and the content of Mo+1/2W in steel powder having particle diameters smaller than 45 μm are in the range of 2.0-4.2 times the average content of Ni and of Mo+1/2W in the entire steel powder.
Claim 11
Dependent Claim
71 words
A high-strength sintered alloy steel which comprises Fe together with Ni, Mo, and W as alloy components in the final product, said alloy being composed of 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo+1/2W, and the remainder of Fe, C, and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after carburizing quenching and tempering.
Claim 12
Dependent Claim
71 words
A high-strength sintered alloy steel which comprises Fe together with Ni, Mo, and W as alloy components in the final product, said alloy being composed of 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo+1/2W, and the remainder of Fe, C, and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after carburizing quenching and tempering.
Claim 13
Dependent Claim
76 words
A high-strength high-toughness sintered alloy steel which comprises Fe together with C, Ni, Mo, and W as alloy components in the final product, said alloy being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo+1/2W, and the remainder of Fe and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 14
Dependent Claim
76 words
A high-strength high-toughness sintered alloy steel which comprises Fe together with C, Ni, Mo, and W as alloy components in the final product, said alloy being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo+1/2W, and the remainder of Fe and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 15
Dependent Claim
79 words
A high-strength sintered alloy steel produced from the composite alloy steel powder defined in claim 6, which comprises Ni, Mo, and W as alloy components in the final product, said alloy being composed of 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo+1/2W, and the remainder of Fe, C, and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after carburizing quenching and tempering.
Claim 16
Dependent Claim
84 words
A high-strength high-toughness sintered alloy steel produced from the composite alloy steel powder defined in claim 6, which comprises C, Ni, Mo, and W as alloy components in the final product, said alloy being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 0.65-3.50 wt. % of Mo+1/2W, and the remainder of Fe and said alloy steel inevitable impurities, and having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 17
Dependent Claim
103 words
A composite alloy steel powder for powder metallurgy composed of iron powder particles and powdery alloy components attached by diffusion to parts of the surfaces of the iron powder particles, which powder comprises Ni and W as alloy components, said alloy being composed of 0.50-3.50 wt. % of Ni, 1.30-7.00 wt. % of W, and the remainder of Fe and inevitable impurities, wherein the content of Ni and the content of W in the steel powder which have particle diameters smaller than 45 μm being in the range of 2.0-4.2 times the average content of Ni and W in the entire steel powder.
Claim 18
Dependent Claim
103 words
A composite alloy steel powder for powder metallurgy composed of iron powder particles and powdery alloy components attached by diffusion to parts of the surfaces of the iron powder particles, which powder comprises Ni and W as alloy components, said alloy being composed of 0.50-3.50 wt. % of Ni, 1.30-7.00 wt. % of W, and the remainder of Fe and inevitable impurities, wherein the content of Ni and the content of W in the steel powder which have particle diameters smaller than 45 μm being in the range of 2.0-4.2 times the average content of Ni and W in the entire steel powder.
Claim 19
Dependent Claim
70 words
A high-strength sintered alloy steel which comprises Ni and W along with Fe as alloy components in the final product, said alloy being composed of 0.50-3.50 wt. % of Ni, 1.30-7.00 wt. % of W, and the remainder of Fe, C and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after carburizing quenching and tempering.
Claim 20
Dependent Claim
70 words
A high-strength sintered alloy steel which comprises Ni and W along with Fe as alloy components in the final product, said alloy being composed of 0.50-3.50 wt. % of Ni, 1.30-7.00 wt. % of W, and the remainder of Fe, C and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after carburizing quenching and tempering.
Claim 21
Dependent Claim
76 words
A high-strength high-toughness sintered alloy steel which comprises C, Ni, and W along with Fe as alloy components in the final product, said alloy steel being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 1.30-7.00 wt. % of W, and the remainder of Fe and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 22
Dependent Claim
76 words
A high-strength high-toughness sintered alloy steel which comprises C, Ni, and W along with Fe as alloy components in the final product, said alloy steel being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 1.30-7.00 wt. % of W, and the remainder of Fe and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
Claim 23
Dependent Claim
81 words
A high-strength sintered alloy steel produced from the composite alloy steel powder defined in claim 11, which comprises Fe together with Ni and W as alloy components in the final product, said alloy being composed of 0.50-3.50 wt. % of Ni, 1.30-7.00 wt. % of W, and the remainder of Fe, C and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after carburizing quenching and tempering.
Claim 24
Dependent Claim
87 words
A high-strength high-toughness sintered alloy steel produced from the composite alloy steel powder defined in claim 11, which comprises Fe together with Ni and W as the alloy components in the final product, said alloy steel being composed of 0.3-0.8 wt. % of C, 0.50-3.50 wt. % of Ni, 1.30-7.00 wt. % of W, and the remainder of Fe and inevitable impurities, and said alloy steel having a density higher than 7.0 g/cm 3 and a tensile strength higher than 130 kgf/mm 2 after quenching and tempering.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-03 | 1994-03-05 | 1994-09-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-03 | 1998-03-05 | 1998-09-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-03 | 2002-03-05 | 2002-09-04 | $7700.00 | Window Closed / Lapsed |