Method of passivating crystalline substrates
Assignee: Schott Solar CSP Inc
•
Filing: 1988-06-02
•
Granted: 1990-07-31
•
Expires: 2008-06-02
Abstract
Abstract A method of bulk passivating a crystalline or polycrystalline substrate made from silicon, germanium, gallium arsenide or other III-V compounds, and II-VI compounds by exposing the substrate to a fluorine ion beam created by a Kaufman ion source. The Kaufman ion source is controlled so that the intensity of and duration of exposure to the fluorine ion beam is sufficient to bulk passivate the substrate. Preferably, the substrate is preheated to a selected temperature prior to the ion beam exposure.
Inventors
- 👤 James A. Gregory
- 👤 Jack I. Hanoka
- 👤 Zinovy Y. Vayman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:36
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/90; H10P95/904
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
106 words
A method of fabricating a solar cell comprising in sequence the steps of: (a) providing a polycrystalline silicon substrate having a p/n junction formed therein adjacent one side of the substrate, said substrate having an electrode grid on one side and an aluminum layer on the other side thereof, further wherein said one side is not coated with a layer of silicon nitride or phosphorus glass; (b) exposing said one side of the substrate to an SiF 4 ion beam of an intensity and for a duration sufficient to bulk passivate said substrate; and (c) applying an antireflection coating to said one side of said substrate.
Claim 2
Independent Claim
106 words
A method of fabricating a solar cell comprising in sequence the steps of: (a) providing a polycrystalline silicon substrate having a p/n junction formed therein adjacent one side of the substrate, said substrate having an electrode grid on one side and an aluminum layer on the other side thereof, further wherein said one side is not coated with a layer of silicon nitride or phosphorus glass; (b) exposing said one side of the substrate to an SiF 4 ion beam of an intensity and for a duration sufficient to bulk passivate said substrate; and (c) applying an antireflection coating to said one side of said substrate.
Claim 3
Dependent Claim
32 words
A method according to claim 1 further including the step of heating said silicon substrate to a temperature of between 400 ° to 800° C. prior to said ion beam exposure step.
Claim 4
Dependent Claim
19 words
A method according to claim 1 wherein said substrate is bulk passivated to a depth of about 10 microns.
Claim 5
Independent Claim
87 words
A method of fabricating a solar cell comprising in sequence the steps of: (a) providing a polycrystalline silicon substrate having a p/n junction formed therein adjacent one side of the substrate, wherein said one side is not coated with a layer of silicon nitride of phosphorus glass; (b) exposing said one side of the substrate to an SiF 4 ion beam of an intensity and for a duration sufficient to bulk passivate said substrate; and (c) applying an antireflection coating to said one side of said substrate.
Claim 6
Independent Claim
87 words
A method of fabricating a solar cell comprising in sequence the steps of: (a) providing a polycrystalline silicon substrate having a p/n junction formed therein adjacent one side of the substrate, wherein said one side is not coated with a layer of silicon nitride of phosphorus glass; (b) exposing said one side of the substrate to an SiF 4 ion beam of an intensity and for a duration sufficient to bulk passivate said substrate; and (c) applying an antireflection coating to said one side of said substrate.
Claim 7
Dependent Claim
31 words
A method according to claim 4 further including the step of heating said silicon substrate to a temperature of between 400° and 800° C. prior to said ion beam exposure step.
Claim 8
Dependent Claim
55 words
A method according to claim 4 wherein said SiF 4 ion beam is generated by a Kaufman ion source which is controlled so as operate at an intensity of between 800 to 2000 eV, with a current density of 1 to 3 mA/cm 2 , and for a duration of between 20 to 180 seconds.
References Cited (Backward Citations)
US4522663A
Cited
US4613382A
Cited
JPS59107576A
Cited
US4569697A
Cited
US4637869A
Cited
US4751191A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-30 | 1994-01-29 | 1994-07-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-30 | 1998-01-29 | 1998-07-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-30 | 2002-01-29 | 2002-07-31 | $7700.00 | Window Closed / Lapsed |