US4937167A — Process for controlling the electrical characteri…

Claim 1

Independent Claim 168 words

A process for controlling the electrical characteristics of colored toner particles which comprises preparing a first core material comprising first pigment particles, core monomers, and a free radical initiator; preparing a second core material which comprises second pigment particles, core monomers, and a free radical initiator, said second pigment particles being of different color from that of the first pigment particles; dispersing the first and second core materials into an aqueous phase; encapsulating separately the first core material and the second core material within polymeric shells by interfacial polymerization reactions between at least two shell monomers, of which at least one is soluble in aqueous media and at least one of which is soluble in organic media, wherein the polymeric shell encapsulating the first core material is of substantially the same composition as the polymeric shell encapsulating the second core material; and subsequently polymerizing the first and second core monomers via free radical polymerization, thereby producing two encapsulated toner compositions of different colors with similar triboelectric charging characteristics.

Claim 2

Dependent Claim 168 words

A process for controlling the electrical characteristics of colored toner particles which comprises preparing a first core material comprising first pigment particles, core monomers, and a free radical initiator; preparing a second core material which comprises second pigment particles, core monomers, and a free radical initiator, said second pigment particles being of different color from that of the first pigment particles; dispersing the first and second core materials into an aqueous phase; encapsulating separately the first core material and the second core material within polymeric shells by interfacial polymerization reactions between at least two shell monomers, of which at least one is soluble in aqueous media and at least one of which is soluble in organic media, wherein the polymeric shell encapsulating the first core material is of substantially the same composition as the polymeric shell encapsulating the second core material; and subsequently polymerizing the first and second core monomers via free radical polymerization, thereby producing two encapsulated toner compositions of different colors with similar triboelectric charging characteristics.

Claim 3

Dependent Claim 21 words

A process according to claim 1 wherein the two resulting toner compositions have mean particle diameters of less than 10 microns.

Claim 4

Dependent Claim 24 words

A process according to claim 1 wherein the two resulting toner compositions have mean particle diameters of from about 5 to about 8 microns.

Claim 5

Dependent Claim 78 words

A process according to claim 1 wherein the core monomers present in the first and second core materials are independently selected from the group consisting of styrene, α-methylstyrene, vinyl toluene, n-alkyl methacrylates, n-alkyl acrylates, branched alkyl methacrylates, branched alkyl acrylates, chlorinated olefins, butadiene, styrene-butadiene oligomers, ethylene-vinyl acetate oligomers, isobutylene-isoprene copolymers, vinyl-phenolic materials, alkoxy alkoxy alkyl acrylates, alkoxy alkoxy alkyl methacrylates, cyano alkyl acrylates and methacrylates, alkoxy alkyl acrylates and methacrylates, methyl vinyl ether, maleic anhydride, and mixtures thereof.

Claim 6

Dependent Claim 19 words

A process according to claim 1 wherein the first and second core materials contain up to 5 core monomers.

Claim 7

Dependent Claim 35 words

A process according to claim 1 wherein the free radical polymerization initiators present are selected from the group consisting of 2,2'-azobis(isobutyronitrile), 2,2'-azobis(2,4-dimethylvaleronitrile), 2,2'-azobis(cyclohexanenitrile), 2,2'-azobis-(2-methylbutyronitrile), 2,2'-azobis(2,4-dimethyl-4-methoxyvaleronitrile), benzoyl peroxide, lauryl peroxide, 2,5-dimethyl-2,5-bis(2-ethylhexanoylperoxy)hexane, Lupersol 256® and mixtures thereof.

Claim 8

Dependent Claim 28 words

A process according to claim 1 wherein the initiators are present in an amount of from about 0.5 to about 8 percent by weight of the core monomer.

Claim 9

Dependent Claim 27 words

A process according to claim 1 wherein said first core components and said second core components comprise at least one polymeric material prior to free radical polymerization.

Claim 10

Dependent Claim 30 words

A process according to claim 8 wherein said polymeric material is selected from the group consisting of styrene-butadiene copolymers, styrene-acrylate copolymers, styrene-methacrylate copolymers, ethylene-vinylacetate copolymers, isobutylene-isoprene copolymers, and mixtures thereof.

