Adhesion layer for platinum based sensors
Assignee: Honeywell Inc
•
Filing: 1988-12-23
•
Granted: 1990-08-28
•
Expires: 2008-12-23
Abstract
Abstract The marginal adhesion of platinum to silicon nitride is a serious issue in the fabrication of microbridge mass air flow sensors. High temperature stabilization anneals (500°-1000° C.) are necessary to develop the properties and stability necessary for effective device operation. However, the annealing process results in a significant reduction in the already poor platinum/silicon nitride adhesion. Annealing at relatively high temperatures leads to the development of numerous structural defects and the production of non-uniform and variable sensor resistance values. The use of a thin metal oxide adhesion Layvr, approximately 20 To 100 angstromw in thickness is very effective in maintaining platinum adhesion to silicon nitride, and through the high temperature anneal sequence.
Inventors
- 👤 Robert G. Johnson
- 👤 James O. Holmen
- 👤 Ronald B. Foster
- 👤 Uppili Sridhar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:57
CPC Classifications
G; G01; G01F; G01F1/00; G01F1/68; G01F1/684; G01F1/6845; H; H01; H01C; H01C7/00; H01C7/006
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
86 words
A thin film platinum on silicon nitride sensor structure with an adhesion enhancement interlayer, the sensor structure comprising: a layer of silicon nitride having a surface on which it is desired to deposit an electrically resistive thin film layer of platinum; a thin film interlayer of a metal oxide deposited on said silicon nitride surface as an adhesion promoter for platinum; and a thin film of platinum deposited on said metal oxide interlayer whereby the metal oxide interlayer enhances the bond of platinum to silicon nitride.
Claim 2
Dependent Claim
86 words
A thin film platinum on silicon nitride sensor structure with an adhesion enhancement interlayer, the sensor structure comprising: a layer of silicon nitride having a surface on which it is desired to deposit an electrically resistive thin film layer of platinum; a thin film interlayer of a metal oxide deposited on said silicon nitride surface as an adhesion promoter for platinum; and a thin film of platinum deposited on said metal oxide interlayer whereby the metal oxide interlayer enhances the bond of platinum to silicon nitride.
Claim 3
Dependent Claim
25 words
The structure according to claim 1 in which the thin film layer of metal oxide has a thickness on the order of about 50 angstroms.
Claim 4
Dependent Claim
21 words
The structure according to claim 1 in which the thin film layer of metal oxide and of platinum are sputtered depositions.
Claim 5
Dependent Claim
29 words
The structure according to claim 1 in which the metal oxide is selected from the group consisting of chromium oxide, titanium oxide, tantalum oxide, nickel oxide, and aluminum oxide.
Claim 6
Dependent Claim
14 words
The structure according to claim 1 in which the metal oxide is chromium oxide.
Claim 7
Dependent Claim
14 words
The structure according to claim 1 in which the metal oxide is tantalum oxide.
Claim 8
Dependent Claim
14 words
The structure according to claim 1 in which the metal oxide is nickel oxide.
Claim 9
Dependent Claim
14 words
The structure according to claim 1 in which the metal oxide is aluminum oxide.
Claim 10
Dependent Claim
98 words
A thin film platinum-based sensor structure comprising: a substrate of silicon having a first surface; a thin film of silicon nitride on said silicon surface; a thin film interlayer of a metal oxide deposited on said silicon nitride as an adhesion promoter for platinum on silicon nitride; a thin film of platinum deposited on said metal oxide interlayer whereby the metal oxide interlayer enhances the bond of platinum to silicon nitride; a second thin film layer of metal oxide over said platinum; and a passivating silicon nitride layer over said second metal oxide layer and said platinum layer.
Claim 11
Dependent Claim
98 words
A thin film platinum-based sensor structure comprising: a substrate of silicon having a first surface; a thin film of silicon nitride on said silicon surface; a thin film interlayer of a metal oxide deposited on said silicon nitride as an adhesion promoter for platinum on silicon nitride; a thin film of platinum deposited on said metal oxide interlayer whereby the metal oxide interlayer enhances the bond of platinum to silicon nitride; a second thin film layer of metal oxide over said platinum; and a passivating silicon nitride layer over said second metal oxide layer and said platinum layer.
Claim 12
Dependent Claim
27 words
The structure according to claim 9 in which the thin film layer of metal oxide has a thickness in the range of about 20 to 100 angstroms.
