Dual ion beam deposition of amorphous semiconductor films
Assignee: Standard Oil Co
•
Filing: 1985-12-30
•
Granted: 1987-01-20
•
Expires: 2005-12-30
Abstract
Abstract A sputtering process for efficiently preparing amorphous semiconducting films having a reduced number of localized states is disclosed. In particular, hydrogenated semiconductor films free of polyhydrides may be prepared according to the inventive process. In one application of the process, a silicon target is simultaneously bombarded by separate beams of relatively heavy sputtering ions, such as argon ions, effective in sputtering the target at relatively high rates, and by ions of a substance effective in passivating localized states in amorphous semiconducting films, such as hydrogen ions. The products of this sputtering process are collected on remotely located substrates to form a passivated amorphous semiconductor film. In another application of the process, a target composed of a semiconductor alloy is used with separate sputtering and passivating ion beams directed at the target to deposit a passivated compound semiconductor film. In still another application, one pair of two pairs of sputtering and passivating ion beams are employed to sputter each of two separate elemental semiconductor targets and to deposit a passivated compound semiconductor film. Films deposited according to the invention may be doped and junction structures formed in them during deposition by adding ions of a gaseous dopant to the beam or beams of passivating ions.
Inventors
- 👤 David A. Glocker
- 👤 John R. Miller
- 👤 Scott F. Grimshaw
- 👤 Henry Windischmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 06:52
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/46; C23C14/0021; C23C14/0036; C23C14/0047; C23C14/0052; H; H10; H10P; H10P14/00; H10P14/20; H10P14/22; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/2921; H10P14/2922; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/36; H10P14/3602
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
152 words
A process for depositing a hydrogenated amorphous semiconductor film on a substrate comprising: simultaneously directing first and second ion beams, produced by first and second ion sources, respectively, against a first target of a semiconductor material that is to be included in said film, said first ion beam including sputtering ions to sputter material from said first target and said second beam including hydrogen ions to reduce the density of localized states in the deposited film; independently controlling the relative energies and currents of ions in said first and second beams so that the sputtering ions are effective in sputtering semiconductor material from said target and so that the energy of said hydrogen ions in the second ion beam does not exceed about 200 electron volts; and collecting sputtering products from said first target on said substrate, whereby a film of hydrogenated amorphous semiconductor material substantially free of polyhydrides is efficiently deposited.
Claim 2
Dependent Claim
152 words
A process for depositing a hydrogenated amorphous semiconductor film on a substrate comprising: simultaneously directing first and second ion beams, produced by first and second ion sources, respectively, against a first target of a semiconductor material that is to be included in said film, said first ion beam including sputtering ions to sputter material from said first target and said second beam including hydrogen ions to reduce the density of localized states in the deposited film; independently controlling the relative energies and currents of ions in said first and second beams so that the sputtering ions are effective in sputtering semiconductor material from said target and so that the energy of said hydrogen ions in the second ion beam does not exceed about 200 electron volts; and collecting sputtering products from said first target on said substrate, whereby a film of hydrogenated amorphous semiconductor material substantially free of polyhydrides is efficiently deposited.
Claim 3
Dependent Claim
12 words
The process of claim 1 wherein said sputtering ions comprise argon ions.
Claim 4
Dependent Claim
20 words
The process of claim 2 wherein said argon ion beam has a current of between approximately 20 to 50 milliamperes.
Claim 5
Dependent Claim
13 words
The process of claim 1 wherein said first target comprises substantially pure silicon.
Claim 6
Dependent Claim
20 words
The process of claim 4 wherein said hydrogen ion beam has a current of between approximately 20 to 60 milliamperes.
Claim 7
Dependent Claim
20 words
The process of claim 4 including elevating the temperature of said substrate to between approximately 100° C. to 300° C.
Claim 8
Dependent Claim
12 words
The process of claim 1 including illuminating said substrate with ultraviolet light.
Claim 9
Dependent Claim
19 words
The process of claim 1 wherein said first target comprises an element from group IVa of the periodic table.
Claim 10
Dependent Claim
20 words
The process of claim 1 wherein said substrate consists of one of the group of glass, fused silica and silicon.
Claim 11
Dependent Claim
10 words
The process of claim 1 wherein said substrate is metallic.
Claim 12
Dependent Claim
12 words
The process of claim 10 wherein said substrate is a stainless steel.
Claim 13
Dependent Claim
16 words
The process of claim 1 wherein said second ion source produces a beam including dopant ions.
Claim 14
Dependent Claim
20 words
The process of claim 12 wherein said dopant ions consists of one of the group of boron and phosphorus ions.
Claim 15
Dependent Claim
166 words
The process of claim 1 further comprising: while directing said first and second ion beams, simultaneously directing third and fourth ion beams, produced by third and fourth ion sources, respectively, against a second target of semiconductor material that is to be included in said film, said second target being of a different composition from said first target, said third ion beam including sputtering ions to sputter said material from said second target, and said fourth beam including hydrogen ions to reduce localized states in the deposited film; independently controlling the relative energies and currents of the ions in said third and fourth beams so that the sputtering ions are effective in sputtering semiconductor material from said second target and so that the energy of said hydrogen ions in the fourth beam does not exceed about 200 electron volts; and collecting sputtering products from said first and second targets on said substrate. whereby a film of hydrogenated amorphous semiconductor alloy substantially free of polyhydrides is efficiently deposited.
Claim 16
Dependent Claim
21 words
The process of claim 14 wherein said first target is substantially pure germanium and said second target is substantially pure silicon.
Claim 17
Dependent Claim
11 words
The process of claim 1 including irradiating said substrate with electrons.
Claim 18
Dependent Claim
26 words
The process of claim 1 wherein said first target comprises an alloy of at least two elemental semiconductors that are to be deposited as said film.
Claim 19
Dependent Claim
17 words
The process of claim 17 wherein said target comprises a substantially pure alloy of silicon and germanium.
References Cited (Backward Citations)
DD149549A1
Cited
US4376688A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-19 | 1990-07-21 | 1991-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-19 | 1994-07-21 | 1995-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-19 | 1998-07-21 | 1999-01-20 | $7700.00 | Window Closed / Lapsed |