Claim 11

Dependent Claim 73 words

A process according to claim 8 wherein the polymeric material is a polymer containing monomers selected from the group consisting of styrene, α-methylstyrene, vinyl toluene, n-alkyl methacrylates, n-alkyl acrylates, branched alkyl methacrylates, branched alkyl acrylates, chlorinated olefins, butadiene, styrene-butadiene oligomers, ethylene-vinyl acetate oligomers, isobutylene-isoprene copolymers, vinyl-phenolic materials, alkoxy alkoxy alkyl acrylates, alkoxy alkoxy alkyl methacrylates, cyano alkyl acrylates and methacrylates, alkoxy alkyl acrylates and methacrylates, methyl vinyl ether, maleic anhydride, and mixtures thereof.

Claim 12

Dependent Claim 30 words

A process according to claim 8 wherein the ratio of the amount of the core monomers to the amount of the polymeric material is from about 0:100 to about 40:60.

Claim 13

Dependent Claim 34 words

A process according to claim 8 wherein the core monomers and the polymeric material are present in a total amount of from about 35 to about 90 percent by weight of the toner compositions.

Claim 14

Dependent Claim 39 words

A process according to claim 1 wherein said first core material and said second core material also comprise a wax selected from the group consisting of candelilla, bees wax, sugar cane wax, carnuba wax, paraffin wax and mixtures thereof.

Claim 15

Dependent Claim 38 words

A process according to claim 13 wherein the wax is present in said first core material and said second core material in an amount of from about 0.5 percent to abut 20 percent by weight of the core.

Claim 16

Dependent Claim 72 words

A process according to claim 1 wherein said first shell monomers are selected from the group consisting of sebacoyl chloride, terephthaloyl chloride, phthaloyl chloride, isophthaloyl chloride, azeloyl chloride, glutaryl chloride, adipoyl chloride, hexamethylene diisocyanate, a 1:1 mixture of 2,2',4- and 2,4,4'-trimethylhexamethylene diisocyanate, Isophorone diisocyanate, m-tetramethylxylene diisocyanate, ρ-tetramethylxylene diisocyanate, 4,4'-dicyclohexylmethane diisocyanate, an 80:20 mixture of 2,4- and 2,6-toluene diisocyanate, trans-1,4-cyclohexane diisocyanate, 4,4'-methyldiphenyl diisocyanate, 1,3,5-benzenetricarboxylic acid chloride, Isonate 143L, tris(isocyanatophenyl) thiophosphate, and mixtures thereof.

Claim 17

Dependent Claim 41 words

A process according to claim 1 wherein said second shell monomers are selected from the group consisting of 1,6-hexanediamine, 1,4-bis(3-aminopropyl)piperazine, 2-methylpiperazine, m-xylene-α,α-diamine, 1,8-diamino-ρ-menthane, 3,3'-diamino-N-methyldipropylamine, 1,3-cyclohexanebis(methylamine), 1,4-diaminocyclohexane, 2-methylpentanediamine, 1,2-diaminocyclohexane, 1,3-diaminopropane, 1,4-diaminobutane, 2,5-dimethylpiperazine, piperazine, fluorine-containing 1,2-diaminobenzenes, N,N'-dimethylethylenediamine, diethylenetriamine, bis(3-aminopropyl)amine), tris(2-aminoethyl)amine, and mixtures thereof.

Claim 18

Dependent Claim 113 words

A process according to claim 1 wherein said first shell monomers are selected from the group consisting of sebacoyl chloride, terephthaloyl chloride, phthaloyl chloride, isophthaloyl chloride, azeloyl chloride, glutaryl chloride, adipoyl chloride, hexamethylene diisocyanate, a 1:1 mixture of 2,2',4- and 2,4,4'-trimethylhexamethylene diisocyanate, Isophorone diisocyanate, m-tetramethylxylene diisocyanate, ρ-tetramethylxylene diisocyanate, 4,4'-dicyclohexylmethane diisocyanate, a 80:20 mixture of 2,4- and 2,6-toluene diisocyanate, trans-1,4-cyclohexane diisocyanate, 4,4'-methyldiphenyl diisocyanate, 1,3,5-benzenetricarboxylic acid chloride, Isonate 143L, tris(isocyanatophenyl) thiophosphate, and mixtures thereof and said second shell monomers are selected from the group consisting of 1,6-hexanediamine, 1,4-bis(3-aminopropyl)piperazine, 2-methylpiperazine, m-xylene-α,α'-diamine, 1,8-diamino-ρ-menthane,3,3'-diamino-N-methyldipropylamine, 1,3-cyclohexanebis(methylamine), 1,4-diaminocyclohexane, 2-methylpentanediamine, 1,2-diaminocyclohexane, 1,3-diaminopropane, 1,4-diaminobutane, 2,5-dimethylpiperazine, piperazine, Isophorone diamine, a 1:1 mixture of 2,2',4- and 2,4,4'-trimethylhexamethylenediamine, N,N'-dimethylethylenediamine, diethylenetriamine, bis(3-aminopropyl)amine, tris(2-aminoethyl)amine, and mixtures thereof.