Claim 13
Dependent Claim
19 words
The structure according to claim 9 in which the metal oxide, platinum and metal oxide layers are sputter depositions.
Claim 14
Dependent Claim
29 words
The structure according to claim 9 in which the metal oxide is selected from the group consisting of chromium oxide, titanium oxide, tantalum oxide, nickel oxide, and aluminum oxide.
Claim 15
Independent Claim
90 words
A method of fabricating a high-adhesion platinum-based sensor on a silicon nitride base comprising the steps of: providing a silicon nitride layer having a surface upon which it is desired to deposit an electrically resistive path of platinum; depositing a thin film interlayer of a metal oxide on said silicon nitride surface as an adhesion promoter for platinum; depositing a thin film of platinum on said metal oxide interlayer whereby the metal oxide interlayer enhances the bond of platinum to silicon nitride so that a high adhesion platinum layer results.
Claim 16
Independent Claim
90 words
A method of fabricating a high-adhesion platinum-based sensor on a silicon nitride base comprising the steps of: providing a silicon nitride layer having a surface upon which it is desired to deposit an electrically resistive path of platinum; depositing a thin film interlayer of a metal oxide on said silicon nitride surface as an adhesion promoter for platinum; depositing a thin film of platinum on said metal oxide interlayer whereby the metal oxide interlayer enhances the bond of platinum to silicon nitride so that a high adhesion platinum layer results.
Claim 17
Dependent Claim
20 words
The method according to claim 13 in which the depositing of metal oxide and of platinum is by sputter deposition.
Claim 18
Dependent Claim
26 words
The method according to claim 13 in which the depositing of metal oxide is to a thickness in the range of about 20 to 100 angstroms.
Claim 19
Dependent Claim
29 words
The method according to claim 13 in which the metal oxide is selected from the group consisting of chromium oxide, titanium oxide, tantalum oxide, nickel oxide, and aluminum oxide.
Claim 20
Independent Claim
117 words
A method of fabricating a high-adhesion platinum-based sensor structure, the steps comprising: providing a substrate of silicon having a thin film of silicon nitride on the surface thereof and upon which it is desired to deposit a thin film layer of platinum; depositing a thin film interlayer of a metal oxide on said silicon nitride; depositing a thin film layer of platinum on said metal oxide interlayer whereby the metal oxide interlayer enhances the bond of platinum to silicon nitride so that a high adhesion platinum layer results; depositing a second thin film interlayer of metal oxide over the platinum; and depositing a passivating silicon nitride layer over said second metal oxide layer and said platinum layer.
Claim 21
Independent Claim
117 words
A method of fabricating a high-adhesion platinum-based sensor structure, the steps comprising: providing a substrate of silicon having a thin film of silicon nitride on the surface thereof and upon which it is desired to deposit a thin film layer of platinum; depositing a thin film interlayer of a metal oxide on said silicon nitride; depositing a thin film layer of platinum on said metal oxide interlayer whereby the metal oxide interlayer enhances the bond of platinum to silicon nitride so that a high adhesion platinum layer results; depositing a second thin film interlayer of metal oxide over the platinum; and depositing a passivating silicon nitride layer over said second metal oxide layer and said platinum layer.
Claim 22
Dependent Claim
26 words
The method according to claim 17 in which the steps of depositing of metal oxide and the step of depositing of platinum is by sputter deposition.
Claim 23
Dependent Claim
26 words
The method according to claim 17 in which the depositing of metal oxide is to a thickness in the range of about 20 to 100 angstroms.
Claim 24
Dependent Claim
28 words
The method of claim 17 in which the metal oxide is selected from the group consisting of chromium oxide, titanium oxide, tantalum oxide, nickel oxide, and aluminum oxide.
Claim 25
Dependent Claim
35 words
The structure according to claim 1 in which the metal oxide is selected from the group of oxides consisting of oxides of metals of Groups III, IV, V, VI, or VIII of the Periodic Table.
Claim 26
Dependent Claim
35 words
The method according to claim 13 in which the metal oxide is selected from the group of oxides consisting of oxides of metals of Groups III, IV, V, VI, or VIII of the Periodic Table.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-27 | 1994-02-26 | 1994-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-27 | 1998-02-26 | 1998-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-27 | 2002-02-26 | 2002-08-28 | $7700.00 | Window Closed / Lapsed |