Manufacturing method for a ceramic capacitor
Assignee: Murata Manufacturing Co Ltd
•
Filing: 1988-07-25
•
Granted: 1990-06-26
•
Expires: 2008-07-25
Abstract
Abstract A manufacturing method for a ceramic capacitor superior in breakdown voltage ability, comprising a process of baking opposite electrode on the surface of ceramic dielectric composed mainly of metal oxide and that, simultaneous with or after the above process, of baking in a ring-like shape insulating layers for air cutoff on at least the edges of an electrode. The opposite electrodes are formed by baking on the ceramic dielectric an electrode material composed mainly of metal of oxidization property more intense than that of the metal oxide at the ceramic dielectric material, in which, when the insulating layers on the electrode are baked, parts covered with the insulating layers at the opposite electrodes are cutoff from air, so that the ceramic dielectrics just below the parts are deprived by the opposite electrodes of inner oxygen so as to be intensively reduced and the reduced areas each become a semiconductor to largely decrease an insulating resistance value, thereby relaxing a potential gradient at the edge of the electrode and improving the breakdown voltage ability.
Inventors
- 👤 Hajime Arakawa
- 👤 Osamu Yamaoka
- 👤 Motoaki Kakio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:00
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/005; H01G4/008; H01G2/00; H01G2/20
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
107 words
A method for manufacturing a ceramic capacitor which comprises: forming an assembly by coating portions of the surface of a dielectric ceramic mainly comprising metal oxide with an electrode composition mainly comprising a metal which is more readily oxidizable than said metal oxide, coating on at least the edges of said electrode composition an insulating composition for preventing penetration of air to said electrode composition and then baking said assembly in an oxidizing atmosphere, whereby electrodes having insulating layers thereon are formed on said dielectric ceramic and whereby portions of said dielectric ceramic beneath said insulating composition are reduced, thereby increasing the breakdown voltage of said capacitor.
Claim 2
Independent Claim
107 words
A method for manufacturing a ceramic capacitor which comprises: forming an assembly by coating portions of the surface of a dielectric ceramic mainly comprising metal oxide with an electrode composition mainly comprising a metal which is more readily oxidizable than said metal oxide, coating on at least the edges of said electrode composition an insulating composition for preventing penetration of air to said electrode composition and then baking said assembly in an oxidizing atmosphere, whereby electrodes having insulating layers thereon are formed on said dielectric ceramic and whereby portions of said dielectric ceramic beneath said insulating composition are reduced, thereby increasing the breakdown voltage of said capacitor.
Claim 3
Dependent Claim
27 words
The method as set forth claim 1, wherein a main constituent of said ceramic dielectric is a metal oxide of strontium titanate series or barium titanate series.
Claim 4
Dependent Claim
28 words
The method as set forth in claim 1, wherein said electrode material forming said electrodes is a conductive paste constituted mainly of aluminum powder and containing glass powder
Claim 5
Dependent Claim
24 words
The method for as set forth in claim 1, wherein said opposite electrodes are baked on the two opposite surfaces of said ceramic dielectric.
Claim 6
Dependent Claim
23 words
The method as set forth in claim 1, wherein said electrodes are baked in an arrangement on one surface of said ceramic dielectric.
Claim 7
Independent Claim
120 words
A method for manufacturing a ceramic capacitor which comprises: forming an assembly by coating portions of the surface of a dielectric ceramic mainly comprising metal oxide with an electrode composition mainly comprising a metal which is more readily oxidizable than said metal oxide, baking said electrode material on said surfaces to form electrodes thereon, coating at least the edges of said electrodes with an insulating composition to prevent air from reaching the coated portions of said electrodes and then baking said assembly in an oxidizing atmosphere, whereby electrodes having insulating layers thereon are formed on said dielectric ceramic and whereby the portions of said dielectric ceramic beneath said insulating composition are reduced, thereby increasing the breakdown voltage of said capacitor.
Claim 8
Independent Claim
120 words
A method for manufacturing a ceramic capacitor which comprises: forming an assembly by coating portions of the surface of a dielectric ceramic mainly comprising metal oxide with an electrode composition mainly comprising a metal which is more readily oxidizable than said metal oxide, baking said electrode material on said surfaces to form electrodes thereon, coating at least the edges of said electrodes with an insulating composition to prevent air from reaching the coated portions of said electrodes and then baking said assembly in an oxidizing atmosphere, whereby electrodes having insulating layers thereon are formed on said dielectric ceramic and whereby the portions of said dielectric ceramic beneath said insulating composition are reduced, thereby increasing the breakdown voltage of said capacitor.
Claim 9
Dependent Claim
28 words
The method as set forth in claim 6, wherein a main constituent of said ceramic dielectric is a metal oxide of strontium titanate series or barium titanate series.
Claim 10
Dependent Claim
28 words
The method as set forth in claim 6, wherein said electrode material forming said electrodes is a conductive paste constitute mainly of aluminum powder and containing glass powder.
Claim 11
Dependent Claim
22 words
The method as set forth in claim 6, wherein said electrodes are baked on the two opposite surfaces of said ceramic dielectric.
Claim 12
Dependent Claim
23 words
The method as set forth in claim 6, wherein said electrodes are baked in an arrangement on one surface of said ceramic dielectric.
References Cited (Backward Citations)
US4215385A
Cited
US4323948A
Cited
US4460622A
Cited
US4397886A
Cited
US4419310A
Cited
US4822645A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-25 | 1993-12-25 | 1994-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-25 | 1997-12-25 | 1998-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-25 | 2001-12-25 | 2002-06-26 | $7700.00 | Window Closed / Lapsed |