Claim 19

Dependent Claim 34 words

A process according to claim 1 wherein the polymeric shell is selected from the group consisting of polyureas, polyurethanes, polyesters, thermotropic liquid crystalline polyesters, polycarbonates, polyamides, polysulfones, poly(urea-urethanes), poly(ester-amides), poly(urea-amides), poly(ester-urethane), and mixtures thereof.

Claim 20

Dependent Claim 28 words

A process according to claim 1 wherein the polymeric shell is present in an amount of from about 5 to about 50 percent by weight of the toner.

Claim 21

Dependent Claim 21 words

A process according to claim 1 wherein from 2 to about 10 shell monomers undergo interfacial polymerization to form the shell.

Claim 22

Dependent Claim 17 words

A process according to claim 20 wherein 3 shell monomers undergo interfacial polymerization to form the shell.

Claim 23

Dependent Claim 21 words

A process according to claim 1 wherein a surface charge control agent is incorporated into the polymeric shells during their formation.

Claim 24

Dependent Claim 43 words

A process according to claim 22 wherein said charge control agent is selected from the group consisting of fumed silicas, colloidal silicas, aluminas, talc powders, metal salts, metal salts of fatty acids, cetyl pyridinium salts, distearyl dimethyl ammonium methyl sulfate, and mixtures thereof.

Claim 25

Dependent Claim 41 words

A process according to claim 22 wherein the surface charge control agent, when incorporated into the polymeric shells, is present in an amount of from about 0.1 to about 20 percent by weight of the shell monomer soluble in aqueous media.

Claim 26

Dependent Claim 24 words

A process according to claim 1 wherein a charge control agent is added to the surface of the polymeric shells subsequent to their formation.

Claim 27

Dependent Claim 65 words

A process according to claim 25 wherein the charge control agent is selected from the group consisting of particles selected from the group consisting of fumed silicas and fumed metal oxides, and wherein upon the surfaces of the particles have been deposited charge enhancing additives selected from the group consisting of cetyl pyridinium chloride, distearyl dimethyl ammonium methyl sulfate, potassium tetraphenyl borate, and mixtures thereof.

Claim 28

Dependent Claim 29 words

A process according to claim 25 wherein the charge control agent is present in an amount of from about 0.01 to about 15 percent by weight of the toner.

Claim 29

Dependent Claim 29 words

A process according to claim 1 wherein the two encapsulated toner compositions of different colors can be triboelectrically charged to within 25 microcoulombs per gram of the same value.

Claim 30

Dependent Claim 56 words

A process according to claim 1 wherein the two encapsulated toner compositions of different colors can be triboelectrically charged to within 25 microcoulombs per gram of the same value when the two toners contain identical charge control additives present in substantially the same amounts and when the two toners are in the presence of identical carriers.

Claim 31

Dependent Claim 29 words

A process according to claim 1 wherein the two encapsulated toner compositions of different colors can be triboelectrically charged to within 10 microcoulombs per gram of the same value.

Claim 32

Dependent Claim 24 words

A process according to claim 1 wherein the interfacial polymerization takes place at a temperature of from about 10° C. to about 30° C.

Claim 33

Dependent Claim 29 words

A process according to claim 1 wherein the free radical polymerization of the core monomers is performed at a temperature of from about 50° C. to about 120° C.

Claim 34

Dependent Claim 30 words

A process according to claim 1 wherein the free radical polymerization of the core monomers is effected by heating the monomers for from about 8 hours to about 24 hours.

