Polyurethane-forming foundry binders containing a polyester polyol
Assignee: Ashland LLC
•
Filing: 1988-10-31
•
Granted: 1990-08-07
•
Expires: 2008-10-31
Abstract
Abstract Certain polyester polyols are used in polyurethane-forming binders to improve the shakeout of molds and cores, made by a cold-box process, used to make low melting metal castings.
Inventors
- 👤 William G. Carpenter
- 👤 William R. Dunnavant
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:20
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/54; C08G18/542; B; B22; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/22; B22C1/2233; B22C1/2273; C08G18/4009; C08G18/4027
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
140 words
A foundry molding composition which comprises: A. a major amount of aggregate; and B. an effective bonding amount of a polyurethane-forming binder composition comprising: (1)phenolic resole resin component comprising: (a) a phenolic resole resin prepared by reacting formaldehyde with a phenol in a molar ratio of formaldehyde to phenol of at least 1.0 and in the presence of a divalent metal catalyst, such that the resulting resin contains polymeric structures having a preponderance of bridges joining the phenolic nuclei of the polymer which are ortho-ortho benzylic ether brides; (b) an effective amount of a polyester polyol; and (c) a solvent in which the phenolic resole resin is soluble, and such that the solvent is present in an amount of from 20 to 80 weight percent based upon the weight of the phenolic resole resin; and (2) a polyisocyanate hardener component.
Claim 2
Dependent Claim
140 words
A foundry molding composition which comprises: A. a major amount of aggregate; and B. an effective bonding amount of a polyurethane-forming binder composition comprising: (1)phenolic resole resin component comprising: (a) a phenolic resole resin prepared by reacting formaldehyde with a phenol in a molar ratio of formaldehyde to phenol of at least 1.0 and in the presence of a divalent metal catalyst, such that the resulting resin contains polymeric structures having a preponderance of bridges joining the phenolic nuclei of the polymer which are ortho-ortho benzylic ether brides; (b) an effective amount of a polyester polyol; and (c) a solvent in which the phenolic resole resin is soluble, and such that the solvent is present in an amount of from 20 to 80 weight percent based upon the weight of the phenolic resole resin; and (2) a polyisocyanate hardener component.
Claim 3
Dependent Claim
24 words
The molding composition of claim 1 wherein the binder composition is about 0.6 to 5.0 weight percent based upon the weight of the aggregate.
Claim 4
Dependent Claim
31 words
The molding composition of claim 2 wherein the phenolic resin of the phenolic resin component is prepared such that the molar ratio of aldehyde to phenol is from 1.1:1.0 to 3.9:1.0.
Claim 5
Dependent Claim
29 words
The molding composition of claim 3 wherein the phenol used to prepare the phenolic resin is selected from the group consisting of phenol, p-cresol, o-cresol, m-cresol, and mixtures thereof.
Claim 6
Dependent Claim
43 words
The molding composition of claim 4 wherein the polyester polyol is a liquid and has an average molecular weight of 300 to 800 and used in an amount of from 2.0 to 15.0 weight percent based upon the weight of the phenolic resin.
Claim 7
Dependent Claim
28 words
The molding composition of claim 4 wherein the ratio of hydroxyl groups of the phenolic resin to isocyanate groups of the polyisocyanate hardener is from 1.25:1.00 to 1.00:1.25.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-06 | 1994-02-05 | 1994-08-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-06 | 1998-02-05 | 1998-08-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-06 | 2002-02-05 | 2002-08-07 | $7700.00 | Window Closed / Lapsed |