Claim 35

Dependent Claim 181 words

A process according to claim 1 wherein the first and second pigments are independently selected from the group consisting of Violet VT-8015, Normandy Magenta RD-2400, Paliogen Violet 5100, Paliogen Violet 5890, Permanent Violet VT-645, Heliogen Green L8730, Argyle Green XP-111-S, Brilliant Green Toner GR0991, Lithol Scarlet D3700, Tolidine Red, Scarlet for Thermoplast NSD PS PA, E. D. Toluidine Red, Lithol Rubine Toner, Lithol Scarlet4440, Bon Red C, Royal Brilliant Red RD-8192, Oracet Pink RF, Paliogen Red 3871K, Paliogen Red 3340, Lithol Fast Scarlet L4300, Heliogen Blue L6900, L7020, Heliogen Blue K6902, K6910, Heliogen Blue D6840, D7080, Sudan Blue OS, Neopen Blue FF4012, PV Fast Blue B2G01, Iragalite Blue BCA, Paliogen Blue 6470, Sudan III, Sudan II, Sudan IV, Sudan Orange 220, Paliogen Orange 3040, Ortho Orange OR2673, Paliogen Yellow 152, 1560, Lithol Fast Yellow 0991K, Paliotol Yellow 1840, Novoperm Yellow FGL, Permanent Yellow YE0305, Lumogen Yellow D0790, Suco-Gelb L1250, Suco-Yellow D1355, Sico Fast Yellow D1355, D1351, Hostaperm Pink E, Fanal Pink D4830, Cinquasia Magenta, Paliogen Black L0084, Pigment Black K801, Regal 330® Carbon Black 5250, Carbon Black 5750 and mixtures thereof.

Claim 36

Dependent Claim 30 words

A process according to claim 1 wherein the first and second pigments are present in amounts of from about 5 to about 15 percent by weight of the respective toners.

Claim 37

Dependent Claim 20 words

A process according to claim 1 wherein subsequent to free radical polymerization the resulting toners are washed and thereafter dried.

Claim 38

Dependent Claim 32 words

A process according to claim 1 wherein the total amount of shell monomer soluble in organic media is from about 4.5 to about 35 percent by weight of the resulting toner composition.

Claim 39

Dependent Claim 32 words

A process according to claim 1 wherein the total amount of shell monomer soluble in aqueous media is from about 2.5 to about 15 percent by weight of the resulting toner composition.

Claim 40

Dependent Claim 31 words

A process according to claim 1 wherein a strengthening agent is incorporated into the polymeric shells, which strengthening agent is selected from the group consisting of epoxy monomers and epoxy oligomers.

Claim 41

Dependent Claim 29 words

A process according to claim 39 wherein the strengthening agent is present in an amount of from about 0.01 to about 30 percent by weight of the polymeric shell.

Claim 42

Dependent Claim 41 words

A process according to claim 1 wherein the polymeric shells also include crosslinking monomers selected from the group consisting of triamines, triisocyanates, and triols in an amount of from about 0.01 to about 30 percent by weight of the shell monomers.

Claim 43

Dependent Claim 35 words

A process according to claim 1 wherein the two encapsulated toners are subsequently mixed with carrier particles to form developer compositions with similar triboelectric charging characteristics, wherein both toners are mixed with substantially identical carriers.

Claim 44

Dependent Claim 197 words

A process according to claim 42 wherein the carrier particles are selected from the group consisting of a ferrite core with a coating comprising a methyl terpolymer which comprises methyl methacrylate in an amount of about 81 percent by weight, styrene in an amount of about 14 percent by weight, and vinyl triethoxysilane in an amount of about 5 percent by weight; an oxidized steel core with a coating comprising a polymer which comprises trifluorochloroethylene in an amount of about 65 percent by weight and vinyl chloride in an amount of about 35 percent by weight, wherein the polymeric coating also contains carbon black particles; a steel core with a coating comprising polyvinylidene fluoride; a steel core with a coating comprising a polymer blend which comprises about 35 percent by weight of polyvinylidene fluoride and about 65 percent by weight of polymethylmethacrylate; and a ferrite core with a coating comprising a methyl terpolymer which comprises methyl methacrylate in an amount of about 81 percent by weight, styrene in an amount of about 14 percent by weight, and vinyl triethoxysilane in an amount of about 5 percent by weight, wherein the polymeric coating also contains carbon black particles.

Claim 45

Dependent Claim 20 words

A process according to claim 1 wherein the polymeric shells are selected from the group consisting of polyamides and polyureas.

Claim 46

Dependent Claim 12 words

A process according to claim 1 wherein the polymeric shells are polyureas.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1993-06-25	1993-12-25	1994-06-26	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1997-06-25	1997-12-25	1998-06-26	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2001-06-25	2001-12-25	2002-06-26	$7700.00	Window Closed / Lapsed

Process for controlling the electrical characteristics of toners

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag